Yin Chiang Freddy Boey

Publications and source records attributed to Yin Chiang Freddy Boey.

4 recordsLinked to original sources

PubMed2005

Hydrolytic degradation of electron beam irradiated high molecular weight and non-irradiated moderate molecular weight PLLA.

The purpose of this study is to examine the hydrolytic degradation of electron beam irradiated ring-opening polymerized (ROP) poly(l-lactide) (PLLA-ir) and non-irradiated melt polycondensation polymerized poly(l-lactic acid) (PLLA-pc). It was observed that irradiation increases the hydrolytic degradation rate constant for ROP PLLA. This was due to a more hydrophilic PLLA-ir, as a result of irradiation. The degradation rate constants (k) of PLLA-ir samples were also found to be similar, regardless of the radiation dose, and an empirically formulated equation relating hydrolytic degradation time span to radiation dose was derived. The k value for PLLA-pc was observed to be lower than that for PLLA-ir, though the latter had a higher molecular weight. This was due to the difference in degradation mechanism, in which PLLA-ir undergoes end group scission, through a back- biting mechanism, during hydrolysis and thus a faster hydrolysis rate. Electron beam irradiation, though accelerates the degradation of PLLA, has been shown to be useful in accurately controlling the hydrolytic time span of PLLA. This method of controlling the hydrolytic degradation time was by far an easier task than through melt polycondensation polymerization. This would allow PLLA to be used for drug delivery purposes or as a temporary implant that requires a moderate time span (3-6 months).

Electrons↗

PubMed2005

Biodegradable stents with elastic memory.

This work reports, for the first time, the development of a fully biodegradable polymeric stent that can self-expand at body temperatures (approximately 37 degrees C), using the concept of elastic memory. This self-expansion is necessary in fully polymeric stents, to overcome the problem of elastic recoil following balloon expansion in a body vessel. Bi-layered biodegradable stent prototypes were produced from poly-L-lactic acid (PLLA) and poly glycolic acid (PLGA) polymers. Elastic memory was imparted to the stents by temperature conditioning. The thickness and composition of each layer in the stents are critical parameters that affect the rate of self-expansion at 37 degrees C, as well as the collapse strengths of the stents. The rate of self-expansion of the stents, as measured at 37 degrees C, exhibits a maximum with layer thickness. The Tg of the outer layer is another significant parameter that affects the overall rate of expansion.

Absorbable Implants↗

PubMed2005

Effect of isothermal annealing on the hydrolytic degradation rate of poly(lactide-co-glycolide) (PLGA).

Isothermal crystallization through annealing at 115 degrees C was conducted to increase the degree of crystallinity of poly (lactide-co-glycolide) (PLGA). The maximum increase in the degree of crystallinity (approximately 21%) was achieved after 60 min of annealing. The crystal size/perfection was observed to increase with annealing time. The annealed PLGA films were then hydrolytically degraded in phosphate buffered saline solution of pH 7.4 at 37 degrees C for up to 150 days. Minimal mass loss was observed throughout the time investigated, suggesting that the samples were still in the first phase of degradation. The increase in the degree of crystallinity of the PLGA samples annealed at 15 and 30 min was found to retard their overall rate of hydrolytic degradation, when compared to those samples with higher initial crystallinity (annealed for 45 and 60 min) that had faster degradation rates. The increased degradation rate at higher crystallinity was associated with the loss of amorphous material and the formation of voids during annealing, which decreases the glass transition temperature and increases the average water uptake in the samples annealed for longer times. Therefore, the increase in degree of crystallinity is found to retard hydrolytic degradation but only to a certain extent, beyond which the formation of voids through annealing increases the rate of hydrolytic degradation.

Biocompatible Materials↗

PubMed2005

Influence of electron-beam radiation on the hydrolytic degradation behaviour of poly(lactide-co-glycolide) (PLGA).

The purpose of this study is to examine the effect of electron-beam (e-beam) radiation on the hydrolytic degradation of poly(lactide-co-glycolide) (PLGA) films. PLGA films were irradiated and observed to undergo radiation-induced degradation through chain scission, as observed from a drop in its average molecular weight with radiation dose. Irradiated (5, 10 and 20 Mrad) and non-irradiated (0 Mrad) samples of PLGA were subsequently hydrolytically degraded in phosphate-buffered saline solution at 37.0 degrees C over a span of 12 weeks. It was observed that the natural logarithmic molecular weight (lnMn) of PLGA decreases linearly with hydrolytic degradation time. The rate of water uptake is higher for samples irradiated at higher radiation dose (e.g. 20 Mrad) and subsequently causing an earlier onset of mass loss. It is postulated that the increase in water uptake is due to the presence of more hydrophilic end groups, which results in the formation of microcavities because of an increase in osmotic pressure. A relationship between radiation dose and the rate of hydrolytic degradation of PLGA films, through its molecular weight was also established. This relationship allows a more accurate and precise control of the life span of PLGA through the use of e-beam radiation.

Absorbable Implants↗