Bioactive macroporous titanium surface layer on titanium substrate.

H M Kim·T Kokubo·S Fujibayashi·S Nishiguchi·T Nakamura
View original source ↗Export metadata ↓

Abstract

A macroporous titanium surface layer is often formed on titanium and titanium alloy implants for morphological fixation of the implants to bone via bony ingrowth into the porous structure. The surface of titanium metal was recently shown to become highly bioactive by being subjected to 5.0 M-NaOH treatment at 60 degrees C for 24 h and subsequent heat treatment at 600 degrees C for 1 h. In the present study, the NaOH and heat treatments were applied to a macroporous titanium surface layer formed on titanium substrate by a plasma spraying method. The NaOH and heat treatments produced an uniform amorphous sodium titanate layer on the surface of the porous titanium. The sodium titanate induced a bonelike apatite formation in simulated body fluid at an early soaking period, whereby the apatite layer grew uniformly along the surface and cross-sectional macrotextures of the porous titanium. This indicates that the NaOH and heat treatments lead to a bioactive macroporous titanium surface layer on titanium substrate. Such a bioactive macroporous layer on an implant is expected not only to enhance bony ingrowth into the porous structure, but also to provide a chemical integration with bone via apatite formation on its surface in the body.

Explore related subjects

ApatitesBody FluidsCoated Materials, BiocompatibleHot TemperatureMaterials TestingMicroscopy, Electron, ScanningPorosityProstheses and ImplantsSodium HydroxideSurface PropertiesTitaniumJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

H M Kim, T Kokubo, S Fujibayashi, S Nishiguchi, T Nakamura. 2000-12-05. Bioactive macroporous titanium surface layer on titanium substrate.. https://doi.org/10.1002/1097-4636(20001205)52%3A3%3C553%3A%3Aaid-jbm14%3E3.0.co%3B2-x

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2001

TEM-EDX study of mechanism of bonelike apatite formation on bioactive titanium metal in simulated body fluid.

Bioactive titanium metal, which forms a bonelike apatite layer on its surface in the body and bonds to the bone through the apatite layer, can be prepared by NaOH and heat treatments to form an amorphous sodium titanate layer on the metal. In the present study, the mechanism of apatite formation on the bioactive titanium metal has been investigated in vitro. The metal surface was examined using transmission electron microscopy and energy dispersive X-ray spectrometry as a function of the soaking time in a simulated body fluid (SBF) and complemented with atomic emission spectroscopy analysis of the fluid. It was found that, immediately after immersion in the SBF, the metal exchanged Na(+) ions from the surface sodium titanate with H(3)O(+) ions in the fluid to form Ti-OH groups on its surface. The Ti-OH groups, immediately after they were formed, incorporated the calcium ions in the fluid to form an amorphous calcium titanate. After a long soaking time, the amorphous calcium titanate incorporated the phosphate ions in the fluid to form an amorphous calcium phosphate with a low Ca/P atomic ratio of 1.40. The amorphous calcium phosphate thereafter converted into bonelike crystalline apatite with a Ca/P ratio of 1.65, which is equal to the value of bone mineral. The initial formation of the amorphous calcium titanate is proposed to be a consequence of the electrostatic interaction of negatively charged units of titania, which are dissociated from the Ti-OH groups, with the positively charged calcium ions in the fluid. The amorphous calcium titanate is speculated to gain a positive charge and to interact with the negatively charged phosphate ions in the fluid to form the amorphous calcium phosphate, which eventually stabilizes into bonelike crystalline apatite.

Apatites↗
PubMed2001

Effect of added NaHCO3 on the basic properties of apatite cement.

Alternation of a composition of set apatite cement (AC) from carbonate-free apatite (CO3-free AP) to carbonate apatite (CO3-AP) may accelerate replacement of the set AC with bone because CO3-AP can be dissolved much faster than CO3-free AP in the weak acidic solution produced by osteoclasts. In this investigation, NaHCO3 was added to the AC component and the effects of added NaHCO3 on cement-setting behavior and on set mass were studied as an initial step for the fabrication of AC, which can be replaced with bone faster than current AC. When NaHCO3 was added to AC, the resultant set mass contained CO3. Although not all CO3 was incorporated in the set AC, the amount of CO3 incorporated into the set AC increased with the amount of added NaHCO3. Powder X-ray diffraction analysis and Fourier transform infrared spectrometer measurements revealed the formation of B-type CO3-AP. The setting time measured in an incubator at 37 degrees C and 100% relative humidity slowed from 30 to 45 min, indicating that NaHCO3 has an inhibitory effect on AP formation. The diametral tensile strength of the set AC decreased significantly with the addition of NaHCO3. Scanning electron microscopic observation revealed that fine crystals were formed in the set AC when NaHCO3 was added to AC. As a result, the crystallinity indices of the set AC measured using X-ray diffraction and Fourier transform infrared spectroscopy decreased with an increase in the amount of added NaHCO3. The dissolution rate of set AC in weak acid, pH 5.5, increased with the amount of added NaHCO3. We concluded that the formation of B-type CO3-AP and the resulting faster dissolution of set AC in weak acidic solution is preferable for the faster replacement of set AC with bone even though the decreased diametral tensile strength value is a shortcoming.

Apatites↗
PubMed2001

A comparative study of in vitro apatite deposition on heat-, H(2)O(2)-, and NaOH-treated titanium surfaces.

Commercially pure titanium specimens are subjected to three different treatments, and their bioactivity are evaluated by immersing the specimens in a simulated body fluid (SBF, Kokubo's recipe) for various periods up to 7 days, with particular attention being paid to the differences in apatite deposition between surfaces open to SBF and surfaces in contact with the container's bottom. The treatment with a H(2)O(2)/HCl solution at 80 degrees C for 30 min followed by heating at 400 degrees C for 1 h produces an anatase titania gel layer on the specimen surface. This gel layer deposits apatite both on the contact and on open surfaces, and apatite deposition ability does not change with pre-staking in distilled water. The treatment with a NaOH solution at 60 degrees C for 3 days produces a sodium titanate gel layer. This gel layer can deposit apatite only on the contact surface, and the apatite deposition ability is completely lost after 1 day of pre-staking in distilled water. It is concluded, therefore, that the bioactivity of the titania gel originates from the favorable structure of the gel itself while the bioactivity of the sodium titanate gel depends heavily on ion release from the gel. The third treatment, a simple heat treatment at 400 degrees C for 1 h, produces a dense (not porous) oxide layer on the specimen surface. The specimens can deposit apatite on the contact surface after only 3 days of staking in SBF, but they cannot deposit apatite on the open surface for up to 2 months of staking. The implications of such apatite deposition behavior have been discussed in relation to the environments of titanium implants in bone as well as to the methodology of the SBF staking experiment.

Apatites↗