Superelastic nickel-titanium wires.

N E Waters
View original source ↗Export metadata ↓

Abstract

Superelastic nickel-titanium archwires, unlike conventional wires, are capable of withstanding very large deflections and on returning to their original shape on deactivation will produce more moderate forces. The region over which there is a 'plateau' depends on the deflection and is greater the larger the deflection. With most wires both the initial wire stiffness in bending and the 'plateau' deactivation loads are very dependent on temperature. Wire size is no longer a guide to wire behaviour and force values for a given temperature and for wires of the same nominal diameter from different manufacturers can vary by a factor of six.

Explore related subjects

Dental AlloysElasticityNickelOrthodontic WiresStress, MechanicalSurface PropertiesTitaniumJournal ArticleReview

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

N E Waters. 1992. Superelastic nickel-titanium wires.. https://doi.org/10.1179/bjo.19.4.319

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2005

Penetration depth into dental casting alloys by Nd:YAG laser.

This study investigated the effect of laser-beam welding conditions [voltage (V) and spot diameter (mm)] on the penetration depth into dental casting alloys. Castings (3.0 mm x 8.0 mm x 50 mm) were prepared from the metals used in this study: commercially pure titanium (CP Ti), Ti-6Al-4V, Ti-6Al-7Nb, cobalt-chromium alloy (Co-Cr) and Type IV gold alloy. Two cast blocks of each metal were butted against one another at the 8.0 x 50-mm surfaces. They were then welded at their interface under the following conditions: voltage of 160-340 V, spot diameter of 0.4-1.6 mm, and pulse duration of 10 ms. After laser welding, the blocks were separated, and the penetration depth into each alloy was measured. The data were analyzed with the use of ANOVA at the p < 0.05 level of significance. The penetration depths were as follows: CP Ti (0.29-6.45 mm), Ti-6Al-4V (0.32-5.24 mm), Ti-6Al-7Nb (0.34-5.65 mm), Co-Cr (0.24-6.15 mm), and Type IV gold alloy (0.12-5.22 mm). The voltage and spot diameter affected the penetration depth into the metals tested. When the voltage increased and the spot diameter decreased, the penetration depth increased for each metal. Selecting suitable conditions for laser welding to obtain sufficient penetration depth for the optimal thickness of the metal is important when welding prostheses.

Dental Alloys↗
PubMed2004

Morphometric analysis of the effectiveness of different concentrations of sodium hypochlorite associated with rotary instrumentation for root canal cleaning.

This study evaluated the cleaning capacity of Profile.04 instruments with different concentrations of NaOCl solutions on flattened root canals. Twenty central mandibular incisors were divided into 4 groups: Group I: 0.5% NaOCl; Group II: 1% NaOCl; Group III: 5% NaOCl; Group IV: distilled and deionized water. After chemomechanical preparation, the teeth were submitted to histological preparation and morphometric analysis. Morphometric analysis showed that the 5% NaOCl was significantly more efficient in cleaning the root canal than 0.5% NaOCl and distilled water, which had the lowest levels of cleaning of the root canals (p<0.01).

Dental Alloys↗
PubMed2004

Materials-induced variation in the torque expression of preadjusted appliances.

The purpose of this article is to comprehensively investigate the sources of variation in the expression of torque in preadjusted appliances. Variables related to properties of materials were systematically analyzed, including (1) the inability to fill the slot because of the size difference of archwires and bracket slot, (2) irregularities from the manufacturing process of brackets precluding proper engagement, (3) differences in the stiffness of wire alloys engaged to the bracket slot, (4) variations between actual and reported bracket torque values, and (5) ligation modes, all of which might account for increased third-order clearance or bracket-archwire "play." The effect of these variations on the expression of torque is discussed, and the net buccolingual inclinations are provided as a function of wire size and composition for common bracket slot-archwire combinations. Most reports published on this issue indicate a loss of torque control as high as 100% of the prescribed value. Furthermore, the fallacy of transferring the ideal crown inclination to the torque prescribed in the bracket is illustrated, along with the underestimation of the prescribed torque relative to the proper tooth crown. The realistically required torque is analyzed to its constituent components, involving tooth inclination, compensation for the slot-wire play, and incomplete ligation with elastomeric ligatures. Based on the evidence available, it is proposed that a high-torque prescription should be selected to account for the lack of full expression of the prescribed torque that occurs clinically.

Dental Alloys↗