SEBS aggregate patterning at a surface studied by atomic force microscopy.

Xia Han·Jun Hu·Honglai Liu·Ying Hu
View original source ↗Export metadata ↓

Abstract

The morphologies of films spin coated from dilute block copolymer solution onto a mica substrate were studied by atomic force microscopy (AFM). Variables of interest were the polymer concentration, solvent, heating temperature, aging, and ultrasonic effect. It is shown that the solution concentration is the predominant factor in determining the shape of the aggregates displayed from spheres and rods to irregular patches with increasing concentration. The solubility parameter of the solvent plays an important role in modifying the distribution and the size of clusters at the surface. The structures of the aggregates at the surface are metastable, which could evolve with temperature from rodlike aggregates into regular stripes when annealed at a temperature higher than the order-disorder transition temperature of SEBS, whereas those in solution could evolve with aging and ultrasonic treatment into a more stable network structure.

Explore related subjects

Aluminum SilicatesMicroscopy, Atomic ForcePolyethylenesPolymersPolystyrenesSpin LabelsSurface PropertiesJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Xia Han, Jun Hu, Honglai Liu, Ying Hu. 2006-03-28. SEBS aggregate patterning at a surface studied by atomic force microscopy.. https://doi.org/10.1021/la051293i

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2006

Adhesion of spherical polyelectrolyte brushes on mica: an in situ AFM investigation.

We demonstrate that the adsorption of cationic spherical polyelectrolyte brushes (SPB) on negatively charged mica substrates can be controlled in situ by the ionic strength of the suspension. The SPB used in our experiments consist of colloidal core particles made of polystyrene. Long cationic polyelectrolyte chains are grafted onto these cores that have diameters in the range of 100 nm. These particles are suspended in aqueous solution with a fixed ionic strength. Atomic force microscopy (AFM) in suspension as well as in air was used for surface characterization. In pure water the polymer particles exhibit a strong adhesion to the mica surface. AFM investigations of the dry samples show that the particles occupy the identical positions as they did in liquid. They were not removed by the capillary forces within the receding water front during the drying process. The strong interaction between the particles and the mica surface is corroborated by testing the adhesion of individual particles on the dried surface by means of the AFM tip: after a stepwise increase of the force applied to the surface by the AFM tip, the polymer particles still were not removed from the surface, but they were cut through and remained on the substrate. Moreover, in situ AFM measurements showed that particles which adsorb under liquid in a stable manner are easily desorbed from the surface after electrolyte is added to the suspension. This finding is explained by a decreasing attractive particle-substrate interaction, and the removal of the particles from the surface is due to the significant reduction of the activation barrier of the particle desorption. All findings can be explained in terms of the counterion release force.

Aluminum Silicates↗
PubMed2006

Decomposition of hydrogen peroxide driven by photochemical cycling of iron species in clay.

The reactivity of iron-bearing clays to catalyze the decomposition of hydrogen peroxide (H2O2) under light irradiation was investigated. Free iron oxides and structural iron in clay octahedral lattice are contained simultaneously in montmorillonite K10 (MK10), a representative natural clay mineral. By pretreatment of clay with the particular method, the reactivities of the two kinds of iron species were differentiated. It was found that free iron oxides on clay surface efficiently catalyzed the decomposition of H202 under UV light irradiation but structural iron in the octahedral lattice showed poor reactivity. This was found to result from the difference in production of Fe(II) species under UV irradiation between iron oxides and structural iron. When photoreactive substances such as N,N-dimethylaniline (DMA), rhodamine B (RhB), or malachite green (MG) were introduced, structural iron was found to promote greatly the decomposition of H202. The reduction of clay iron(II) to iron(II) is essential for the decomposition of H2O2, which is achieved by light-induced ligand to metal charge transfer (for iron oxides) or organic matters donating electrons upon irradiation (for structural iron). The light-induced redox cycling of iron did not lead to the release of iron and decomposition of H202 primarily localized on the clay surface. This work implies that iron-bearing clays could be a sink of H2O2 in the environmental system.

Aluminum Silicates↗
PubMed2006

Effect of surfactant and solvent properties on the stacking behavior of non-aqueous suspensions of organically modified clays.

Montmorillonite clay was treated with quaternary ammonium surfactants with 1-3 long chains of 10-18 carbons to form organoclays which can be suspended in non-aqueous solvents. The effects of surfactant chain length, number of long chains, and the properties of the solvent on the colloidal behavior of the surfactant coated clay plates were studied using small-angle X-ray scattering. The scattering data were modeled using a one-dimensional aggregation theory to describe the stacking of the clay plates. The plates self-organize into stacks with a reproducible basal spacing in the range of 30-50 A, and for each surfactant, the basal spacing falls into one of two preferred distances. We interpret this by considering that the surfactant layer on the clay has two strata, one being the polar near-clay headgroup region and the other the nonpolar alkane chain region. Polar solvents will swell the polar stratum preferentially while nonpolar solvents will swell the nonpolar stratum of the surfactant. As the nonpolar stratum is larger than the polar one, the nonpolar solvents increase the basal spacing between the clay plates more than the polar solvents. The number of long chains on the surfactant does not have an effect on the basal spacing, as the density of surfactant molecules on the surface is low enough to allow the unimpeded swelling of the chains. The one-dimensional aggregation theory can be used to determine the number of plates in a stack, but the effect of changing clay particle size or concentration is not as great as would be expected from this theory. This may be due to the formation of large-scale structures in the suspensions which prevent a true equilibrium stack size being attained.

Aluminum Silicates↗