PubMed1999

Effects of water-soluble component content on cephalexin release from bioactive bone cement consisting of bis-GMA/TEGDMA resin and bioactive glass ceramics.

The effect of the amount of a water-soluble, lactose, on cephalexin (CEX) release from bioactive bone cement consisting of bisphenol-alpha-glycidyl methacrylate (bis-GMA), triethylene-glycol dimethacrylate (TEGDMA) resin and apatite- and wollastonite-containing glass-ceramic (A-W GC) powder was investigated. A-W GC powder containing 5% CEX and lactose powders hardened within 5 min after mixing with bis-GMA/TEGDMA resin, and furthermore its compressive strength was expected to be higher than that of polymethylmethacrylate cement. In vitro CEX release from bioactive bone cement pellets in a simulated body fluid at pH 7.25 and 37 degrees C continued for more than 2 wk. The drug-release rate increased with increasing amount of lactose powder in the mixture. CEX release profiles followed the Higuchi equation in the initial stage, but not in later stages. As hydroxyapatite was precipitated out on the cement surface, the CEX release rate decreased. The micropore distribution of the cements measured by mercury porosimetry also supported the variation in drug release due to cement porosity being mainly a result of the dissolution of lactose in the cements. These results suggest that the rate of CEX release from bioactive bone cement could be controlled by varying the amount of lactose in the cement system.

Journal Article↗

PubMed1999

Preparation of phosphorus-containing silica glass microspheres for radiotherapy of cancer by ion implantation.

A chemically durable glass microsphere containing a large amount of phosphorus is useful for in situ irradiation of cancers, since they can be activated to be a beta-emitter with a half-life of 14.3 d by neutron bombardment. When the activated microspheres are injected to the tumors, they can irradiate the tumors directly with beta-rays without irradiating neighboring normal tissues. In the present study, P+ ion was implanted into silica glass microspheres of 25 microm in average diameter at 50 keV with nominal doses of 2.5 x 10(16) and 3.35 x 10(1)6 cm(-2). The glass microspheres were put into a stainless container and the container was continuously shaken during the ion implantation so that P+ ion was implanted into them uniformly. The implanted phosphorus was localized in deep regions of the glass microsphere with the maximum concentration at about 50 nm depth without distributing up to the surface even for a nominal dose of 3.35 x 10(16) cm(-2). Both samples released phosphorus and silicon into water at 95 degrees C for 7 d. On the basis of the previous study on P+-implanted silica glass plates, the silica glass microspheres containing more phosphorus which is desired for actual treatment could be obtained, without losing high chemical durability, if P+ ion would be implanted at higher energy than 50 keV to be localized in deeper region.

Journal Article↗

PubMed1999

Total inhibition of high shear stress induced platelet aggregation by homodimeric von Willebrand factor A1-loop fragments.

Under high shear stress, the binding of von Willebrand factor (VWF) A1-loop domain to platelet glycoprotein (GP) Ib alpha occurs as the earliest event in thrombus formation. Therefore recombinant VWF A1-loop fragments could be of therapeutic use in blocking this interaction as competing ligands. We have prepared three homodimeric VWF A1-loop fragments [315 kD Fr III (a homodimer of amino acid [aa] residues 1-1365 of the subunit), 220 kD Fr (a homodimer of aa residues 1-708 of the subunit), and 116 kD Fr (a homodimer of aa residues 449-728 of the subunit) and two monomeric fragments [39/34 kD Fr (a monomer of aa residues 480/481-718 of the subunit] and His-rVWF465-728 (a monomer of aa residues 465-728 of the subunit)], and assessed their potency as inhibitors of botrocetin-induced VWF binding to GPIb alpha and high shear stress induced platelet aggregation mediated by intact VWE All these fragments completely inhibited botrocetin-induced VWF binding to GPIb alpha at a final concentration of 40-200 microM. The homodimeric A1-loop fragments also totally inhibited high shear stress induced platelet aggregation at a final concentration of 0.45-2.0 microM in the following order: 315 kD Fr > or = 220 kD Fr >> 116 kD Fr. In contrast, the monomeric A1-loop fragments were only partial inhibitors of high shear stress induced platelet aggregation even at a final concentration of 20 microM, and their IC50s were 13-39 times higher than those of the homodimers. These results indicate that the homodimeric structure of the A1-loop fragment is important for optimal molecular interaction with GPIb alpha under high shear stress.

Humans↗

PubMed1999

Exposed peptide core of IgA1 hinge region in IgA nephropathy.

BACKGROUND: The human IgA1 hinge region is a very unique O-linked glycopeptide, and its sialylation and galactosylation recently were reported to be defective in the serum IgA1 derived from patients with IgA nephropathy (IgAN). This study was performed to examine the underglycosylation of the IgA1 hinge region and consequent exposure of the peptide core in IgAN. METHODS: A polyclonal antibody against a synthetic human IgA1 hinge peptide, PVPSTPPTP SPSTPPTPSPS, (anti-sHP ab) was raised in rabbits and shown specifically to recognize the IgA1 which was treated with neuraminidase, beta-galactosidase and alpha-N-acetylgalactosaminidase. The reactivity of the anti-sHP ab against the purified serum IgA1 was compared among the following three groups: 39 patients with IgAN, 30 patients with other renal diseases (ORD) and 21 healthy controls (HC) using an enzyme-linked immunosorbent assay. RESULTS: The reactivity was significantly higher in the IgAN group (mean +/- SD of OD 490 nm: 0.327 +/- 0.059) than in the ORD group (0.274 +/- 0.043, P=0.0002) and in the HC group (0.265 +/- 0.037, P<0.0001). No significant difference was observed between the latter two groups. The frequency of positive cases (> mean +/- 2SD of HC) was 46.2% (18/39) in the IgAN group, 6.7% (2/30) in the ORD group and 0% (0/21) in the HC group. CONCLUSIONS: It was suggested that the peptide core of the IgA1 hinge region is exposed aberrantly by a defective N-acetylgalactosaminylation and plays a possible role in the pathogenesis of IgAN.

Adolescent↗

PubMed1999

Cloning, sequencing, and functional expression in Escherichia coli of chaperonin (groESL) genes from Vibrio cholerae.

Using a series of oligonucleotides synthesized on the basis of conserved nucleotide motifs in heat-shock genes, the groESL heat-shock operon from a Vibrio cholerae TSI-4 strain has been cloned and sequenced, revealing that the presence of two open reading frames (ORFs) of 291 nucleotides and 1,632 nucleotides separated by 54 nucleotides. The first ORF encoded a polypeptide of 97 amino acids, GroES homologue, and the second ORF encoded a polypeptide of 544 amino acids, GroEL homologue. A comparison of the deduced amino acid sequences revealed that the primary structures of the V. cholerae GroES and GroEL proteins showed significant homology with those of the GroES and GroEL proteins of other bacteria. Complementation experiments were performed using Escherichia coli groE mutants which have the temperature-sensitive growth phenotype. The results showed that the groES and groEL from V. cholerae were expressed in E. coli, and groE mutants harboring V. cholerae groESL genes regained growth ability at high temperature. The evolutionary analysis indicates a closer relationship between V. cholerae chaperonins and those of the Haemophilus and Yersinia species.

Amino Acid Sequence↗

PubMed1999

Transcatheter embolization of arteriovenous malformations in Cowden disease.

A patient with Cowden disease and multiple arteriovenous malformations (AVMs) that resulted in high output heart failure is described. Cowden disease is a familial syndrome characterized by endodermal, mesodermal and ectodermal dysplasia causing benign and malignant tumors of the skin, breast, gastrointestinal tract, and thyroid gland. Our patient had gastrointestinal polyposis, a right renal tumor, a left lung tumor, an adenomatous goiter, and typical dermatologic findings such as facial papules, acral keratosis, gingival papillomatosis and hemangiomas. AVMs were observed in the pelvis, cervical vertebra, liver, and right supraclavicular area. Transcatheter embolization was performed 7 times for the pelvic AVMs, but the effect decreased with repetition and the patient died of heart failure 2 years after the first embolization. The serum levels of tissue plasminogen activator (t-PA), platelet-derived growth factor (PDGF), hepatocyte growth factor (HGF), vascular endothelial growth factor (VEGF), and transforming growth factor beta1 were high, suggesting that these angiogenic molecules may play a role in the pathogenesis of AVMs in Cowden disease.

Adult↗

PubMed1999

Underglycosylation of IgA1 hinge plays a certain role for its glomerular deposition in IgA nephropathy.

This study was performed to isolate and investigate the IgA1 that could accumulate in glomeruli (glomerulophilic IgA1). IgA1 was fractionated by the electric charge and the reactivity to Jacalin. Serum IgA1 of IgA nephropathy patients was separated and fractionated using a Jacalin column and subsequent ion-exchange chromatography. The fractions were divided into three groups of relatively cationic (C), neutral (N), and anionic (A). IgA1 was also divided into Jacalin low (L), intermediate (I), and high (H) affinity fractions by serial elution using 25, 100, and 800 mM galactose. The left kidneys of Wistar rats were perfused with 2, 5, or 10 mg of each group of IgA1. The rats were sacrificed 15 min, 30 min, 3 h, or 24 h after the perfusion. The accumulation of each IgA1 in the glomeruli was then observed by immunofluorescence. The IgA1 of the fractions N and H separated by the two methods was definitely accumulated in the rat glomeruli with a similar pattern. The electrophoresis revealed that the macromolecular IgA1 was increased in fraction H compared with other fractions. Therefore, Jacalin high-affinity IgA1(fraction H) was applied on a diethylaminoethyl column and divided into electrically cationic (HC), neutral (HN), and anionic (HA). Only the asialo-Galbeta1,3GalNAc chain was identified in the fraction HN IgA1 by gas-phase hydrazinolysis. Furthermore, the IgA1 fraction was strongly recognized by peanut agglutinin, Vicia Villosa lectins, and antisynthetic hinge peptide antibody. These results indicated that the IgA1 molecules having the underglycosylated hinge glycopeptide played a certain role in the glomerular accumulation of IgA1 in IgA nephropathy.

Animals↗

PubMed1999

[A gastrointestinal radiographic study of 18 patients with esophageal adenocarcinoma arising from Barrett's epithelium].

Gastrointestinal radiographs were reviewed with pathological correlation in 18 patients with histologically proven esophageal adenocarcinoma arising from Barrett's epithelium. Comparison was also made with postoperative radiographs of resected esophageal specimens from 3 of the patients. Esophageal carcinoma could be observed in the gastrointestinal radiographs in 17 of the 18 patients. In 14 of the 17, the classification based on the gastrointestinal radiographs was consistent with the gross classification. In 10 of the 18 patients, rough mucosa was seen on gastrointestinal radiographs in the same area in which Barrett's epithelium was observed in the histopathological specimens. Sliding esophageal hiatus hernia was present in 12 of the 18 patients, a relatively high incidence. Regular granular or reticular shadows were observed on the mucosal surface of the esophagus on the postoperative radiographs of 3 patients. It is believed that a diagnosis of Barrett's epithelium can be made from gastrointestinal radiographs if these mucosal patterns are present. Although a definitive diagnosis of Barrett's epithelium based on upper gastrointestinal radiographs is considered difficult, the presence of rough mucosa in the esophagus around the carcinoma in combination with esophageal hiatus hernia are suggestive of esophageal adenocarcinoma arising from Barrett's epithelium.

Adenocarcinoma↗

PubMed1998

Surface structural change of bioactive inorganic filler-resin composite cement in simulated body fluid: effect of resin.

Recently much attention has been paid to bioactive filler-resin composite cements because they can solidify in a few minutes to give high mechanical strengths and they can bond to living bone. In this study the dependence on resin of apatite-forming ability in simulated body fluid (SBF) was investigated for the composite cements of bioactive CaO-SiO2-P2O5-CaF2 glass with polymethyl methacrylate (PMMA) or bisphenol-a-glycidyl methacrylate/triethyleneglycol (Bis-GMA/TEGDMA) resin. The PMMA-containing composite cement did not show the apatite-forming ability in SBF because the reaction of the glass grains with SBF was inhibited due to the complete covering of the grains with PMMA. To the contrary, the Bis-GMA/TEGDMA-containing cement exhibited high apatite-forming ability in SBF; these monomers significantly dissolved from the composite surface into SBF, causing a direct exposure of the glass grains to SBF to convert into silica gel. It is assumed that thus formed silica gels, and the silicate ions that were dissolved and adsorbed onto the composite surface, induced the apatite nucleation between the spaces of the glass grains and on the composite surface, respectively. A continuous bone-like apatite layer was formed on the top surface of the glass-Bis-GMA/TEGDMA composite cement in a short period.

Apatites↗

PubMed1998

Identification of highly conserved amino-terminal segments of dTAFII230 and yTAFII145 that are functionally interchangeable for inhibiting TBP-DNA interactions in vitro and in promoting yeast cell growth in vivo.

TFIID is a multiprotein complex composed of TBP and several TAFIIs. Small amino-terminal segments (TAF N-terminal domain (TAND)) of Drosophila TAFII230 (dTAFII230) and yeast TAFII145 (yTAFII145) bind strongly to TBP and inhibit TBP-DNA interactions. yTAFII145 TAND (yTAND) was divided into two subdomains, yTANDI10-37 and yTANDII46-71, that function cooperatively. Here, we identify dTANDII within the amino terminus of dTAFII230 at 118-143 amino acids in addition to dTANDI18-77, reported previously. dTANDII exhibits pronounced sequence similarity to yTANDII, and the two were shown to be functionally equivalent in binding to TBP and inhibiting TBP-DNA interactions in vitro. Alanine scanning mutation analysis demonstrated that Phe-57 (yTANDII) and Tyr-129 (dTANDII) are critically required for the interaction with TBP. Yeast strains containing mutant yTAFII145 lacking yTANDI or yTANDII showed a temperature-sensitive growth phenotype. The conserved core of dTANDII could substitute for the yTANDII core, and Phe-57 or Tyr-129 described above was critically required for the function of this segment in promoting normal cell growth at 37 degreesC. In these respects, the impact of yTANDII mutations on cell growth paralleled their effects on TBP binding in vitro, strongly suggesting that the yTAFII145-TBP interaction and its negative effects on TFIID binding to core promoters are physiologically important.

Amino Acid Sequence↗

PubMed1998

Solution structure of a TBP-TAF(II)230 complex: protein mimicry of the minor groove surface of the TATA box unwound by TBP.

General transcription factor TFIID consists of TATA box-binding protein (TBP) and TBP-associated factors (TAF(II)s), which together play a central role in both positive and negative regulation of transcription. The N-terminal region of the 230 kDa Drosophila TAF(II) (dTAF(II)230) binds directly to TBP and inhibits TBP binding to the TATA box. We report here the solution structure of the complex formed by dTAF(II)230 N-terminal region (residues 11-77) and TBP. dTAF(II)230(11-77) comprises three alpha helices and a beta hairpin, forming a core that occupies the concave DNA-binding surface of TBP. The TBP-binding surface of dTAF(II)230 markedly resembles the minor groove surface of the partially unwound TATA box in the TBP-TATA complex. This protein mimicry of the TATA element surface provides the structural basis of the mechanism by which dTAF(II)230 negatively controls the TATA box-binding activity within the TFIID complex.

Amino Acid Sequence↗

PubMed1998

Application of matrix-assisted laser desorption ionization time-of-flight mass spectrometry to the analysis of glycopeptide-containing multiple O-linked oligosaccharides.

In our previous report [Iwase et al., J. Biochem., 120 (1996) 393], the number of O-linked oligosaccharide chains on the hinge region of IgA1 was estimated by matrix-assisted laser desorption ionization time-of-flight mass spectrometry (MALDI-TOFMS). In this experiment, the number of non-substituted N-acetylgalactosamines and Galbeta1,3GalNAc residues, as the core O-linked oligosaccharide structure per heavy chain of normal human serum IgA1, was estimated by digestion of the asialo-hinge glycopeptide with alpha-N-acetylgalactosaminidase (GalNAc-ase) or endo-alpha-N-acetylgalactosaminidase (endo-GalNAc-ase). GalNAc-ase treatment of the asialoglycopeptide produced two major peaks, one being a glycopeptide containing four GalNAc and four Gal residues, and the other contained three GalNAc and three Gal residues. Treatment with endo-GalNAc-ase also produced a nearly equal amount of the two peaks, with the naked hinge peptide and the peptide having one GalNAc residue. From those results, we concluded that the asialo-hinge glycopeptide was composed of three components bearing four Galbeta1,3GalNAc and one GalNAc, only four Galbeta1,3GalNAc, and three Galbeta1,3GalNAc and one GalNAc, respectively. This method was useful for determining the glycoforms on the IgA1 molecule with respect to the core O-linked oligosaccharide structure.

Carbohydrate Conformation↗

PubMed1998

CD4+ T cells from peripheral blood of a melanoma patient recognize peptides derived from nonmutated tyrosinase.

Tyrosinase is an antigen that is expressed by normal melanocytes as well as melanoma cells, against which responses by autologous T cells have been detected. Although CD4+ T cells play an important role in tumor immunity in animal tumor models, little information about CD4+ T-cell immunity against human tumors exists. Here, we report that CD4+ T cells from the peripheral blood of a patient with melanoma respond to synthetic peptides derived from nonmutated tyrosinase. T-cell clones were generated that recognized the tyrosinase p386-406 peptide when it was presented by the HLA-DR15 (DRB1*1501) molecule. The CD4+ T-cell clone also recognized autologous EBV-transformed B-lymphoblastoid cell lines that had been pulsed with the lysate of melanoma cells. The synthetic tyrosinase p386-406 peptide was capable of binding to HLA-DR15 (DRB1*1501) molecules on cell surface of DR15 homozygous cells. Thus, the finding that nonmutated tyrosinase peptides are immunogenic in a melanoma patient may provide the basis for the development of cancer immunotherapy, based on knowledge of synthetic tumor-associated peptide antigens.

Antigen-Presenting Cells↗

PubMed1998

Bioactive bone cement: effect of the amount of glass-ceramic powder on bone-bonding strength.

We examined the influence of the proportion of glass-ceramic powder in a bioactive bone cement of our formula on the bone-bonding ability of cement. Changes in cement bonding with time also were examined. The bioactive bone cement consisted of MgO-CaO-SiO2-P2O5-CaF2 glass-ceramic powder (AW-GC powder) and bisphenol-alpha-glycidyl methacrylate (Bis-GMA)-based resin. AW-GC powder was added to the cement as 0%, 30%, 50%, 70%, and 80% w/w. Rectangular plates (2 x 10 x 15 mm) of each cement with polished surfaces were implanted into the proximal metaphysis of the tibiae of male rabbits, and the failure load was measured by detaching tests 10 and 25 weeks after implantation. The failure loads of each cement were 0% = 0.03, 30% = 1.52, 50% = 2.67, 70% = 3.56, and 80% = 5.59 kg at 10 weeks, and 0% = 0.05, 30% = 1.68, 50% = 2.77, 70% = 3.80, and 80% = 6.37 kg at 25 weeks. Observation of the cement-bone interface revealed that all bioactive bone cements (30%-80%) formed direct contact with bone whereas intervening fibrous tissue was observed in all specimens of the 0% group. By scanning electron microscopy, all bioactive bone cements (30%-80% groups) showed direct contact with bone at the cement-bone interface. In the 0% group, direct contact with bone at the cement-bone interface was not observed. By electron-probe microanalysis, a Ca-P-rich layer was not detected at the cement-bone interfaces of the 30%-70% bioactive bone cements, but in some samples of the 80% cement specimens a thin Ca-P-rich layer (3 microns thick) was observed at the interface at 10 and 25 weeks after implantation. These results show that all of the bioactive bone cements tested had the ability to bond to bone and to function as bioactive composites of ceramics and polymers.

Animals↗

PubMed1998

Cartilage formation by fetal rat chondrocytes cultured in alginate beads: a proposed model for investigating tissue-biomaterial interactions.

Chondrocytes from 21-day-old rat fetal nasal cartilage were cultured in alginate beads for up to 20 days. It was found that chondrocytes retained their spherical shape and typical chondrocytic appearance. During the culture time, chondrocytes underwent differentiation, as demonstrated by the alkaline phosphatase-specific activity and rate of proteoglycan synthesis. Morphological data confirmed chondrocyte differentiation with the appearance of hypertrophic chondrocytes scattered in the alginate gel and a dense extracellular matrix containing filamentous structures and matrix vesicles. In addition, Northern blot analysis performed on day 8 of culture showed that chondrocytes cultured in alginate beads expressed type II collagen mRNA. The alginate bead method also appeared to be suitable for testing biomaterials, and the ready dissolution of the alginate beads by chelating agents provided a simple means for the rapid recovery of encapsulated chondrocytes. Powdered glass-ceramic particles entrapped in the alginate gel were colonized by chondrocytes, which then proliferated and formed a tissue similar to a true calcified cartilaginous structure. These results indicate that the alginate system represents a relevant model for studies of chondrogenesis and endochondral ossification. Furthermore, the encapsulation method could prove useful for studies of tissue-biomaterial interactions in an in vitro environment which more closely mirrors the cartilage matrix than other culture methods.

Animals↗

PubMed1998

Bioactive bone cement: comparison of apatite and wollastonite containing glass-ceramic, hydroxyapatite, and beta-tricalcium phosphate fillers on bone-bonding strength.

A study was conducted to compare the bone-bonding strengths of three types of bioactive bone cement, consisting of either apatite- and wollastonite-containing glass-ceramic (AW-GC) powder, hydroxyapatite (HA) powder, or beta-tricalcium phosphate (beta-TCP) powder as an inorganic filler and bisphenol-a-glycidyl methacrylate (Bis-GMA) based resin as an organic matrix. Seventy percent (w/w) filler was added to the cement. Rectangular plates (10 x 15 x 2 mm) of each cement were made and abraded with #2000 alumina powder. After soaking in simulated body fluid for 2 days, the AW cement (AWC) and HA cement (HAC) formed bonelike apatite over their entire surfaces, but the TCP cement (TCPC) did not. Plates of each type of cement were implanted into the tibial metaphyses of male Japanese white rabbits, and the failure loads were measured by a detaching test at 10 and 25 weeks after implantation. The failure loads of AWC, HAC, and TCPC were 3.95, 2.04, and 2.03 kgf at 10 weeks and 4.36, 3.45, and 3.10 kgf at 25 weeks, respectively. The failure loads of the AWC were significantly higher than those of the HAC and TCPC at 10 and 25 weeks. Histological examination by contact microradiogram and Giemsa surface staining of the bone-cement interface revealed that all the bioactive bone cements were in direct contact with bone. However, scanning electron microscopy and energy-dispersive X-ray microanalysis showed that only AWC had contacted to the bone via a Ca-P rich layer formed at the interface between the AW-GC powder and the bone, which might explain its high bone-bonding strength. Neither the HAC nor the TCPC contacted the bone through such a layer between each powder and the bone, although the HAC and TCPC directly contacted with bone. Our results indicate that all three types of abraded and prefabricated cement have bonding strength to bone, but AWC has superior bone-bonding strength compared to HAC and TCPC.

Animals↗

PubMed1998

Osteoclastic resorption of bone-like apatite formed on a plastic disk as an in vitro assay system.

We have investigated the applicability of a simple and inexpensive osteoclastic assay system using bone-like apatite-coated polyethyleneterephthalate (PET) disks. A 1 microm thick apatite layer, uniform and homogeneous bone-mineral-like with no organic components, was made on PET disks using a biomimetic process. As substrates for an osteoclastic assay, these coated disks were compared with dentine as well as with bone-like or heat-treated apatite of various thicknesses on apatite- and wollastonite-containing glass ceramic (A-W GC) disks. The unfractionated bone cells, including osteoclasts, of a neonatal rabbit were seeded onto these substrates. By scanning electron microscopic examination, the resorption lacunae of the thick bone-like apatite clearly showed track-like shapes at various depths, similar to those of dentine although the border between the A-W GC and the apatite was unclear. In contrast, those of heat-treated apatite showed small and shallow shapes with irregular margins, quite different from those of dentine. By reducing the thickness of bone-like apatite to 1 microm as well as using PET as its substrate, the margins of the resorption lacunae became quite clear, and with the use of phase-contrast microscopy during culture, osteoclasts and resorption pits could be precisely observed. The resorbed area, easily measured with the aid of bright-field microscopy and an image analyzer, was found to have increased in a time-dependent manner and at the end of 4 days of culture was not statistically different from that of dentine.

Animals↗

PubMed1998

Effect of polymerization reaction inhibitor on mechanical properties and surface reactivity of bioactive bone cement.

We introduced an inhibitor to the polymerization reaction of bioactive bone cement (AWC) consisting of MgO-CaO-SiO2-P2O5-CaF2 apatite and wollastonite containing glass-ceramic powder and bisphenol-alpha-glycidyl methacrylate based resin, together with an increased amount of accelerator but without any prolongation of its setting time in order to improve the degree of polymerization and decrease the amount of incompletely polymerized monomers on the cement surface. A comparison was made between the AWC containing the inhibitor [AWC(I+)] and the AWC without it [AWC(I-)] with regard to setting parameters, mechanical properties, and surface reactivity in vitro and in vivo. The proportion of glass-ceramic powder added to the AWC was 70% (w/w). The total amount of heat generation and the peak temperature of the AWC(I+) during polymerization were slightly greater than those of the AWC(I-). The mechanical strength of AWC(I+) was higher than that of the AWC(I-) under wet conditions. In simulated body fluid, the width of the Ca-P rich layer on the surface of the AWC(I+) was less than that on the AWC(I-) after 28 days of immersion, although the rate of apatite formation on the top surface of the AWC(I+) was almost identical to that on the AWC(I-) surface. Histological examination using rat tibiae up to 26 weeks revealed that the bioactivity of the AWC(I+) was equivalent to that of the AWC(I-). Scanning electron microscopy and energy-dispersive X-ray microanalysis demonstrated that the Ca-P rich layer in the AWC(I+) was significantly narrower than that in the AWC(I-) at the same time points. These results indicate that introduction of the inhibitor improved the mechanical properties of the AWC and made the Ca-P rich layer narrower, but it had no adverse effect on bioactivity.

Animals↗