Polyurethanes containing oxetane-derived poly(2,2-substituted-1,3-propylene oxide) soft blocks: copolymer effect on wetting behavior.

Hydroxy-terminated poly(2,2-substituted-1,3-propylene oxide) telechelics and co-telechelics bearing semifluorinated (R = -CH(2)OCH(2)(CF(2))(n)CF(3), n = 0, 1) and/or bromomethyl pendant groups were synthesized from the corresponding 3,3-substituted oxetanes. The new telechelics were incorporated in polyurethanes (PUs) with isophorone diisocyanate (IPDI) and 1,4-butanediol (BD) as the hard block. Surface properties were evaluated using tapping mode atomic force microscopy (TM-AFM) and dynamic contact angle (DCA) analysis. Interestingly, polyurethanes containing P(3FOx-BrOx) have higher theta(adv) and lower theta(rec) than the homo-telechelic PUs [P(3FOx) = poly(2-methyl-2-trifluoroethoxymethyl-1,3-propylene oxide; P(BrOx) = poly(2-methyl-2-bromomethyl-1,3-propylene oxide)]. For IPDI-BD(40)/P(3FOx/BrOx-1:1), theta(adv) (116 degrees) is higher and theta(rec) (32 degrees) is lower (Deltatheta, 84 degrees ) than any other homo- or co-telechelic polyurethane. The unusual wetting behavior for P(FOx/BrOx) polyurethanes is correlated with FOx-BrOx dyad content, and a reversible H-bonding mechanism is proposed to explain the results.

Journal Article↗

PubMed2005

Polyurethane biocidal polymeric surface modifiers.

Polyurethanes (PUs) with soft blocks containing semifluorinated (-CH2OCH2CF3) and 5,5-dimethylhydantoin pendant groups were prepared and employed (2 wt%) as biocidal polymeric surface modifiers (PSMs) for a conventional PU coating comprised of an isophorone diisocyanate/1,4-butanediol-derived hard block (50%) and poly(tetramethylene oxide) soft block. Surface enrichment of the PSM was verified by dynamic contact angle measurements. The PSM modified PU was activated by converting near-surface amide groups to chloramide with 3wt% hypochlorite. The conversion of near-surface amide to chloramide is reflected in somewhat increased hydrophobic character for the antimicrobial chloramide functionalized surfaces. Biocidal activity against both Gram-positive (Staphylococcus aureus) and Gram-negative (Pseudomonas aeruginosa, and Escherichia coli) bacteria was demonstrated by using a modified version of American Association of Textile Chemists and Colorists (AATCC-100) test. By changing the PSM concentration it was found that only 1.6 wt% PSM (0.66 wt% biocide, 5,5-dimethylhydantoin) in a conventional PU affected complete kill of P. aeruginosa in 15 min by using this biocidal testing protocol.

Anti-Infective Agents↗

PubMed2005

Water induced hydrophobic surface.

A polyurethane coating is described that has hydrophilic wetting behavior when dry and hydrophobic when wet. A difference of approximately 25 degrees in advancing contact angles for dry (83 degrees ) and wet (108 degrees ) states is found by sessile drop and dynamic methods. The term "contraphilic" is suggested for this reversible change opposite customary amphiphilic behavior. Contraphilic behavior results from a soft block containing semifluorinated and 5,5-dimethyhydantoin segmers. Amide inter/intramolecular hydrogen bonding is proposed for the hydrophilic (dry) state, while surface-confined, amide-water hydrogen bonding "releases"semifluorinated groups, giving the hydrophobic state. Water-induced hydrophobic surfaces may lead to applications for easily switched wetting, such as in microfluidics.