PubMed1995

Scanning electron microscopy-electron probe microanalysis study of the interface between apatite and wollastonite-containing glass-ceramic and rabbit tibia under load-bearing conditions after long-term implantation.

Glass-ceramic implants containing oxy- and fluoroapatite [Ca10(PO4)6(O, F2)] and beta-wollastonite (CaSiO3) were studied under load-bearing conditions in a segmental replacement model in the tibia of the rabbit. A 16-mm segment of the middle of the tibial shaft was resected at a point distal to the junction of the tibia and the fibula. The defect was replaced by a 15 mm-long hollow, cylindrical implant that was fixed by intramedullary nailing using Kirschner wire. The implants were 9 mm in diameter and 15 mm long bearing a central hole 3.05 mm in dianeter. The rabbits used were killed 6 months, 1 year, 18 months, and 2 years after implantation. The interface between the bone and the glass-ceramic was investigated by scanning electron microscopy-electron-probe microanalysis (SEM-EPMA). None of the glass-ceramic implants broke, and the glass-ceramic had bonded directly to the bone tissue without any intervening soft tissue. A calcium-phosphorus layer (Ca-P layer) was observed at the glass-ceramic/bone interface. This layer was 30-100 microns thick at 6 months after implantation, 60-110 microns thick at 1 year after implantation, 80-200 microns thick at 18 months, and 120-350 microns thick at 2 years. At the lateral surface of the glass-ceramic uncovered by the bone, the calcium-phosphorus layer was 50-80 microns thick at 6 months after implantation, 250-450 microns thick at 1 year, 300 approximately 400 microns thick at 18 months, and 300 microns thick at 2 years. The thickness of the calcium-phosphorus layer increased moderately after long-term implantation. However, it was difficult to estimate the rate of increase in the thickness of calcium-phosphorus layer.

Animals↗
PubMed1995

Transmission electron microscopy observations at the interface of bone and four types of calcium phosphate ceramics with different calcium/phosphorus molar ratios.

Four kinds of calcium phosphate ceramics, beta-calcium pyrophosphate (Ca2P2O7), beta-tricalcium phosphate (Ca3(PO4)2), hydroxyapatite (Ca10(PO4)6(OH)2) and tetracalcium phosphate (Ca4(PO4)2O), were prepared. The calcium/phosphorus molar ratios were 1, 1.5, 1.66 and 2, respectively. Particles (150-300 microns) of these ceramics were packed into holes (diameter 2.5 mm) made in the tibial metaphysis of mature male rats. At 2 weeks, 4 weeks, 8 weeks and 6 months after the operation, undecalcified specimens were prepared. Transmission electron microscopy showed that the bone-bonding behaviour of calcium phosphate ceramics at the interface with bone did not vary with the calcium/phosphate molar ratio. Amorphous substances or needle-like microcrystals were observed on the surface of the ceramics at 2 weeks after implantation. The ceramics showed direct continuity with small crystallites of bone tissue at 4 weeks, 8 weeks and 6 months after implantation. The ceramics appeared to be getting smaller with time. Collagen fibres were not observed at the bone/ceramic interface. Neither chemical bonding nor mechanical bonding by interlocking between bone and ceramics was described by morphological observation using transmission electron microscopy.

Animals↗
PubMed1995

Toe-to-finger transfer combined with wrap-around flap: a new technique for four-finger amputation.

A surgical technique for reconstruction of four-finger amputation, toe-to-finger transfer combined with wrap-around flap procedure, is described. Opposable ulnar fingers, reconstructed using the second and third toe, provide sufficient grip function. The long finger, reconstructed with the wrap-around flap using the lateral aspect of the great toe, provides pinch function. Improving the hand function is worthwhile despite morbidity from losing two toes.

Amputation, Traumatic↗
PubMed1995

Two-stage reconstruction for the hypoplastic thumb.

A 2-year-old boy with grade 3 hypoplastic thumb (Blauth's classification) underwent reconstruction in two stages. Stage 1 was an abductor digiti quinti musculocutaneous flap, first web space widening, and insertion of a silicone rod to prepare for a flexor pollicis longus transfer. Stage 2 (6 months later) was a vascularized second toe proximal interphalangeal joint transfer for carpometacarpal joint replacement, plus tendon transfers for thumb flexion, extension, and adduction. Three years following the procedures, the thumb had an open physis by x-ray film and was functioning well. Pollicization is the traditional procedure for this degree of thumb hypoplasia, but the two-stage reconstruction is an alternative for patients in cultures where the presence of five fingers is important.

Bone Wires↗
PubMed1995

Influence of disodium (1-hydroxythylidene) diphosphonate on bone ingrowth into porous, titanium fiber-mesh implants.

The influence of disodium (1-hydroxythylidene) diphosphonate on the bonding between bone and porous, titanium fiber-mesh implants was studied. Rectangular, porous, titanium fiber-mesh implant (15 x 10 x 2.4 mm) were implanted into the tibial bone of mature male rabbits. The rabbits were divided into six groups. Disodium diphosphonate was administered daily by subcutaneous injection to groups 1-5. Groups 1-4 received doses of 5.0, 2.5, 1.0, and 0.1 mg per kilogram of body weight per day for 8 weeks, respectively. Group 5 received a dose of 5 mg per kilogram of body weight per day for 4 weeks. Group 6 (control group) was given saline injections. At 8 weeks after implantation, the rabbits were killed. The tibiae containing the implants were dissected out and subjected to detachment tests. The failure load, when an implant became detached from the bone or when the bone itself broke, was measured. The interface of the bone and implant was investigated by Giemsa surface staining and contact microradiography. Giemsa surface staining and contact microradiography showed that porous implant bonding to bone tissue was inhibited by a high dose of disodium diphosphonate in groups 1, 2, and 5. Soft tissue was observed at the interface. In groups 3, 4, and 6, bone tissue ingrowth was observed at the interface between the porous implant and bone tissue. Growth of bone into the porous fiber-mesh implant of a cementless prosthesis is possible if a low dose of diphosphonate below 1.0 mg per kilogram of body weight is given subcutaneously.

Animals↗
PubMed1995

Anterior decompression and fusion for ossification of posterior longitudinal ligament in the thoracic spine.

Twelve cases are reviewed of ossification of posterior longitudinal ligament (OPLL) in the thoracic spine for which anterior decompression and fusion were performed. A transthoracic approach was used in 10 patients, and median sternotomy and a transsternal approach were used in one each. The clinical symptoms and the Japanese Orthopaedic Association (JOA) score improved in 10 patients, whereas they were unchanged in two patients who underwent a revision operation for a previous laminectomy. An anterior procedure that results in adequate decompression of the spinal cord and good spinal stability is recommended for anterior lesions, such as OPLL, which compress the anterior spinal cord at each level of the thoracic spine.

Adult↗
PubMed1995

Diagnostic value of Tc-99m (V) DMSA for chondrogenic tumors with positive Tc-99m HMDP uptake on bone scintigraphy.

Technetium-99m (V) DMSA scintigraphy was performed in 17 patients with 37 chondrogenic tumors (13 osteochondromas, 14 enchondromas, and 10 chondrosarcomas) that had previously shown uptake of Tc-99m HMDP. Technetium-99m (V) DMSA showed high uptake by all chrondrosarcomas, but low or no uptake always indicated benign chondrogenic tumors. Technetium-99m (V) DMSA scintigraphy may be superior to Tc-99m HMDP scintigraphy for distinguishing benign and malignant chondrogenic tumors, and could also be useful for diagnosing the malignant transformation of chondrogenic tumors.

Bone Neoplasms↗
PubMed1995

Appearance of calpain correlates with arthritis and cartilage destruction in collagen induced arthritic knee joints of mice.

OBJECTIVES: To determine the relevance of calpain in murine collagen induced arthritis (CIA) and to correlate the presence of m-calpain with the appearance of arthritis and cartilage destruction. METHODS: The immunohistochemical appearance and localisation of m-calpain at different stages of arthritis were analysed and compared with the histological changes occurring during type II CIA. The arthritic knee joint lavage was also examined for m-calpain by immunoelectrophoretic blotting. RESULTS: Immunohistochemical staining demonstrated a clear positive correlation between the appearance of m-calpain and both a histological grade of arthritis and an acute phase of cartilage destruction. Further development of the disease showed continual presence of m-calpain but with reduced intensity. Intra-articular inflammatory cells (mainly polymorphonuclear leucocytes, synovial lining cells, and sublining fibroblasts) were found to be the most positively stained, but extracellular localisation of m-calpain on the surface of cartilage and synovium, and in the articular cartilage matrix and chondrocyte lacunae, was also observed. In the knee joint lavage obtained at the most intensive stage of acute arthritis, m-calpain was detectable by immunoelectrophoretic blotting. CONCLUSIONS: The findings suggest that m-calpain may act at an early phase of CIA as a matrix proteinase and take part in the destruction of articular cartilage or activate other destructive enzymes.

Acute Disease↗
PubMed1995

Proteoglycan degradation in hemarthrosis. Intraarticular, autologous blood injection in rat knees.

We determined the degradation of articular cartilage proteoglycans in a single episode of experimental hemarthrosis in rat knees. The right knee joints of rats were injected once with autologous whole blood. Both knee joints were examined histologically. Biochemical studies of cartilage proteoglycans extracted from the knees were also conducted. Histological examination revealed an accumulation of mononuclear cells in intraarticular fibrin clots and subsynovial layers 8 hours after the injection of blood. Accordingly, initiation of proteoglycan degradation occurred 8 hours after injection of blood, lasting from 1 day of limited degradation to 3 days; recovery then occurred within 7 days. The proteoglycan degradation could be inhibited by 1 mM phenylmethylsulfonyl fluoride, a general serine proteinase inhibitor, 0.1 M 6-aminohexanoic acid, a specific inhibitor of plasminogen activators, 10 mM EDTA, and 10(-6) to 10(-8) M dexamethasone, indicating that the accumulation of mononuclear cells in intraarticular fibrin clots and subsynovial layers may play an important role in cartilage damage.

Aminocaproic Acid↗
PubMed1995

Relationship between axonal regeneration and vascularity in tubulation--an experimental study in rats.

This study investigated the effect of vascularity in a nerve conduit on peripheral nerve regeneration. The effect of three different types of tube (empty, blood vessel-containing and ligated vessel-containing) was compared using a rat sciatic nerve preparation with a 10-mm gap. Nerve regeneration through the vessel-containing tube was more efficient than in the other tubes 6 and 12 weeks after tubulation surgery, but there were no statistically significant differences among the three types of tube after 24 weeks. Electrophysiological, histological and microangiographic studies showed that vessels which were preinserted in the nerve conduit accelerated axonal regeneration through rapid capillary formation in the tube.

Animals↗
PubMed1995

Biodegradable plate fixation of rabbit femoral shaft osteotomies. A comparative study.

Femoral shaft transverse osteotomies in 58 rabbits were fixed with ultrahigh strength poly-L-lactic acid plates made by a drawing technique. Similar osteotomies in another 35 rabbits were fixed using stainless steel plates. The union rate, the mechanical strength of the united bones, bone mineral content and density in the area beneath the plate using dual energy x-ray absorptiometry, and the cortical thickness beneath and opposite the plate using a digitizer was compared between the poly-L-lactic acid and stainless steel groups after postoperative periods of 8, 25, and 40 weeks. The poly-L-lactic acid and stainless steel groups showed union rates of 67% (39 of 58) and 80% (28 of 35) without displacement, respectively. In the poly-L-lactic acid group, plate failure occurred in 14% (8 of 58). The mechanical strength of the specimen was restored to a level equal to that on the untreated side by 25 weeks, and cortical thickness and bone mineral content and density were maintained almost normal for 40 weeks in the poly-L-lactic acid group. The stainless steel group showed significantly lower mechanical strength and led to osteopenia because of stress shielding after 25 weeks.

Animals↗
PubMed1995

Tissue reaction of bioabsorbable ultra high strength poly (L-lactide) rod. A long-term study in rabbits.

Bioabsorbable ultra high strength poly (L-lactide) rods, which were developed for internal fixation of fractures, were fabricated using a drawing technique. These rods were implanted in the subcutaneous tissue and in the medullary cavity of rabbits to investigate tissue reactions to poly (L-lactide) and to study their degradation process. After 18 months, histiocytes were found, and their phagocytic activity continued for as long as 42 months, with maximum activity observed between 24 and 36 months after implantation. At 62 months after intramedullary implantation, the materials had been absorbed almost completely and were replaced by bone marrow cells, with only a small amount of residual tissue reaction. At 69 months after subcutaneous implantation, the materials had been absorbed completely without any scar formation. During degradation, no foreign body giant cells were found and osteolytic expansion caused by liquid degradable materials was not seen.

Animals↗
PubMed1995

Autogenous callo-osseous grafts for the repair of osteochondral defects.

We describe a new method of biological repair of osteochondral defects. In rabbit knees an osteochondral defect was reconstructed with a callo-osseous graft made of a superficial sheet of medullary fracture callus attached to a base of cancellous bone. This was taken from the iliac bone of the same animal which had been osteotomised ten days earlier. The reparative tissues were evaluated for 24 weeks by quantitative histology, biochemical analysis of the uronic acid content, and immunohistochemical staining of collagen constituents. The callo-osseous graft provided significantly faster and better repair of the articular surface than an untreated defect or a callo-osseous graft in which the cells had been devitalised by irradiation before transplantation. Our findings indicate that the callo-osseous graft contributes to the repair process by providing both favourable extracellular matrices and pluripotential mesenchymal cells. Our study tested the hypothesis that early medullary callus generates hyaline cartilage instead of bone after transfer to an articular surface.

Adaptation, Physiological↗
PubMed1994

The effects of intraoperative radiotherapy on bone-healing ability in relation to different doses and postradiotherapy intervals.

PURPOSE: Alterations in bone-healing ability after intraoperative radiotherapy were investigated in relation to different doses and postradiotherapy intervals in an experimental model. METHODS AND MATERIALS: Bilateral osteotomy of the fibulae of 56 rabbits was carried out either immediately, 13 weeks or 39 weeks after unilateral intraoperative radiotherapy with 10-MV X ray using one of three doses, 25, 50, or 100 Gy. The healing of the fibulae was evaluated radiographically and histologically 13 weeks after the osteotomy. RESULTS: Bone-healing ability was irreversibly reduced in all irradiated fibulae and these damages occurred in a dose-dependent manner. The severity of the damage also tended to increase with the time interval between irradiation and osteotomy. This interval-related aggravation was characterized by augmented bone loss at the osteotomy ends and atrophy of the neighboring areas. CONCLUSION: These results serve as useful information concerning the surgical intervention of irradiated bone during and after intraoperative radiotherapy, and also after conventional radiotherapy.

Animals↗
PubMed1994

Mutation spectrum of the retinoblastoma gene in osteosarcomas.

We have performed an intensive mutation survey of the Rb gene in 63 osteosarcomas. Loss of heterozygosity (LOH) at the Rb locus was analyzed by using polymerase chain reaction at four intronic polymorphic sites, and 62.9% (39 of 62) of tumors showed LOH. Mutation analysis of the Rb gene was performed by Southern blot for structural anomalies, polymerase chain reaction-single strand conformation polymorphism analysis followed by direct genomic sequencing for subtle mutations, and immunohistochemistry for protein expression. The frequencies of each type of abnormalities were: structural anomalies, 28.6% (18 of 63); subtle mutations, 6.0% (3 of 50); negative protein expression, 53.6% (30 of 56); 54.5% (18 of 33) of tumors with LOH at the Rb locus were proved to show negative Rb expression, while 50.0% (11 of 22) of tumors without LOH also showed negative Rb, indicating that LOH at the Rb locus in osteosarcoma will not necessarily correlate with the actual inactivation of the Rb gene at the protein level. Findings in primary tumors were correlated with clinical outcome, and the presence of LOH and DNA alterations of the Rb gene were proved to indicate poor prognosis.

Adolescent↗
PubMed1994

Apatite coated on organic polymers by biomimetic process: improvement in its adhesion to substrate by NaOH treatment.

A dense, uniform and highly biologically active bone-like apatite layer can be formed in arbitrary thickness on any kind and shape of solid substrate surface by the following biomimetic method at ordinary temperature and pressure. First, a substrate is set in contact with particles of bioactive CaO SiO2 based glass soaked in a simulated body fluid (SBF) with inorganic ion concentrations nearly equal to those of human blood plasma. Second, the substrate is soaked in another solution with ion concentrations 1.5 times those of SBF (1.5 SBF). In the present study, organic polymer substrates treated with 5 M NaOH solution were subjected to the above mentioned biomimetic process. The induction periods for the apatite nucleation on polyethyleneterephthalate (PET), polymethylmethacrylate (PMMA), polyamide 6 (PA6), and polyethersulfone (PESF) substrates were reduced from 24 to 12 h with the NaOH treatment. The adhesive strength of the formed apatite layer were increased from 3.5 to 8.6 MPa, from 1.1 to 3.4 MPa, and from 0.6 to 5.3 MPa with the NaOH treatment, for PET, PMMA, and PA 6, respectively. It was assumed that highly polar groups, such as carboxyl and sulfinyl ones formed by the hydrolysis of an ester group on PET and PMMA and of an amide group on PA 6, or of a sulfonyl group on PESF with the NaOH treatment, attached a large number of hydrated silica dissolved from the glass particles, to accelerate the apatite nucleation, and also to form a strong bond with the apatite. The apatite-organic polymer composites thus obtained are expected to be useful as bone-repairing as well as soft tissue-repairing materials.

Adhesiveness↗
PubMed1994

Ultrastructural study of the A-W GC-bone interface after long-term implantation in rat and human bone.

The interface between apatite- and wollastonite-containing glass-ceramic (A-W GC) and bone after long-term implantation was studied by scanning and transmission electron microscopy (SEM and TEM) using rat and human specimens. First, particles of A-W GC (100-220 microns in diameter) were implanted into rat tibiae, and specimens were prepared for observation at 24, 48, 72, and 96 weeks after the operation. These long-term specimens showed an A-W GC-bone interface different from that at an earlier stage, which was investigated in our previous studies. SEM showed that the Ca-P-rich layer was wider, suggesting that leaching of ions from the A-W GC had continued even after bonding with bone. In some regions, the material particles were evidently replaced by the bone. TEM showed that the intervening apatite layer had become indistinct, and that A-W GC had intermingled with bone at the interface. In some regions, the surface of the A-W GC was degraded. These findings suggest that the surface region of A-W GC is slowly replaced by bone. Second, a human bone specimen, which included A-W GC particles (300-700 microns in diameter) implanted as a bone filler for about 75 weeks was harvested and investigated. Excellent A-W GC-bone bonding was observed, and the ultrastructure of the interface was similar to that in rats after long-term implantation. This finding demonstrated that A-W GC possibly worked in human bone in the same way as in rat bone, showing excellent bioactivity.

Adult↗