PubMed · 284980
The source did not provide an abstract. Follow the original record for more information.
Explore connections, maps & timelines
R J Simonsen. 1978. Space maintenance utilizing acid etch bonding.. https://pubmed.ncbi.nlm.nih.gov/284980/
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
When transmission electron microscopy (TEM) is used to evaluate resin-dentin interface specimens for completeness of hybridization, the epoxy resin embedding medium that normally facilitates ultrathin sectioning may produce a secondary or artifactual hybrid layer. This secondary hybrid layer, composed of epoxy resin rather than adhesive resin, may fill the pores that remain as evidence of incomplete resin infiltration, obscuring the fact that they ever existed. In this study, resin-dentin interfaces produced by two dentin adhesive systems, Optibond (OPTI, Kerr) and Scotchbond Multi-Purpose (SBMP, 3M), were comparatively investigated by TEM in epoxy-embedded and nonembedded nondemineralized sections. The hypothesis advanced was that no difference in ultramorphology of the hybrid layer would result from either specimen preparation method. The two adhesive systems were applied to four mid-coronal dentin disks per manufacturer's instructions. One half of each sample was processed following common procedures for TEM sample preparation with epoxy embedding, whereas the other half was not embedded but instead immersed in hexamethyldisilazane (HMDS), dried and mounted so that it protruded from a base of cold-cure acrylic resin. Each sample was then sectioned using a diamond knife in an ultramicrotome. With either means of preparation, a hybrid layer with a relatively uniform electron density and a loose collagen fibril arrangement with electron lucent interfibrillar channels was formed by OPTI. At the base of the hybrid layer, collagen fibrils were anchored in the underlying unaffected dentin, and no microporosities or gaps were observed. Similarly, whether SBMP was embedded or nonembedded, it was found to have a hybrid layer of variable electron density and an electron dense phase localized at the surface of the hybrid layer. No porosities were evident at the base of the hybrid layer. Thus, with either of the two adhesive systems, no ultrastructural difference in hybrid layer formation was observed between epoxy-embedded and nonembedded sections, and no direct evidence of ineffective resin-infiltration of the demineralized collagen scaffold was found.
PURPOSE: In vitro bond strengths of a traditional denture base resin (Lucitone 199) and three adhesive denture base resins (Meta-Dent, Meta-Fast with liner, and Meta-Fast without liner) to treated nickel-chromium-beryllium (Ni-Cr-Be) partial denture alloy were tested with four alloy surface pretreatments (sandblast, Met-etch, Rocatec with silane, and Rocatec without silane), with or without primer (Dentsply). The Lucitone 199 resin bonded to the nonprimed sandblasted group was the control group. The hypothesis was the use of alloy pretreatments and/or primer does not improve the bond strength of denture base resins to sandblasted Ni-Cr-Be partial denture alloy. MATERIAL AND METHODS: Primed and nonprimed bonded specimens were prepared and finished, stored in 37 degrees C distilled water for 24 hours, then debonded in tension on a testing machine. The bond strength was calculated in megapascals (MPa). Five specimens were prepared and tested for each experimental condition, both with and without primer, for a total of 160 specimens. RESULTS: For three-way analysis of variance, the main effects of resins and treatment were statistically significant (p < 0.05), but the main effect of primer was not statistically significantly (p > 0.05). Without primer, the control group had the lowest bond strength (0 MPa). The three adhesive resin groups produced significantly higher bond strengths than the Lucitone resin groups. For the treated groups, nearly all sandblasted groups produced significantly lower bond strength than the other three treated groups. Meta-Dent to Met-etch treated group had the highest bond strength (23.9 MPa). With primer, the bond strengths of the Lucitone resin groups were significantly higher than the nonprimed groups, and the Lucitone resin-primed Rocatec treated group had the highest bond strength (14.8 MPa). For the three adhesive denture base resins, nearly all primed treated groups had significantly lower bond strengths than nonprimed groups. CONCLUSIONS: Without primer, the Lucitone resin-sandblast treated group (control) had the lowest bond strength (0 MPa). The Meta-Dent denture base resin with the Met-etch treated group had the highest bond strength (23.9 MPa). With primer, the Lucitone resin-primed Rocatec-silane treated group had the highest bond strength (14.8 MPa). For the adhesive denture base resins, nearly all bond strengths of the primed treated groups were significantly lower than the values of the nonprimed groups.
PURPOSE: This report presents the preliminary results of a prospective multicenter study to evaluate the efficacy of a chemically etched pure titanium surface on screw-type dental implants. MATERIAL AND METHODS: The results of 147 implants placed in 75 patients were evaluated and followed for up to 3 years, using clinical and radiographic examinations. The implants were inserted to support single crowns, overdentures, and fixed prostheses, as dictated by the individual patient's need. RESULTS: Of the 147 implants placed, 5 were lost and the remaining implants were followed throughout, to the end of the study period. Crestal bone levels adjacent to each implant were monitored and the amount of total bone loss was calculated. Clinically healthy peri-implant gingival tissues were observed on 95% of the implants, whereas 88.3% demonstrated no bleeding on probing and no recession during the follow-up period. According to the criteria used in this study, the total success rate was calculated to be 96.6%.