Oxygen-controlled gamma-irradiation and annealing enable terminal processing of collagen-based biomaterials.

Abstract

Gamma irradiation is a widely adopted method for terminal sterilization of medical devices; however, its application to collagen-based extracellular matrix (ECM) materials remains limited due to radiation-induced degradation of structural integrity and mechanical performance. Here, we present an engineered terminal-processing strategy that combines oxygen controlled gamma irradiation (25-30 kGy) with post-irradiation dry-heat annealing to preserve ECM functionality while achieving effective sterilization. By modulating oxygen availability during irradiation, this approach alters radical reaction pathways, suppresses oxygen-mediated oxidative degradation, and generates a metastable radical-containing intermediate, which is subsequently converted into a structurally stabilized collagen network through thermal annealing. As a result, the treated matrices preserved ECM integrity and recovered clinically relevant mechanical properties. Furthermore, the process achieved cumulative viral reductions exceeding 6 log10 across a representative panel including enveloped and non-enveloped DNA and RNA viruses, demonstrating compatibility with sterility assurance and viral safety requirements for biologically derived medical devices. Notably, preliminary observations indicate that mechanical integrity can be partially preserved even at elevated irradiation doses up to 50 kGy, suggesting potential applicability to sterilization validation frameworks requiring higher assurance levels. Overall, this work establishes a mechanistically grounded terminal-processing paradigm that enables control of radical fate, decouples sterilization efficacy from material degradation, and integrates sterilization, viral safety, and functional preservation into a unified and scalable framework for collagen-based biomaterials. This concept repositions gamma-irradiation from a purely degradative process to a controllable tool for tuning collagen structure and performance.