Cyclic loading comparison between biodegradable interference screw fixation and biodegradable double cross-pin fixation of human bone-patellar tendon-bone grafts.

Thore Zantop·Markus Ruemmler·Barbara Welbers·Martin Langer·Andre Weimann·Wolf Petersen
View original source ↗Export metadata ↓

Abstract

PURPOSE: The aim of this study was to compare ultimate load, yield load, stiffness, and displacement after cyclic loading of a cross-pin technique and an interference screw technique for the fixation of bone-patellar tendon-bone (BPTB) grafts in anterior cruciate ligament (ACL) reconstruction. TYPE OF STUDY: Biomechanical in vitro study. METHODS: The devices tested were 2 2.7-mm biodegradable pins (RigidFix; Ethicon, Mitek Division, Norderstedt, Germany) and biodegradable interference screws (Absolute; Innovasive Devices, Marlborough, MA). Each device was used for the fixation of 10 8-mm, 9-mm, or 10-mm sized human BPTB grafts in tunnels drilled in bovine knees. Ultimate load, yield load, stiffness, and displacement after cyclic loading (1,000 cycles between 50 and 250 N) were then evaluated. RESULTS: All 8-mm grafts that were fixed with cross-pins failed after a mean of 124 cycles of load. The 9-mm and 10-mm grafts survived the cyclic loading protocol. Yield load and maximum load of the 10-mm groups (cross-pin and interference screw) were significantly higher than that of the 9-mm groups. There was no significant difference in maximum load, yield load, and stiffness between the cross-pin and interference screw fixation technique for 1 graft size. CONCLUSIONS: The biomechanical data suggest that femoral fixation of 9-mm and 10-mm BPTB grafts using 2.7-mm biodegradable cross-pins leads to primary stability that is comparable to that of biodegradable interference screws. Fixation of 8-mm BPTB grafts using 2.7-mm biodegradable cross-pins had poor results. CLINICAL RELEVANCE: The diameter of the bone block is the limiting factor for the final fixation strength and the cyclical survival when using cross-pins. We strongly recommend not using this technique for bone blocks smaller than 9 mm in diameter.

Explore related subjects

Absorbable ImplantsAnimalsAnterior Cruciate LigamentBone NailsBone ScrewsCattleEquipment FailureFemurHumansMaterials TestingPatellar LigamentTensile StrengthTibiaWeight-BearingComparative StudyEvaluation StudyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Thore Zantop, Markus Ruemmler, Barbara Welbers, Martin Langer, Andre Weimann, Wolf Petersen. 2005. Cyclic loading comparison between biodegradable interference screw fixation and biodegradable double cross-pin fixation of human bone-patellar tendon-bone grafts.. https://doi.org/10.1016/j.arthro.2005.05.022

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Encapsulation of proteins in biodegradable polymeric microparticles using electrospray in the Taylor cone-jet mode.

Solvent extraction (or evaporation from a W(1)/O/W(2)-dispersion), coacervation, and spray drying methods are commonly employed to encapsulate protein drugs in polymeric microparticles for sustained delivery applications. To overcome the limitations of these methods, a novel electrospray method was developed to encapsulate a model protein drug-bovine serum albumin (BSA) in biodegradable polymeric microparticles and examine the feasibility of the process in not denaturing the protein. Microparticles of approximately 20 microm diameter with corrugated surfaces and smooth surfaces were observed by scanning electron microscope. Confocal laser scanning microscope images showed that BSA was distributed evenly in microparticles. Sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) was employed to investigate the protein integrity of BSA released from the polymer matrix after 38 days. No protein degradation was observed during the 38 days release. The secondary structure of released BSA was characterized by Fourier transform infrared (FTIR) and circular dichroism (CD), which suggested that the released BSA was almost identical to native BSA. The encapsulation efficiency could reach 76% by adjusting the amount of the additive Pluronic F127 and processing parameters. The release profile could be tailored by the fabrication process and the sustained release of BSA could endure for more than 1 month. More than 80% of the bioactivity of BSA (evaluated by BSA ELISA kit) could be maintained after releasing from polymer matrix. Findings of the present study demonstrate that this novel electrospray method is a promising approach to encapsulate bioactive materials such as proteins, enzymes, antibiotics, and DNA fragments in biodegradable polymeric particles.

Absorbable Implants↗
PubMed2007

A novel poly(ethylene glycol)-fibrinogen hydrogel for tibial segmental defect repair in a rat model.

The aim of this study is to investigate regeneration in a segmental bone defect using a novel fibrinogen-based hydrogel material. The use of hydrogels made from poly(ethylene glycol) (PEG) conjugated to fibrinogen for this purpose may be better to conventional fibrin-based materials as it offers an additional degree of control over the structural characteristics and biodegradation of the material. At the same time, it maintains some of the inherent biofunctionality of the fibrinogen molecule. PEGylated fibrinogen hydrogels with various degrees of proteolytic resistance based on PEG and fibrinogen composition were designed for slow, intermediate, and fast biodegradation. The hydrogels were implanted into 7-mm segmental rat tibial defects without additional osteoinductive factors with the rationale that the ingrowth matrix will displace the normal fibrin clot while sustaining a similar healing effect for a longer duration. Histological and X-ray results confirmed that the extent and distribution of newly formed bone in the defect after 5 weeks strongly parallels the biodegradation pattern of the implanted material. When compared to nonunions in animals treated with the fast-degrading implants and untreated control animals, the rats implanted with the intermediate-degrading material exhibited osteoneogenesis. This data supports the hypothesis that the perseverance of the PEGylated fibrinogen material can be synchronized with the optimal healing characteristics of a segmental osseous defect and that the consequent sustained release of fibrinogen fragments facilitates the osteogenic response at the injury site. The PEGylated fibrinogen material may, therefore, be a highly efficacious material for promoting the healing of bone defects and especially nonunion fractures.

Absorbable Implants↗
PubMed2007

Pores in synthetic nerve conduits are beneficial to regeneration.

Current opinion holds that pores in synthetic nerve guides facilitate nerve regeneration. Solid factual support for this opinion, however, is absent; most of the relevant studies assessed only morphological parameters and results have been contradictory. To evaluate the effect of pores, the rat sciatic nerve was either autografted or grafted with nonporous, macroporous (10-230 mum), and microporous (1-10 microm) biodegradable epsilon-caprolactone grafts. Twelve weeks later, the grafted nerves were resected, and the electrophysiological properties were determined in vitro. Subsequently midgraft-level sections were inspected, and peroneal nerve sections were evaluated morphometrically. Finally, the gastrocnemic and tibial muscle morphometrical properties were quantified. The microporous nerve graft performed much better than the nonporous and macroporous grafts with respect to most parameters: it was bridged by a free floating bundle that contained myelinated nerve fibers, there were more nerve fibers present distal to the graft, the electrophysiological response rate was higher, and the decrease in muscle cross-sectional area was markedly smaller. Hence, the present study demonstrates the beneficial effect of synthetic nerve guide pores on nerve regeneration, although with the caveat that not pores per se, but only small (1-10 microm) pores were effective.

Absorbable Implants↗