Resin pattern material with low polymerization shrinkage.

J Takahashi; K Kitahara; F Teraoka; F Kubo

PubMed · 10635201

Resin pattern material with low polymerization shrinkage.

Abstract

PURPOSE: The purpose of this study was to develop a material with low polymerization shrinkage for resin patterns to improve the fit of a long superstructure to implants. MATERIALS AND METHODS: Three different chemical substances were added at 1, 2, 3, 5, 10, and 20 wt% to the liquid component of a self-curing acrylic resin. Specimens for measuring shrinkage during self curing were prepared in a metal mold that took the form of a conical cavity with slightly tapered walls. The specimens were prepared using three different methods: (1) a brush-on technique, (2) an injection method, and (3) an injection-press method. The percentage of linear shrinkage was calculated from the protrusion of the specimen from the bottom of the cavity. RESULTS: The injection-press method and the brush-on method gave the lowest polymerization shrinkage results (P < 0.05). The standard deviation of the former method was smaller than that of the latter. The linear shrinkage in the injection-press method decreased with the increase of the powder-to-liquid ratio (P < 0.05). All three additives reduced shrinkage to about 1/3 of the shrinkage of the basic resin using the injection-press method and a 2.00:1.00 powder-to-liquid ratio. CONCLUSION: The addition of three different chemical substances to liquid reduces linear shrinkage to about 1/3 of the shrinkage of the original self-curing acrylic resin.

Explore related subjects

Acrylic Resins Alcohols Analysis of Variance Dental Casting Investment Dental Prosthesis Design Dental Prosthesis, Implant-Supported Indenes Materials Testing Morpholines Polymers Statistics, Nonparametric Comparative Study Journal Article Research Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

J Takahashi, K Kitahara, F Teraoka, F Kubo. Resin pattern material with low polymerization shrinkage.. https://pubmed.ncbi.nlm.nih.gov/10635201/

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Calcium polycarbophil improves constipation in primary autonomic failure and multiple system atrophy subjects.

Explore the source record for details and available documents.

Acrylic Resins↗

PubMed2007

Influence of the activator in an acrylic bone cement on an array of cement properties.

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

Acrylic Resins↗

PubMed2007

Dynamic scaling of polymer gels comprising nanoparticles.

We present dynamic light scattering (DLS) measurements of soft poly(methyl-methacrylate) (PMMA) and polyacrylamide (PA) polymer gels prepared with trapped bodies (latex spheres or magnetic nanoparticles). We show that the anomalous diffusivity of the trapped particles can be analyzed in terms of a fractal Gaussian network gel model for the entire time range probed by DLS technique. This model is a generalization of the Rouse model for linear chains extended for structures with power law network connectivity scaling, which includes both percolating and uniform bulk gel limits. For a dilute dispersion of strongly scattering particles trapped in a gel, the scattered electric field correlation function at small wavevector ideally probes self-diffusion of gel portions imprisoning the particles. Our results show that the time-dependent diffusion coefficients calculated from the correlation functions change from a free diffusion regime at short times to an anomalous subdiffusive regime at long times (increasingly arrested displacement). The characteristic time of transition between these regimes depends on scattering vector as approximately q(-2), while the time decay power exponent tends to the value expected for a bulk network at small q. The diffusion curves for all scattering vectors and all samples were scaled to a single master curve.

Acrylic Resins↗