E Sacher

Publications and source records attributed to E Sacher.

At least 19 recordsLinked to original sources

PubMed2006

Evidence of the interaction of evaporated Pt nanoparticles with variously treated surfaces of highly oriented pyrolytic graphite.

The interactions of Pt nanoparticles, deposited by evaporation onto highly oriented pyrolytic graphite surfaces modified by kiloelectronvolt Ar+ beam treatment, have been studied by X-ray photoelectron spectroscopy core-level line shape analysis. The C1s and Pt4f7/2 peaks were each considered to be composed of one asymmetric peak, and changes in their asymmetry parameters were used to study their interfacial interactions. In addition to these changes, strong signal intensity changes with time were found for both the C1s and Pt4f peaks, indicating an initial crystalline orientational instability of the Pt nanoparticles, which is supported by time-dependent high-resolution electron microscopy studies at elevated temperatures.

Journal Article↗

PubMed2005

Interaction of evaporated nickel nanoparticles with highly oriented pyrolytic graphite: Back-bonding to surface defects, as studied by X-ray photoelectron spectroscopy.

Ni nanoparticle evaporation onto highly oriented pyrolytic graphite (HOPG), with low and high surface defect densities, has been studied in situ by X-ray photoelectron spectroscopic (XPS) techniques, including binding energy shifts, Auger parameters, and Wagner plots. Ni nucleates at defect sites, whether initially present or those introduced by Ar+ bombardment, with the formation of spherical nanoparticles, which adhere strongly through Ni/HOPG back-bonding. The variation of the C 1s peak intensity with Ni coverage suggests that the photoelectron emission yield may be enhanced at lower Ni coverages, due to Ni nanoparticle-induced electron localization and work function reduction at the HOPG surface, which is evidence of such back-bonding.

Journal Article↗

PubMed2005

Surface diffusion and coalescence of mobile metal nanoparticles.

The diffusion and coalescence of metal nanoparticles play important roles in many phenomena. Here, we offer a new integrated overview of the main factors that control the nanoparticle coalescence process. Three factors are considered in our description of the coalescence process: nanoparticle diffusion across the surface, their physical and thermodynamic properties, and the mechanism of coalescence. We demonstrate that the liquid-like properties of the surface layers of the nanoparticles play an essential role in this process. We present experimental evidence for our opinion, based on the high-resolution electron microscopic analysis of several different types of nanoparticles.

Journal Article↗

PubMed2005

A mediatorless biosensor for putrescine using multiwalled carbon nanotubes.

Poly(diallyldimethylammonium) chloride, having a capability of dispersing multiwalled carbon nanotubes (MWCNTs), permits the modification of electrode surfaces. Together with putrescine oxidase, a MWCNT modified glassy carbon electrode was constructed for the development of a mediatorless putrescine biosensor. Nanoscale "dendrites" of MWCNTs were reasoned to form a network, projecting outward from the electrode surface acting like bundled ultra-microelectrodes, thereby permitting access to the active site and facilitating direct electron transfer to the immobilized enzyme. Our biosensor was capable of efficiently monitoring the direct electroactivity of putrescine oxidase at the electrode surface. Direct electron transfer permits the detection of putrescine at negative potentials, circumventing the interference of endogenous ascorbic and uric acids, which often complicate the analysis of important compounds in plasma. Compared with the most common interfering species, such as spermine, spermidine, cadaverine, and histamine, a detection limit of 5 microM and a response 20 times greater were found for putrescine. Tests performed on plasma of cancerous mice demonstrated that the detection of putrescine could be carried out very quickly on mammalian plasma without previous purification.

Animals↗

PubMed2001

A tapping mode AFM study of collapse and denaturation in dentinal collagen.

OBJECTIVES: Tapping mode atomic force microscopy (AFM) was used to investigate the surface changes of collagen exposed to phosphoric acid treatment. We focus on denaturation and collapse following demineralization and exposure to air. METHODS: Unpolished dentin disks, obtained from freshly extracted human molars, were etched in 37% phosphoric acid for 15s, rinsed ultrasonically and gently blotted with soft paper; the specimens were then continuously observed using tapping mode AFM. RESULTS: Immediately after the removal of bulk water, the surface consisted of a porous network of banded collagen fibrils, having periodicities of 67nm. After approximately 8min of subsequent air-drying, the spacing between fibrils was lost, and the surface was observed to consist of a dense array of closely spaced fibrils. The banding periodicity was still observable. SIGNIFICANCE: The air drying of etched dentin results in the collapse of the collagen network, but not in the denaturation of the collagen fibrils. This study indicates that collapse and denaturation are separate phenomena. It further shows that water loss occurs rapidly, and disrupts the native conformation of the collagen network. This would have adverse effects on adhesion.

Acid Etching, Dental↗

PubMed2001

A photoacoustic FTIRS study of the chemical modifications of human dentin surfaces: II. Deproteination.

This work focuses on the chemical alterations occurring on the dentin surface on treatment with sodium hypochlorite (NaOCl), a known deproteinating agent. In addition, sequential treatment with both acid and NaOCl are characterized. Modifications are evaluated using photoacoustic FTIR (PA-FTIRS), a surface-sensitive spectroscopy. Spectra of NaOCl-treated dentin samples show a slow and heterogeneous removal of its organic phase, leaving calcium hydroxyapatite and carbonate apatite unchanged. Spectra of this deproteinated surface resemble those of apatites synthesized at low temperatures and having very high-surface areas. A combined sequential 2-min treatment of dentin with both maleic acid and NaOCl indicates that this treatment can produce a surface region which is neither significantly demineralized nor deproteinated. This sequential treatment can be used to remove the smear layer and restore the dentin surface to its natural composition.

Acid Etching, Dental↗

PubMed2001

A photoacoustic FTIRS study of the chemical modifications of human dentin surfaces: I. Demineralization.

Acids are used to modify the structure and composition of dentin surfaces to improve bonds formed with resins. The purpose of this work is to investigate such chemical modifications using the surface-sensitive technique photoacoustic Fourier transform infrared spectroscopy (PA-FTIRS). Spectra of acid-treated samples (citric, maleic, nitric, and phosphoric at pH = 1.0) were recorded at various time intervals. Analysis of these spectra indicates a gradual increase in sample surface area with treatment time. A decrease of the bands associated with calcium hydroxyapatite (HAP) and carbonate apatite inherent to the mineral phase of dentin are also observed. A comparison of spectra of samples treated for 2 min with each acid also reveals that maleic and phosphoric acids remove more HAP than citric acid. We conclude that citric acid may cause the formation of precipitates at the etching front which inhibit etching.

Acids↗

PubMed1999

Field emission in-lens SEM study of enamel and dentin.

This investigation used field emission in-lens scanning electron microscopy (FEISEM) for the study of tooth surfaces, with particular reference to adhesive bonding and acid conditioning. Dentin wafers with an intact enamel periphery were treated by either ethylenediaminetetraacetic acid (EDTA) (pH 7.4) or phosphoric acid (pH 0.7). The samples were then fixed, sequentially dehydrated in alcohol, and either air- or critical point-dried. After coating, surfaces were examined by FEISEM. For enamel, intraprismatic crystals were clearly recognizable, with the crystals showing both a longitudinal and parallel orientation to the long axis of the prisms. For dentin, the surface ultrastructure (mineral crystals and collagen banding) for the both untreated and treated samples was observed. Fine structures measuring on the order of 6 nm were also observed on samples treated by EDTA. We conclude that FEISEM can routinely provide high-resolution images of enamel and dentin, and that it has the capability of revealing the defined distribution of crystals and collagen fibers in dental tissues.

Acid Etching, Dental↗

PubMed1998

Moisture-dependent renaturation of collagen in phosphoric acid etched human dentin.

We used atomic force microscopy (AFM) to investigate the effects of acidic and aqueous treatments on human dentin. Two basic points were determined: the first is the ability of AFM to discriminate the effect of phosphoric acid (pH approximately equal to 1) on polished dentin, and the second is the demonstrable effect of moisture on fibrous collagen structure. AFM images confirmed that the polishing process led to the removal of both smear layer and smear plugs. Our AFM study of undried dentin, which was then acid treated and kept moist, revealed substantial morphological changes at the dentin surface. Collagen fibers, having a characteristic periodicity of 67 nm, were imaged in situ for the first time; these structures were absent in dentin treated by phosphoric acid and subsequently vacuum dried, even after prolonged reimmersion in water. The AFM technique permitted us to demonstrate the important roles that moisture and etching play in the determination of the structure of collagen fibrils. Such structure may also play an important role in the diffusibility of subsequently applied dental adhesion systems.

Collagen↗

PubMed1994