PubMed · 3422124
The source did not provide an abstract. Follow the original record for more information.
Explore connections, maps & timelines
G E Scott. 1988. Ceramic vs. metal brackets.. https://doi.org/10.1016/0889-5406(88)90198-9
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
The purpose of this study was to evaluate the effect of crystallization heat treatment on the flexural strength of potassium fluorrichterite glass-ceramics for biomedical applications. After melting and casting, discs were sectioned from the glass ingots, randomly divided into 10 groups, and heat treated at various temperatures ranging between 890 degrees C and 925 degrees C for various durations. One group was air-abraded after heat treatment. XRD revealed the presence of fluorrichterite and fluormica for all heat-treated groups. SEM confirmed the presence of both fluorrichterite and fluormica crystals. Crystal size increased with temperature and duration of the heat treatment. The mean flexural strength after air abrasion was not significantly different than that of the other groups except the group heat treated at 925 degrees C. The mean flexural strength was maximum after heat treatment at 900 degrees C for 1 h (497.6 +/- 25.5 MPa) and decreased linearly with the longer durations of heat treatment at 900 degrees C.
The purpose of this study was to investigate the influences of contaminations and cleaning methods on bonding to dental zirconia ceramic. After saliva immersion and using silicone disclosing agent, airborne-particle abraded ceramic specimens were cleaned with isopropanol (AL), acetone (AC), 37% phosphoric acid (PA), additional airborne-particle abrasion (AA), or only with water rinsing (SS). Airborne-particle abraded specimens without contaminations (CL) were used as control group. For chemical analysis specimens of all groups were examined with X-ray photoelectron spectroscopy (XPS). Plexiglas tubes filled with composite resin were bonded to ceramic specimens using a phosphate-monomer containing composite luting resin. After 3-day water storage, tensile bond strengths (TBS) were tested. XPS analysis of group SS showed the presence of saliva and silicone (Si) contamination on the surface. The ratios of carbon/zirconium and oxygen/zirconium for groups PA and AA were comparable to those ratios obtained for group CL, indicating the removal of the organic saliva contamination. Airborne-particle abrasion and acetone completely removed Si contamination from ceramic surfaces. Isopropanol had little cleaning effect on the two contaminants. TBS (median +/- standard deviation) in MPa of the groups SS (11.6 +/- 3.1), AL (10.0 +/- 2.9), and AC (13.0 +/- 2.8) were statistically lower than those of groups PA (33.6 +/- 5.5), AA (40.1 +/- 3.6), and CL (47.0 +/- 8.1) (p < 0.001), while no differences were found in TBS between groups AA and CL (p > 0.5). Contamination significantly reduced bond strengths to zirconia ceramic. Airborne-particle abrasion was the most effective cleaning method.
The role of substrate modulus on critical loads to initiate and propagate radial cracks to failure in curved brittle glass shells on compliant polymeric substrates is investigated. Flat glass disks are used to drive the crack system. This configuration is representative of dental crown structures on dentin support in occlusal contact. Specimens are fabricated by truncating glass tubes and filling with epoxy-based substrate materials, with or without alumina filler for modulus control. Moduli ranging from 3 to 15 GPa are produced in this way. Critical loads for both initiation and propagation to failure increase monotonically with substrate modulus, by a factor of two over the data range. Fracture mechanics relations provide a fit to the data, within the scatter bands. Finite element analysis is used to determine stress distributions pertinent to the observed fracture modes. It is suggested that stiffer substrate materials offer potential for improved crown lifetime in dental practice.