[Shape-memory polymers for biomedical engineering applications].

Guangming Zhu; Zhongrang Liu

Home/Archive/PubMed

PubMed · 16294760

[Shape-memory polymers for biomedical engineering applications].

Guangming Zhu·Zhongrang Liu

View original source ↗Export metadata ↓

Abstract

The latest progress in shape-memory polymer for biomedical engineering applications was summarized in this paper. The mechanism responsible for shape memory effect was analyzed in reference to the polymer structure. Also introduced and reviewed were the characteristics of some shape-memory polymers (polyurethane polycaprolactone and polylactide) and their applications in medical engineering.

Explore related subjects

Alloys Biomedical Engineering Corrosion Elasticity Equipment and Supplies Materials Testing Polyesters Polymers Polyurethanes Journal Article Research Support, Non-U.S. Gov't Review

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Guangming Zhu, Zhongrang Liu. 2005. [Shape-memory polymers for biomedical engineering applications].. https://pubmed.ncbi.nlm.nih.gov/16294760/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Magnetic resonance imaging of phase transitions in nitinol.

Magnetic resonance images are prone to artifacts caused by metallic objects. Apart from being a source of image degradation, such artifacts can also provide information about the magnetic properties of the foreign object. In this work, we aim to explore the potential of magnetic resonance imaging to detect and characterize changes in magnetic properties of nitinol undergoing temperature- or strain-induced phase changes. A spin echo and a gradient echo method were used to measure the magnetization changes related to the phase transformations. Results of both methods were in agreement and in accordance with the independent measurements using a vibrating sample magnetometer. Magnetic resonance imaging turned out to be a suitable method to visualize and quantify magnetization and phase changes in situ. It is not restricted to a single imaging strategy and does not require any modification of the test object. The results indicate the potential of magnetic resonance imaging to provide direct feedback of the thermomechanical state of the alloy.

Alloys↗

PubMed2007

Human gingival fibroblast response to electropolished NiTi surfaces.

In the present study the in vitro biocompatibility of electropolished NiTi sheets is investigated. The assessment of cytotoxic effects due to potential Ni leaching from metal sheets was performed in direct contact with primary human fibroblast cultures using the 5-bromo-2'-deoxyuridine cell proliferation assay and morphologic studies via light microscopy and scanning electron microscopy. To assess toxic effects related to Ni-ions release, cells cultured in the presence of increasing concentrations of Ni(2+) (NiSO(4).6H(2)O) served as positive controls. It is shown that while the addition of NiSO(4) caused severe proliferation decrease (approximately 80%) and morphologic damage at a concentration of 50 mg/L Ni(2+) no negative effects were observed in fibroblasts cultured in the presence of electropolished NiTi sheets. The results are discussed in terms of surface topography effects on the biocompatibility of NiTi shape memory alloys.

Alloys↗

PubMed2007

Purified titanium oxide with novel morphologies upon spark anodization of Ti alloys in mixed H2SO4/H3PO4 electrolytes.

The spark anodization behavior of alpha/beta Ti6Al4V and Ti6Al7Nb alloys and of alpha c.p. Ti in H2SO4, H3PO4, and mixtures of these acids was studied. Chemical depth profiling revealed oxides purified with respect to the substrate alloying elements. This was particularly pronounced on Ti alloys spark anodized in H2SO4/H3PO4 mixtures, the Al content decreasing continuously towards the surface, and V and Nb hardly detectable in the outermost 200 nm. The incorporation of S was significantly reduced in mixed electrolytes, while about 8 at-% P was present. A novel oxide morphology with "worm-like" features in the micrometer range, very different from well-known nano/microporous oxides, was found in mixed electrolytes under suitable conditions. Similar but more porous-like morphologies were formed on Ti. Simple alpha/beta substrate microstructural considerations cannot explain the morphological and chemical observations. Raman spectroscopy indicated the presence of mixed anatase, rutile, and brookite phase on anodized Ti alloys. Bond strengths of 34 MPa for worm-like and 40-50 MPa for nano/microporous morphologies as well as excellent abrasion behavior were found. The compatibility of grit-blasting with the spark anodization process for creating multitopography surfaces was demonstrated. Neither the observed chemical effects, nor the observed particular morphology or the presence of brookite have been reported before.

Alloys↗