Solid state NMR and DSC methods for quantifying the amorphous content in solid dosage forms: an application to ball-milling of trehalose.

R Lefort; A De Gusseme; J-F Willart; F Danède; M Descamps

doi:10.1016/j.ijpharm.2004.05.012

Home/Archive/PubMed

PubMed · 15265560

Solid state NMR and DSC methods for quantifying the amorphous content in solid dosage forms: an application to ball-milling of trehalose.

R Lefort·A De Gusseme·J-F Willart·F Danède·M Descamps

View original source ↗Export metadata ↓

Abstract

The purpose of this study was to determine quantitatively the amorphous fraction in crystalline-amorphous powder mixtures of trehalose, in order to assess the ability of the (13)C NMR technique for quantitative amorphous characterization. The NMR method is described in detail and its accuracy is compared to that of the DSC technique. Amorphous trehalose was prepared by mechanical milling. Samples with different amorphous fractions were prepared by physical mixing of purely amorphous and purely crystalline powders. The results reveal a close correlation between the imposed compositions of the physical mixtures and those determined by NMR and DSC, indicating that both are useful and accurate methods for compositional characterization of powders. The NMR method is then used to determine the evolution of the amorphous fraction in a trehalose powder, during a milling procedure which ultimately leads to a fully amorphous state.

Explore related subjects

Calorimetry, Differential Scanning Dosage Forms Magnetic Resonance Spectroscopy Trehalose Comparative Study Journal Article Research Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

R Lefort, A De Gusseme, J-F Willart, F Danède, M Descamps. 2004-08-06. Solid state NMR and DSC methods for quantifying the amorphous content in solid dosage forms: an application to ball-milling of trehalose.. https://doi.org/10.1016/j.ijpharm.2004.05.012

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Relationship between blood compatibility and water structure--comparative study between 2-methoxyethylacrylate- and 2-methoxyethylmethacrylate-based random copolymers.

We have proposed that the excellent blood compatibility of poly(2-methoxyethylacrylate (MEA)) is caused by freezing bound water contained in it on the basis of results on platelet activation (Tanaka and Mochizuki, J Biomed Mater Res A 2004; 68:684-695). To clarify the applicability of this mechanism to other indexes for blood compatibility, the relationship between complement activation and water structure was investigated by using two copolymers, poly(MEA-2-hydroxyethylmethacrylate (HEMA)) and poly(2-methoxyethylmethacrylate (MEMA)-HEMA), where HEMA content was varied from 25 to 90 mol %. ESCA analysis revealed that the surface compositions of these copolymers (dry state) agreed with the compositions determined by (1)H NMR. However, analysis by water contact angle (wet state) showed that their surfaces were quite different. The contact angle of poly(MEMA-HEMA) depended on the monomer composition, whereas the angle of poly(MEA-HEMA) was close to that of polyHEMA regardless of the monomer composition. The effect of HEMA content in the copolymers on complement activation (production of C3a) was investigated in an in vitro test. The activation by poly(MEMA-HEMA) was enhanced according to the HEMA content, while the activation by poly(MEA-HEMA) with 0-40 mol % of HEMA was weak and did not depend on the HEMA content. These properties are discussed from the viewpoints of the water structure observed by DSC and the surface structure.

Calorimetry, Differential Scanning↗

PubMed2007

Shape dependence in the formation of condensed phases exhibited by disubstituted sucrose esters.

We report on the self-organizing properties of sucrose esters that are di-(1',6', 1',6, and 6,6')-substituted with aliphatic chains of identical or different chain lengths and levels of saturation. For the materials possessing two saturated aliphatic chains, the compounds exhibited thermotropic lamellar smectic A phases. A remarkable new phase transition was observed for the di-octadecanoyl homologue in which one smectic A phase transformed into another with a continuous change in layer spacing, but with a discontinuous change in the correlation length. The incorporation of long cis-unsaturated chains led to increased cross-sectional areas of the chains relative to the sucrose head groups and, hence, columnar phases were observed.

Calorimetry, Differential Scanning↗

PubMed2007

Photoluminescence and conductivity of self-assembled pi-pi stacks of perylene bisimide dyes.

The self-assembly of a new, highly fluorescent perylene bisimide dye 2 into pi stacks, both in solution and condensed phase, has been studied in detail by NMR spectroscopy, vapor pressure osmometry (VPO), UV/Vis and fluorescence spectroscopy, differential scanning calorimetry (DSC), optical polarizing microscopy (OPM) and X-ray diffraction. The NMR and VPO measurements revealed the formation of extended pi-pi stacks of the dye molecules in solution. The aggregate size determined from VPO and DOSY NMR measurements agree well with that obtained from the concentration and temperature-dependent UV/Vis spectral data by employing the isodesmic model (equal K model). In the condensed state, dye 2 possesses a hexagonal columnar liquid crystalline (LC) phase as confirmed by X-ray diffraction analysis. The columnar stacking of this dye has been further explored by atomic force microscopy (AFM). Well-resolved columnar nanostructures of the compound are observed on graphite surface. A color-tunable luminescence from green to red has been observed upon aggregation which is accompanied by an increase of the fluorescence lifetime and depolarization. The observed absorption properties can be explained in terms of molecular exciton theory. The charge transport properties of dye 2 have been investigated by pulse radiolysis-time resolved microwave conductivity measurements and a 1D charge carrier mobility up to 0.42 cm(2) V(-1) s(-1) is obtained. Considering the promising self-assembly, semiconducting, and luminescence properties of this dye, it might serve as a useful functional material for nano(opto)electronics.

Calorimetry, Differential Scanning↗