Retention force and fatigue strength of overdenture attachment systems.

This study evaluated retention force and fatigue resistance of two overdenture attachment systems. Twenty samples (O-ring and Bar-Clip) from two manufacturers (Conexão Sistemas de Prótese and Lifecore Biomedical) were prepared and divided into four groups: (i) Conexão/O-ring; (ii) Conexão/Bar-Clip; (iii) Lifecore/O-ring and (iv) Lifecore/Bar-Clip, with five samples in each group. They were submitted to mechanical fatigue test using a servohydraulic machine performing 5500 cycles of insertion and removal (f=0.8 Hz), immersed in artificial saliva. Retention force values were obtained three times (0, 3000 and after 5500 cycles) simulating the clinical service, using a tensile strength at 1 mm min(-1) and load cell of 1 kN. Data were analysed with analysis of variance and Tukey's test at 5% level. Results showed that Conexão/Bar-Clip specimens had significantly higher retention values than Lifecore/Bar-Clip (44.61 and 18.44 N, respectively), Conexão/O-ring specimens had significantly lower values than Lifecore/O-ring (13.91 and 19.75 N, respectively). Conexão/Bar-Clip values were always significantly higher than those of Conexão/O-ring group (44.61 and 13.91 N, respectively). Lifecore (O-ring and Bar-Clip) presented similar values (19.75 and 18.44 N, respectively). The systems evaluated showed satisfactory retention force values, before and after fatigue testing. Conexão/Bar-Clip specimens presented the highest values. A 5-year simulation of insertion and removal did not decrease retention values or fracture components.

Dental Implants↗
PubMed2004

Corrosion-fatigue of laser-repaired commercially pure titanium and Ti-6Al-4V alloy under different test environments.

This study evaluated the corrosion-fatigue life of laser-repaired specimens fabricated from commercially pure titanium (CP Ti) and Ti-6Al-4V alloy, tested under different storage conditions. For each metal, 30 dumbbell rods with a central 2.3 mm diameter were prepared by lost-wax casting with the Rematitan System. Simulating the failure after service, corrosion-fatigue life in different media at room temperature (air, synthetic saliva and fluoride synthetic saliva) was determined at a testing frequency of 10 Hz for intact specimens and after laser repairing, using a square waveform with equal maximum tensile and compressive stress that was 30% lower than the 0.2% offset yield strength. For laser welding, the fractured specimens were rejoined using a jig to align the sections invested in type-IV dental stone. The adjacent areas of the gap was air-abraded with 100 microm aluminum oxide, laser welded and retested under the same conditions as the initial intact specimens. The number of cycles at failure was recorded, and the fracture surface was examined with a scanning electron microscope (SEM). The number of cycles for failure of the welded and intact specimens was compared by anova and the Tukey test at a 5% probability level. Within the limitations of this study, the number of cycles required for fracture decreased in wet environments and the laser repairing process adversely affected the life of both metals under the corrosion-fatigue conditions.

Aluminum↗
PubMed2004

Surface roughness of acrylic resins submitted to mechanical and chemical polishing.

Surface roughness is extremely important as it influences micro-organism accumulation and consequently oral health. The aim of the present study was to evaluate the influence of mechanical polishing (MP) and chemical polishing (CP) on surface roughness of four heat-cured denture base acrylic resins. Twenty sample discs were prepared for each of the following acrylic resins: Classico (CL), QC 20 (QC), Acron MC (AC) and Onda Cryl (ON). The first two are boiling cured resins and the latter two are microwave cured. After curing and deflasking, samples were ground and subdivided into two groups: MP, which received pumice slurry, chalk powder, soft brush and felt cone, at a bench vice; and CP, which received fluid specifically for chemical polisher. Surface roughness was measured using a Surf Corder SE 1700 rugosimeter. Data collected were statistically analysed by analysis of variance followed by Tukey's test. Surface roughness means in mum were: CL-MP: 0.0350; CL-CP: 0.2298; QC-MP: 0.0307; QC-CP: 0.1792; AC-MP: 0.0312; AC-CP: 0.2700; ON-MP: 0.0321; ON-CP: 0.2949. It can be concluded that MP produced significantly smoother surfaces than CP and that surface roughness because of MP was not influenced by acrylic resin type, whereas this was not true of CP.

Acrylic Resins↗
PubMed1999

Effect of storage and acid etching on the tensile bond strength of composite resins to glass ionomer cement.

This in vitro study evaluates the effect of storage time and acid etching on the tensile bond strength of glass ionomer cement to composite resins. The bonded assemblies were stored at 100% relative humidity and 37 degrees C for 1 hour, 1 day, 1 week, 1 month and 3 months. The test specimen was loaded at tension to failure on an Otto Wolpert-Werke testing instrument with a crosshead speed of 6 mm/min. The results showed a significant statistical difference for etched Vidrion F when compared to etched Ketac Bond at all storage periods. The unetched samples were statistically similar at 3 months, with the highest values for Vidrion F.

Acid Etching, Dental↗
PubMed1988

Increased VLDL.

Explore the source record for details and available documents.

Arteriosclerosis↗
PubMedDate not supplied

Influence of flask closure and flask cooling methods on tooth movement in maxillary dentures.

PURPOSE: This study investigated the tooth movement of standardized simulated dentures processed by traditional closure or the new Rafael Saide (RS) tension system when cooled in the curing water itself or in curing water followed by bench storage for 3 hours. MATERIALS AND METHODS: Forty stone casts were formed from a mold of an edentulous maxillary arch. The wax denture record bases were made on the casts; the height of the wax rim occlusion was 20 mm in the labial sulcus of the cast and 10 mm in the posterior region. The upper stone cast was mounted on a Mondial 4000 semi-adjustable articulator with wax rim interocclusal references in relation to the lower stone cast teeth. Metallic pins were placed in the incisal border of the maxillary central incisors (I), labial cusp of the first premolars (PM), and mesiolabial cusp of the second molars (M). The incisor-to-incisor (I-I), premolar-to-premolar (PM-PM), and molar-to-molar (M-M) transversal distances and left incisor-to-left molar (LI-LM), and right incisor-to-right molar (RI-RM) anteroposterior distances were measured before and after denture polymerization with an optical microscope with a tolerance of 0.0005 mm. For traditional closure, the dentures were flasked conventionally in standard metallic flasks, which were afterward placed in spring clamps. For the new RS system closure, the flasks were pressed between the metallic plates of the tension system after the final closure. The Clássico heat-polymerizing acrylic resin dough was packed in the flasks under a final packing pressure of 1.250 kg f. Twelve hours after flask closure, the dentures were polymerized in a moist heat-polymerizing cycle for 9 hours at 74 degrees C. The denture was deflasked after cooling in the water of the polymerizing cycle (groups A and C) or in the water of the polymerizing cycle and then bench-stored for 3 hours (groups B and D). Collected data were analyzed with analysis of variance and Tukey's test (p< 0.05). RESULTS: There was no statistically significant difference (p> 0.05) between the conventional and new RS system closure methods for the transversal distances after polymerization in all studied groups. The anteroposterior distances did not change with deflasking after water bath cooling. There were statistically significant differences (p< 0.05) in the anteroposterior distances with deflasking after water bath cooling and then bench storage for 3 hours. CONCLUSION: Tooth movement was similar in dentures processed by traditional closure and by the new RS tension system, with the exception of the anteroposterior distances when the flasks were cooled in their own curing water and bench-stored for 3 hours.

Analysis of Variance↗