PubMed · 15378977
The source did not provide an abstract. Follow the original record for more information.
Explore connections, maps & timelines
Julian Webber. 2004. ProTaper for hand use.. https://doi.org/10.1111/j.1747-4477.2004.tb00193.x
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
This study investigated the effect of laser-beam welding conditions [voltage (V) and spot diameter (mm)] on the penetration depth into dental casting alloys. Castings (3.0 mm x 8.0 mm x 50 mm) were prepared from the metals used in this study: commercially pure titanium (CP Ti), Ti-6Al-4V, Ti-6Al-7Nb, cobalt-chromium alloy (Co-Cr) and Type IV gold alloy. Two cast blocks of each metal were butted against one another at the 8.0 x 50-mm surfaces. They were then welded at their interface under the following conditions: voltage of 160-340 V, spot diameter of 0.4-1.6 mm, and pulse duration of 10 ms. After laser welding, the blocks were separated, and the penetration depth into each alloy was measured. The data were analyzed with the use of ANOVA at the p < 0.05 level of significance. The penetration depths were as follows: CP Ti (0.29-6.45 mm), Ti-6Al-4V (0.32-5.24 mm), Ti-6Al-7Nb (0.34-5.65 mm), Co-Cr (0.24-6.15 mm), and Type IV gold alloy (0.12-5.22 mm). The voltage and spot diameter affected the penetration depth into the metals tested. When the voltage increased and the spot diameter decreased, the penetration depth increased for each metal. Selecting suitable conditions for laser welding to obtain sufficient penetration depth for the optimal thickness of the metal is important when welding prostheses.
OBJECTIVES: Since the low friction of NiTi wires allows a rapid and efficient orthodontic tooth movement, the aim of this research was to investigate the friction and surface roughness of different commercially available superelastic NiTi wires before and after clinical use. The surface of all of the wires had been pre-treated by the manufacturer. MATERIALS: Forty superelastic wires (Titanol Low Force, Titanol Low Force River Finish Gold, Neo Sentalloy, Neo Sentalloy Ionguard) of diameter 0.016 x 0.022 in. were tested. The friction for each type of NiTi archwire ligated into a commercial stainless steel bracket was determined with a universal testing machine. Having ligated the wire into the bracket, it could then be moved forward and backwards along a fixed archwire whilst a torquing moment was applied. The surface roughness was investigated using a profilometric measuring device on defined areas of the wire. Statistical data analysis was conducted by means of the Wilcoxon test. RESULTS: The results showed that initially, the surface treated wires demonstrated significantly (p < 0.01) less friction than the non-treated wires. The surface roughness showed no significant difference between the treated and the non-treated surfaces of the wires. All 40 wires however showed a significant increase in friction and surface roughness during clinical use. SIGNIFICANCE: Whilst the Titanol Low Force River Finish Gold (Forestadent, Pforzheim, Germany) wires showed the least friction of all the samples and consequently should be more conservative on anchorage, the increase in friction of all the surface treated wires during orthodontic treatment almost cancels out this initial effect on friction. It is therefore recommended that surface treated NiTi orthodontic archwires should only be used once.
STATEMENT OF PROBLEM: It is not known whether different high-palladium alloys of similar composition possess comparable tensile strength properties associated with connector soldering. PURPOSE: The purpose of this study was to evaluate the tensile strength properties of 2 high-palladium alloys on soldered connectors under simulated pre-ceramic and post-ceramic soldering conditions. MATERIAL AND METHODS: Eighty cylindrical castings were fabricated (Rx Naturelle Plus alloy and Option alloy). The 40 castings for each alloy were subdivided into 2 groups of 20 each. In the first group, castings for each alloy were randomly paired and soldered with presolder (SMG2) to produce 10 preceramic test connector specimens for each alloy. In the second group, castings were similarly paired and soldered with postsolder (490 fine) to produce 10 postceramic test connector specimens for each alloy. Each soldered connector was subjected to tensile force until failure in a universal testing machine. Statistical analysis using a Wilcoxon rank sums test was performed (alpha=.05) RESULTS: No significant difference was found between the mean tensile failure stress for Rx Naturelle Plus preceramic solder (344.7 +/- 77.6 MPa) compared to Option preceramic solder (411.5 +/- 112.8 MPa) (P =.1202). However, the mean tensile failure stress for Rx Naturelle Plus postceramic solder (260.8 +/- 223.7 MPa) was significantly lower than the Option postceramic solder (312.6 +/- 120.8 MPa) (P =.0407). Not only did Rx Naturelle Plus postceramic solder connectors show evidence of lower strength, but also an increased variation among specimens. CONCLUSIONS: Rx Naturelle Plus solder connectors provided better strength with the preceramic as opposed with the postceramic connectors. For postsolder connectors, Rx Naturelle Plus alloy had less acceptable strength and a wider variation, suggesting it is more technique sensitive than Option alloy connectors.