[Surface biochemical modification for the titanium implants].

Yanyan Zhuang·Ren Hu·Fei Chen·Haiyan Shi·Changjian Lin
View original source ↗Export metadata ↓

Abstract

This paper reviews the progress in biochemical design and modification for the surfaces of titanium implants in recent years, the emphasis being laid on the introduction of the surface molecular construction, self-assembly technique and its application in biomedical materials.

Explore related subjects

Biocompatible MaterialsProstheses and ImplantsSurface PropertiesTitaniumJournal ArticleReview

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Yanyan Zhuang, Ren Hu, Fei Chen, Haiyan Shi, Changjian Lin. 2005. [Surface biochemical modification for the titanium implants].. https://pubmed.ncbi.nlm.nih.gov/16013273/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Poly(lactic-co-glycolic acid) hollow fibre membranes for use as a tissue engineering scaffold.

Mass transfer limitations of scaffolds are currently hindering the development of 3-dimensional, clinically viable, tissue engineered constructs. We have developed a poly(lactide-co-glycolide) (PLGA) hollow fibre membrane scaffold that will provide support for cell culture, allow psuedovascularisation in vitro and provide channels for angiogenesis in vivo. We produced P(DL)LGA flat sheet membranes using 1, 4-dioxane and 1-methyl-2-pyrrolidinone (NMP) as solvents and water as the nonsolvent, and hollow fibre membranes, using NMP and water, by dry/wet- and wet-spinning. The resulting fibres had an outer diameter of 700 micro m and an inner diameter of 250 micro m with 0.2-1.0 micro m pores on the culture surface. It was shown that varying the air gap and temperature when spinning changed the morphology of the fibres. The introduction of a 50 mm air gap caused a dense skin of 5 micro m thick to form, compared to a skin of 0.5 micro m thick without an air gap. Spinning at 40 degrees C produced fibres with a more open central section in the wall that contained more, larger macrovoids compared to fibres spun at 20 degrees C. Culture of the immortalised osteogenic cell line 560pZIPv.neo (pZIP) was carried out on the P(DL)LGA flat sheets in static culture and in a P(DL)LGA hollow fibre bioreactor under counter-current flow conditions. Attachment and proliferation was statistically similar to tissue culture polystyrene on the flat sheets and was also successful in the hollow fibre bioreactor. The P(DL)LGA hollow fibres are a promising scaffold to address the size limitations currently seen in tissue engineered constructs.

Biocompatible Materials↗
PubMed2007

Effect of sterilization on the physicochemical properties of molded poly(L-lactic acid).

In this study, the process of manufacturing and sterilizing an orthopedic implant constructed from poly(L-lactic acid) (PLLA) was closely simulated. The hydrogen peroxide gas plasma (HPGP) sterilization process was comparatively investigated against ethylene oxide (EtO). Characterization of the physical, thermal, mechanical, morphological, and chemical properties was monitored. The results indicate that the HPGP sterilization process did not have a significant influence on M(n) or M(w) initially or through 12 weeks of in vitro conditioning when compared with EtO. Only indications of physical aging were evident in the analysis of the thermal and mechanical properties by differential scanning calorimeter and tensile testing for each sterilization processes. Using wide angle X-ray diffraction to determine morphology characteristics, it was determined that no changes were observed between the as molded, HPGP, and EtO specimens initially or through the 12 week in vitro conditioning period. Contact angle measurements revealed a significant reduction in the surface energy following treatment by the HPGP process, suggesting the formation of polar groups. However, surface chemistry analysis by ATR-FTIR indicated no significant chemical modification from either sterilization method. PLLA showed intermediate levels of residual hydrogen peroxide absorption following processing by HPGP.

Biocompatible Materials↗
PubMed2007

Equivalences between refractive index and equilibrium water content of conventional and silicone hydrogel soft contact lenses from automated and manual refractometry.

PURPOSE: The purpose of the present study was to develop mathematical relationships that allow obtaining equilibrium water content and refractive index of conventional and silicone hydrogel soft contact lenses from refractive index measures obtained with automated refractometry or equilibrium water content measures derived from manual refractometry, respectively. METHODS: Twelve HEMA-based hydrogels of different hydration and four siloxane-based polymers were assayed. A manual refractometer and a digital refractometer were used. Polynomial models obtained from the sucrose curves of equilibrium water content against refractive index and vice-versa were used either considering the whole range of sucrose concentrations (16-100% equilibrium water content) or a range confined to the equilibrium water content of current soft contact lenses (approximately 20-80% equilibrium water content). RESULTS: Values of equilibrium water content measured with the Atago N-2E and those derived from the refractive index measurement with CLR 12-70 by the applications of sucrose-based models displayed a strong linear correlation (r2 = 0.978). The same correlations were obtained when the models are applied to obtain refractive index values from the Atago N-2E and compared with those (values) given by the CLR 12-70 (r2 = 0.978). No significantly different results are obtained between models derived from the whole range of the sucrose solution or the model limited to the normal range of soft contact lens hydration. CONCLUSIONS: Present results will have implications for future experimental and clinical research regarding normal hydration and dehydration experiments with hydrogel polymers, and particularly in the field of contact lenses.

Biocompatible Materials↗