Self-curing, self-etching adhesive cement systems.

Ulrich Salz·Jörg Zimmermann·Tobias Salzer
View original source ↗Export metadata ↓

Abstract

PURPOSE: To investigate the influence of the acid-base reaction between acidic monomers and amines on the polymerization behavior of self-etching, self-curing adhesives, determine the effect of the application mode on the shear bond strength and morphology, and elucidate the adhesion performance of such systems by shear bond strength measurements. MATERIALS AND METHODS: The amine redox-initiator system N,N-di(2-hydroxyethyl)p-toluene (DEPT)/dibenzoyl peroxide (BPO) was selected to investigate the influence of the amine-base reaction on polymerization behavior. The PKa value of DEPT hydrochloride was measured by titration with NaOH. The influence of the pH value and DEPT concentration on the polymerization rate of methacrylates was investigated by exotherm time measurements. Three different application protocols of Multilink Primer (Ivoclar Vivadent) and Panavia 21 ED-Primer (Kuraray) were tested, 15 s passive vs 15 s agitation vs 60 s passive in combination with the corresponding resin luting material. The effects of these three application protocols were evaluated and monitored by both shear bond strength tests and SEM characterization of the surface morphology. The adhesion potential of these self-etching, self-curing luting systems was compared on enamel and dentin both directly after application and after 24 h. RESULTS: The pKa of DEPT-HCl is 4.45. The polymerization rate of the DEPT-containing, self-etching, self-curing adhesive system is highly influenced by both the amine concentration and the pH value. In the case of Multilink, agitation of the primer mixture for 15 s, especially on dentin, resulted in a higher bond strength and a more pronounced removal of the smear layer. Multilink resulted in statistically higher bond strengths (p < 0.05) than Panavia 21 for both the enamel and dentin directly after application and for the dentin after 24 h. CONCLUSION: Radical polymerization initiators used in self-curing systems are strongly adversely affected by acidic monomers incorporated in self-etching adhesives. However, if there is a good adjustment of these components and effects of adhesive application are taken in account, high bond strengths can be achieved.

Explore related subjects

Acid Etching, DentalAdhesivesAminesAnalysis of VarianceDental BondingDental Enamel PermeabilityDental Stress AnalysisDentin PermeabilityHydrogen-Ion ConcentrationMaterials TestingOxidation-ReductionPeroxidesPhase TransitionPhosphatesResin CementsShear StrengthTerpenesToluidinesComparative StudyJournal Article

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Ulrich Salz, Jörg Zimmermann, Tobias Salzer. 2005. Self-curing, self-etching adhesive cement systems.. https://pubmed.ncbi.nlm.nih.gov/15892359/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Resin strengthening of dental ceramics- the impact of surface texture and silane.

OBJECTIVES: To examine the effect of porcelain surface texture achieved utilising three clinically relevant surface preparation methods prior to silane and unfilled resin application on the flexure strength of a low fusing feldspathic porcelain. MATERIALS AND METHODS: Five hundred and forty dentine disc-shaped specimens (15.0mm diameter and 0.9mm thickness) were condensed, fired and allocated to 18 groups. Six groups were stored as-fired, six were alumina abraded and six were acid-etched. Samples were coated with silane, unfilled resin or both prior to bi-axial flexure testing. Group means were compared utilising a three factor design general linear model and post hoc all paired Tukey tests at P<0.05. Weibull analysis was employed to examine the reliability of the strength data. Profilometry was used to characterise the surface texture of the specimen surfaces. RESULTS: Alumina abraded and acid-etched specimens had significantly lower flexure strengths than the as-fired specimens. A significant difference between the degree of strengthening observed following unfilled resin application on the three surface texture investigated was observed (P<0.001). Silane application prior to resin coating resulted in no further significant increases in the mean bi-axial flexure strengths of the three surface textures. The as-fired surfaces had a low frequency of irregular amplitude defects, alumina abraded surfaces had an increased frequency of regular amplitude defects whilst the acid-etched surface consisted of an increased frequency of irregular amplitude defects. CONCLUSION: The strengthening mechanism whilst dependent on surface texture was independent of defect severity. No significant strengthening occurred following silane priming suggesting that, for the unfilled resin utilised, the strengthening mechanism was not enhanced by improved resin-ceramic adhesion.

Acid Etching, Dental↗
PubMed2007

Effect of different types of enamel conditioners on the bond strength of orthodontic brackets.

AIM: A unique characteristic of some new bonding systems in operative dentistry is they combine conditioning and priming agents into a single acidic primer solution for simultaneous use on both enamel and dentin. Combining conditioning and priming into a single treatment step results in improvement in both time and cost-effectiveness to the clinician and, indirectly, to the patient. The purpose of this study was to determine the effects of the use of a self-etching primer on the bond strength of orthodontic brackets and on the bracket/adhesive failure mode. METHODS AND MATERIALS: Thirty-six fresh bovine incisors were collected and stored in a solution of 0.1% (weight/volume) thymol. The criteria for tooth selection included intact buccal enamel, no cracks caused by the presence of the extraction forceps, and no defects. The teeth were cleansed and polished with pumice and rubber prophylactic cups for ten seconds. Brackets were bonded to the teeth according to one of three protocols following the manufacturers' instructions--Group 1: Conventional multistep bonding system (control group) (n=12); Group 2: Self-etching primer system (n=12); and Group 3: Acid+self-etching primer system (n=12). Specimens were loaded to failure in a Zwick test machine (Zwick GmbH & Co, Ulm, Germany). Shear bond strengths were measured at a crosshead speed of 5 mm/min. RESULTS: The mean shear bond strength in megapascals (Mpa) (standard deviation) were 11.7 (4.2), 10.5 (4.4), and 10.9 (4.8) for Groups 1, 2, and 3, respectively. The analysis of variance (ANOVA) was used to compare the three groups. The results indicated no significant difference in the bond strength between the three groups (P=0.800). The results of the Chi square test, evaluating the residual adhesives on the enamel surfaces, revealed no significant difference between the three groups (P=0.554). CONCLUSION: Results of the present in vitro study indicate the use of self-etching primers may be an alternative to conventional phosphoric acid pre-treatment in orthodontic bonding.

Acid Etching, Dental↗
PubMed2007

Removal of noncollagenous components affects dentin bonding.

The structural integrity of fibrillar type I collagen is critical for effective dentin bonding. Since most noncollagenous matrix components in dentin are closely associated with collagen, we hypothesized that they may also contribute to dentin bonding. To test this hypothesis, bovine dentin was acid-etched, treated with chondroitinase ABC (C-ABC), endo-beta-galactosidase (Endo-beta), or trypsin. Controls were prepared in the same manner but without the enzymes. All control and experimental specimens were then bonded with One-Step. Bond strength data were analyzed by one-way ANOVA and Fisher's PLSD test (p < 0.05). When dentin was treated with C-ABC or trypsin, bond strengths significantly decreased for the rewetted groups (p < 0.05). The treatment with Endo-beta showed no effects on bond strengths (p > 0.05). When the treated dentin surfaces were observed under SEM, the C-ABC and trypsin treated groups revealed significant loss of collagen fibril architecture. The results indicate that chondroitin sulfate glycosaminoglycans and trypsin-digestible noncollagenous proteins play roles in maintaining the open dimensions of the collagen fibril scaffold, which is essential for optimal dentin bonding.

Acid Etching, Dental↗