Highly active copper-based catalyst for atom transfer radical polymerization.

Atom transfer radical polymerization (ATRP) generally requires a catalyst/initiator molar ratio of 0.1 to 1 and catalyst/monomer molar ratio of 0.001 to 0.01 (i.e., catalyst concentration: 1000-10,000 ppm versus monomer). Herein, we report a new copper-based complex CuBr/N,N,N',N'-tetrakis(2-pyridylmethyl)ethylenediamine (TPEN) as a versatile and highly active catalyst for acrylic, methacrylic, and styrenic monomers. The catalyst mediated ATRP at a catalyst/initiator molar ratio of 0.005 and produced polymers with well-controlled molecular weights and low polydispersities. ATRP occurred even at a catalyst/initiator molar ratio as low as 0.001 with copper concentration in the produced polymers as low as 6-8 ppm (catalyst/monomer molar ratio = 10(-5)). The catalyst structures were studied by X-ray diffraction and NMR spectroscopy. The activator CuIBr/TPEN existed in solution as binuclear and mononuclear complexes in equilibrium but as a binuclear complex in its single crystals. The deactivator CuIIBr2/TPEN complex was mononuclear. High stability and appropriate KATRP (ATRP equilibrium constant) were found crucial for the catalyst working under high dilution or in coordinating solvents/monomers. This provides guidance for further design of highly active ATRP catalysts.

Journal Article↗

PubMed2006

Diminishing catalyst concentration in atom transfer radical polymerization with reducing agents.

The concept of initiators for continuous activator regeneration (ICAR) in atom transfer radical polymerization (ATRP) is introduced, whereby a constant source of organic free radicals works to regenerate the Cu(I) activator, which is otherwise consumed in termination reactions when used at very low concentrations. With this technique, controlled synthesis of polystyrene and poly(methyl methacrylate) (Mw/Mn < 1.2) can be implemented with catalyst concentrations between 10 and 50 ppm, where its removal or recycling would be unwarranted for many applications. Additionally, various organic reducing agents (derivatives of hydrazine and phenol) are used to continuously regenerate the Cu(I) activator in activators regenerated by electron transfer (ARGET) ATRP. Controlled polymer synthesis of acrylates (Mw/Mn < 1.2) is realized with catalyst concentrations as low as 50 ppm. The rational selection of suitable Cu complexing ligands {tris[2-(dimethylamino)ethyl]amine (Me6TREN) and tris[(2-pyridyl)methyl]amine (TPMA)} is discussed in regards to specific side reactions in each technique (i.e., complex dissociation, acid evolution, and reducing agent complexation). Additionally, mechanistic studies and kinetic modeling are used to optimize each system. The performance of the selected catalysts/reducing agents in homo and block (co)polymerizations is evaluated.

Catalysis↗

PubMed2006

Inverse miniemulsion ATRP: a new method for synthesis and functionalization of well-defined water-soluble/cross-linked polymeric particles.

A new methodology for the synthesis and functionalization of nanometer-sized colloidal particles consisting of well-defined, water-soluble, functional polymers with narrow molecular weight distribution (M(w)/M(n) < 1.3) was developed, utilizing atom transfer radical polymerization (ATRP) of water-soluble monomers in an inverse miniemulsion. The optional introduction of a disulfide-functionalized cross-linker allowed for the synthesis of cross-linked (bio)degradable nanogels. Dynamic light scattering (DLS) and atomic force microscopy (AFM) measurements indicated that these particles possessed excellent colloidal stability. ATRP in inverse miniemulsion led to materials with several desirable features. The colloidal particles preserved a high degree of halogen chain-end functionality, which enabled further functionalization. Cross-linked nanogels with a uniformly cross-linked network were prepared. They were degraded to individual polymeric chains with relatively narrow molecular weight distribution (M(w)/M(n) < 1.5) in a reducing environment. Higher colloidal stability, higher swelling ratios, and better controlled degradability indicated that the nanogels prepared by ATRP were superior to their corresponding counterparts prepared by conventional free radical polymerization (RP) in inverse miniemulsion.

Journal Article↗

PubMed2006

Determination of equilibrium constants for atom transfer radical polymerization.

Atom transfer radical polymerization (ATRP) equilibrium constants (K(ATRP)) were determined using modified Fischer's equations for the persistent radical effect. The original Fischer's equations could be used only for low conversion of Cu(I) to X-Cu(II) and consequently for relatively low values of K(ATRP). At higher conversion to X-Cu(II) (>10%) and for larger values of K(ATRP) (>10(-)(7)), modified equations that take into account the changes in catalyst and initiator concentrations should be used. The validity of new equations was confirmed by detailed kinetic simulations. UV-vis spectrometric and GC measurements were used to follow the evolution of X-Cu(II) species and the initiator concentration, respectively, and to successfully determine values of K(ATRP) for several catalysts and alkyl halides. The effect of structure on reactivities of ATRP components is presented.

Journal Article↗

PubMed2002

Nanostructured carbon arrays from block copolymers of polyacrylonitrile.

Arrays of graphitic carbon nanoclusters were obtained by pyrolysis of nanoscale phase-separated block copolymers of polyacrylonitrile and poly(n-butyl acrylate). Upon heating in an inert atmosphere to temperatures ranging from approximately 400 to 1200 degrees C, polyacrylonitrile domains were converted into carbon nanoclusters, maintaining the overall shape and spacing, whereas the poly(n-butyl acrylate) phase was sacrificed. Preservation of the original nanoscale morphology of a block copolymer was possible only if pyrolysis was preceded by oxidation at temperatures of approximately 230 degrees C, in analogy with thermal stabilization of polyacrylonitrile precursor in the process used in the manufacturing of carbon fibers. Preorganization of the carbon precursor through self-assembly in block copolymers of polyacrylonitrile appears to be an attractive and robust strategy for templated synthesis of well-defined nanostructured carbon materials.