Disclosing medium for adjusting removable partial denture framework.

Pure titanium and titanium alloys are potential materials for the fabrication of cast dental appliances. One important factor in producing sound castings is the capacity of the metal to fill the mold. This study used a wedge-shaped mold to compare the mold filling of titanium with that of conventional dental casting alloys. The metals used were CP Ti, Ti-6Al-7Nb, Ti-6Al-4V, Ti with 1 and 4wt% Cu and ADA Type III gold alloy and an Ni-Cr alloy. The castings were cut into four pieces parallel to the triangular surface. Mold filling was evaluated as the distance between the tip of the cast wedge and theoretical tip of the triangle. The mold filling of the gold alloy was superior compared to all the metals tested, while the mold filling of the Ni-Cr alloy was the worst. There were no statistical differences at the 30 degrees marginal angle for all the cast titanium metals. At the sharper 15 degrees angle, CP Ti and Ti-6Al-7Nb was superior to both the Ti-Cu alloys. Although the mold filling of titanium was inferior compared to the gold alloy, the data justify the use of titanium for the production of dental appliances.

Dental Alloys↗

PubMed2002

Elastic flexural properties of multistranded stainless steel versus conventional nickel titanium archwires.

Based on a recent investigation that modeled the elastic properties (ie, strength, stiffness and range) of multistranded wires made from linearly elastic materials, three-stranded (triple) and six-stranded coaxial (coax) stainless steel (SS) wires were compared to single-stranded (single) SS and conventional nickel titanium (NiTi) leveling wires. To measure Young's modulus of elasticity (E), flexural tests were performed with an Instron mechanical testing machine in a three-point bending arrangement having a span length of 8.9 mm or 12.5 mm. A strong correlation between wire stiffness and the area moment of inertia demonstrated that strand interaction was negligible at low activations and that E = 199 GPa was constant even for the heavily drawn coax strands. Using the Instron with an extensometer, the 0.1% yield strengths (sigma(YS)) of the single SS wires and the straight inner strands within the coax wires were tested. The ratio of the sigma(YS) to the ultimate tensile strength averaged 0.81 for the single wires, 0.88 for the coax wires, and was subsequently assigned 0.85 for the triple wires. The average sigma(YS) values were 1.88, 1.83, and 1.78 GPa for the single, triple, and coax SS wires, respectively. For each NiTi wire, both the sigma(YS) and the elastic limit (sigma(EL)) via cyclic loading were measured. The conventional NiTi wires displayed nonlinear elasticity, as the average sigma(EL) values (1.10 GPa) were 50% higher than the average sigma(YS) values (0.73 GPa). Compared to the elastic properties of the conventional NiTi wires, the triple and coax SS wires generally matched the stiffness, but had only one-third to one-half of the strength and range. Since the properties of strength and range are both proportional to sigma(YS), fabrication using alloys with enhanced sigma(YS) values would allow multistranded SS archwires to compete better against conventional NiTi products.

Dental Alloys↗

PubMed2002

Influence of rotational speed, torque and operator proficiency on failure of Greater Taper files.

AIM: The purpose of this study was to evaluate the influence of rotational speed. torque, and operator experience on the incidence of locking, deformation, and separation of instruments when using a specific Ni-Ti rotary instrumentation technique in extracted human teeth. METHODOLOGY: Greater Taper Ni-Ti rotary instruments (GT) were used in a crown-down technique. In one group (rotational speed evaluation) of canals (n = 300) speeds of 150, 2 50 and 350 r.p.m. (subgroups 1, 2 and 3) were used. Each one of the subgroups included 100 canals. In a second group (evaluation of torque) (n = 300) torque was set at 20, 30 and 55 Ncm (subgroups 4, 5 and 6). In the third group (evaluation of operator proficiency) (n = 300 three operators with varying experience (subgroups 7, 8 and 9) were also compared. Each subgroup included the use of 10 sets of GT rotary instruments and 100 canals of extracted human molars. Each set of instruments was used in up to 10 canals and sterilized before each case. NaOCl 2.5% was used as an irrigant. The number of locked, deformed, and separated instruments was recorded for each group. Statistical analysis was carried out with pairwise comparisons using Fisher's exact tests for each of the failure type. RESULTS: When the influence of rotational speed was evaluated, instrument deformation and separation did not occur in subgroups 1 (150) r.p.m.), 2 (250 r.p.m.), and 3 (350) r.p.m.). Instrument locking occurred in subgroup 3 only. Statistical analysis demonstrated a significant difference between the 150 and 350 r.p.m. groups and between the 250 and 350 r.p.m. groups with respect to instrument locking. In torque evaluation, neither separation, deformation nor locking occurred during the use of the instruments, at 150 r.p.m., and at the different torque values. When the operators were compared, although two instruments were separated in canals prepared by the least experienced operator. Fisher's exact tests did not demonstrate a significant difference between the three subgroups. Instrument locking, deformation, and separation did not occur with the most experienced operator. None of the instruments separated with the trained operator. CONCLUSIONS: Preclinical training in the use of the GT rotary instruments when used with a crown-down technique at 150 r.p.m. was crucial in avoiding instrument separation and reducing the incidence of instrument locking and deformation.

Dental Alloys↗