Osteoblastic cell response on fluoridated hydroxyapatite coatings.

Fluoridated hydroxyapatite (FHA) coatings were deposited onto Ti6Al4V substrates by sol-gel dip-coating method. X-ray photoelectron spectroscopy results showed that fluoride ions were successfully incorporated into the hydroxyapatite (HA) lattice structure. The dissolution behavior in Tris-buffered physiological saline indicated that all fluoridated HA coatings had lower solubility than that of the pure HA coating. The lowest solubility was obtained at fluoride ion concentrations of 0.8-1.1M. In vitro cell responses were evaluated with human osteosarcoma MG63 cells in terms of cell morphology, proliferation and differentiation (alkaline phosphatase activity and osteocalcin level). For all coatings tested, similar cell morphologies and good cell viability were observed. Coatings fluoridated to 0.8-1.1 had a stronger stimulating effect on cell proliferation and differentiation activities. The influences on cell phenotypes were attributed mainly to a combined ion effect of Ca, P and F released from the coating during dissolution. For the best dissolution resistance and cell activities, it is recommended that the molar level of fluoride ion be from 0.8 to 1.1, such that the coating takes the form of Ca(10)(PO(4))(6)(OH)(1.2-0.9)F(0.8-1.1).

Alkaline Phosphatase↗

PubMed2006

A novel route to fabricate the biomedical material: structure strategy and the biologically active ions controllable release.

The multiple biologically active trace element delivery remains a problem in regeneration medicine and tissue engineering. A novel approach to fabricate the biologically active trace elements assembly in a core-shell system for cooperative controlled-release has been proposed. Firstly, using a pH-dependent electrostatic interaction, zinc and strontium ions were incorporated into the silica gel nanospheres. Subsequently a porous octacalcium phosphate (OCP) shell was coated on the nanospheres tailored by poly(acrylate sodium) molecules. In vitro test shows that this hierarchical multilayered nanostructure can achieve a shell-/pH-dependent controlled-release of silicon, strontium and zinc ions. The wet-chemical route to selective synthesis of the core-shell Silica@OCP system may provide a general model to develop cooperative encapsulation of biologically active ions in a silica-based system by using layer-by-layer assembly technique for controlled-release in biomedical areas.

Calcium Phosphates↗

PubMed2006

Novel highly biodegradable biphasic tricalcium phosphates composed of alpha-tricalcium phosphate and beta-tricalcium phosphate.

Novel biodegradable biphasic tricalcium phosphates (BTCP) composed of alpha-tricalcium phosphate (alpha-TCP) and beta-tricalcium phosphate (beta-TCP) were successfully synthesized by heating amorphous calcium phosphate precursors with different structures at 800 degrees C for 3 h. The ratio of alpha-TCP and beta-TCP in the calcium phosphate particle can be controlled by aging time and pH value during synthesis of the amorphous precursor.

Biocompatible Materials↗

PubMed2006

Preparation, characterization and cytocompatibility of porous ACP/PLLA composites.

The purpose of this work was to incorporate amorphous calcium phosphate (ACP) into porous poly(L-lactic acid) (PLLA), because ACP is capable of fast phase transformation and morphological change in body fluid, such, a desired pore wall surface within bone tissue engineering scaffolds can be created. A highly porous ACP/PLLA composite was prepared by a thermally induced phase separation technique. The results showed that the composite had an interconnected pore structure with 100 mum macropores and 10 mum micropores, and 91% porosity; 40 nm primary particles of ACP were agglomerated to 3 mum aggregates, and the aggregates were homogeneously distributed in pore walls; These aggregates showed to be in situ transformed into bone-like apatite after 1 h soaking in phosphate buffered saline solution. Human osteoblast-like cell culture showed that the ACP/PLLA composite had better cell adhesion and alkaline phosphotase activity than pure PLLA. This study demonstrates that the ACP/PLLA composite can enhance cytocompatibility and could act as a promising scaffold for bone tissue engineering.

Biocompatible Materials↗

PubMed2005

Preparation and characterization of porous beta-tricalcium phosphate/collagen composites with an integrated structure.

Porous beta-tricalcium phosphate (TCP)/collagen composites with different beta-TCP/collagen weight ratio were prepared. The influences of the preparation conditions on the microstructure of porous composite and the joint status of beta-TCP particles with collagen fibrils were characterized by X-ray diffractometer, scanning electron microscopy and transmission electron microscopy. The results showed: (1) an acid treatment could effectively disassemble collagen fibrils; (2) in the resulting porous composites, beta-TCP particles homogenously existed on the skeleton of the collagen fibril network and bonded tightly to both the fibrils and themselves. The tight bonding formation could be due to the reaction between Ca ions in the particles and carboxyl groups in collagen polypeptide chains and due to the reprecipitation of partially dissolved beta-TCP during synthesis. The tight bonding between beta-TCP particles and collagen fibrils in the composites demonstrated an integrated structure, which was reproducible when beta-TCP/collagen ratio ranged from 2 to 4. Such integrated structure would make significant contributions in reliably tailoring properties of the porous composites by varying beta-TCP content. In addition, the porous composites had large porosity (approximately 95%) and appropriate pore size (approximately 100 microm), showed no negative impact in cytotoxicity assay and complete bone tissue regeneration after 12 weeks in animal test.

Animals↗

PubMed2005

In vitro behavior of osteoblast-like cells on fluoridated hydroxyapatite coatings.

In this work, fluoridated hydroxyapatite (Ca10(PO4)6Fx(OH)(2-x) or FHA) coatings are prepared by sol-gel method for study of the influence of F content on the behavior of osteoblast-like cells. The results show that the cells well attach and proliferate on the FHA coatings studied (Ca10(PO4)6F(0.67-2.00)(OH)(0-1.33)). With increasing F content in the FHA coatings, percentage of cell in S period increases, indicating F in the coating favors the proliferation process of the cells. On the other hand, the proliferation rate increases inversely with zeta potential of the coating surface. As tested from the MTT of the cells cultured in the leaching out solution, increase of F content in the FHA coatings results in a slight decrease in cell proliferation rate, which is most probably due to reduction in release of Ca2+ ions. As a compromise among cell attachment, cell proliferation, apatite deposition and ability to resist dissolution, it is suggested that FHA coatings (Ca10(PO4)6Fx(OH)(2-x)) with x in the range of 0.67-1.48, from the results of this study, may be most suitable for real case implantation.

Animals↗

PubMed2004

Sol-gel preparation and in vitro test of fluorapatite/hydroxyapatite films.

Fluorapatite/hydroxyapatite (FA/HA) films have been demonstrated to be a good alternative to pure hydroxyapatite (HA) ones in medical applications because of their bioactivity and relatively low solubility. In this study, Ca(NO(3))(2), P(2)O(5), and HPF(6) were used to prepare FA/HA films on Ti6Al4V substrate with the use of a sol-gel method. The F contents in the films could be tailored by adjusting the amount of HPF(6) added. The in vitro evaluation of the films was carried out in both SBF9# solution and TRIS buffer solution. The films with appropriate F contents showed a better ability to induce calcium phosphate deposition on their surfaces than either pure HA film and FA/HA films with even higher F content, as well as smaller dissolution amounts than HA film in TRIS buffer solution. Hence, the FA/HA films obtained in this work integrate both good bioactivity and stability, and could be a better choice for bioactive film on titanium alloys to produce high-quality implants.

Apatites↗

PubMed2003

[Bone tissue engineering scaffolds].

Bone tissue engineering may provide an alternative to the repairs to skeletal defects resulting from disease, trauma or surgery. Scaffold has played an important role in bone tissue engineering, which functions as the architecture for bone in growth. In this paper, the authors gave a brief introduction about the requirement of bone tissue engineering scaffold, the key of the design of scaffolds and the current research on this subject.

Biodegradation, Environmental↗