Influence of different etchants and etching times on shear bond strength.

This study compared the shear bond strength to enamel of Scotchbond Multi-Purpose Dental Adhesive System's bonding resin following etching of enamel with 10% maleic, 1.6% oxalic, 10% phosphoric, and 35% phosphoric acids for 15, 30, and 60 seconds. Three hundred and sixty human molar teeth were used to create 12 groups of 30 enamel specimens per group (n = 30). Flattened enamel surfaces were treated with the different etchants for the time periods indicated, the surfaces primed, and adhesive resin applied according to the manufacturer's recommendations. The specimens were completed with Silux Plus resin and subjected to 1000 thermocycles (5-55 degrees C) followed by shear stress in an Instron Testing Machine to failure within a 24-hour period. A two-way ANOVA revealed significant differences for shear bond strength values by type of etchant (10% phosphoric, 35% phosphoric > 10% maleic > 1.6% oxalic acid) (P < 0.005) and by length of application time (P < 0.005). The interaction term for these two treatments was statistically significant (P < 0.005).

Acid Etching, Dental↗

PubMedDate not supplied

Temperature and humidity effects on bond strength of a dentinal adhesive.

Dentin specimens from 46 extracted human molar teeth were used in a matched-pair design examining the factors of temperature/humidity on shear bond strength of a dentinal adhesive to dentin. For one tooth-half, all procedures using restorative materials were accomplished in a controlled temperature and humidity chamber (humidity 95.0 +/- 2.0%, temperature 37.0 +/- 0.3 degrees C). For the other matched tooth-half all procedures were performed at ambient room conditions (humidity 52%, temperature 23.3 degrees C/74 degrees F). Oil-free air and water were used in all restorative procedures. Application of Scotchbond Multi-Purpose Adhesive System was followed by placement of Z100 Restorative Resin, and thermocycling 1000 cycles from 5 to 55 degrees C. Each matched specimen was tested 24 hours later in an Instron Testing Machine. A paired t-test was performed for comparison of bond strength set values, since they were obtained from matching halves of the same teeth. Paired t-test comparison showed that the average humidity/temperature chamber mean of 7.14 +/- 3.12 MPa was significantly less than the ambient conditions mean of 14.29 +/- 5.07 (P = 0.0000). Bond strength testing under simulated oral conditions may produce significantly different findings than customary bench-top laboratory experiments.

Composite Resins↗