In vivo performance of biodegradable calcium phosphate glass ceramics using the rabbit model: histological and SEM observation.

Two MK5 (45CaO-45P(2)O(5)-5MgO-5K(2)O, in mol%) and MT13 (45CaO-37P(2)O(5)-5MgO-13TiO(2), in mol%) glasses are prepared in the meta- and pyrophosphate regions and crystallized to obtain MK5B and MT13B, respectively. MK5B was obtained by controlled crystallization, and MT13B by powder sintering. As a result of these heat treatment processes, the crystalline phases precipitated in the glassy matrix are KCa(PO(3))(3), beta-Ca(PO(3))(2), beta-Ca(2)P(2)O(7) and Ca(4)P(6)O(19) phases for MK5B and CaTi(4)(PO(4))(6), TiP(2)O(7), alpha- and beta-Ca(2)P(2)O(7) phases for MT13B. To assess the in vivo biological behavior of these glass ceramics, a mixed granulometry in the range 250-355 mum and 355-425 mum with a ratio of 1/1 was implanted for 2, 4, and 12 weeks in the tibiae of Japanese white rabbits. The results showed that the in vivo behavior was strongly affected by their solubility. All implanted materials, MK5B and MT13B, and beta-tricalcium phosphate (beta-TCP) as control material, showed signs of degradation in vivo. However, the levels of degradation were quite different throughout the implantation periods. The highest degradation was observed for MK5B glass ceramic and the lowest for MT13B with beta-TCP in-between. All implanted materials allow for new bone formation in the bone defect area. At the longest implantation period (12 weeks), the MT13B and beta-TCP materials were almost completely surrounded by new bone tissue, whereas MK5B showed some unfilled spaces. This behavior is discussed in terms of the high degradation observed in previous studies.

Absorbable Implants↗
PubMed2003

UV-induced skin damage.

Solar radiation induces acute and chronic reactions in human and animal skin. Chronic repeated exposures are the primary cause of benign and malignant skin tumors, including malignant melanoma. Among types of solar radiation, ultraviolet B (290-320 nm) radiation is highly mutagenic and carcinogenic in animal experiments compared to ultraviolet A (320-400 nm) radiation. Epidemiological studies suggest that solar UV radiation is responsible for skin tumor development via gene mutations and immunosuppression, and possibly for photoaging. In this review, recent understanding of DNA damage caused by direct UV radiation and by indirect stress via reactive oxygen species (ROS) and DNA repair mechanisms, particularly nucleotide excision repair of human cells, are discussed. In addition, mutations induced by solar UV radiation in p53, ras and patched genes of non-melanoma skin cancer cells, and the role of ROS as both a promoter in UV-carcinogenesis and an inducer of UV-apoptosis, are described based primarily on the findings reported during the last decade. Furthermore, the effect of UV on immunological reaction in the skin is discussed. Finally, possible prevention of UV-induced skin cancer by feeding or topical use of antioxidants, such as polyphenols, vitamin C, and vitamin E, is discussed.

Animals↗
PubMed2002

Localized heat urticaria in a patient is associated with a wealing response to heated autologous serum.

We report a case of localized heat urticaria in a 71-year-old woman who developed weals and loss of consciousness after taking a bath. Exposing her skin to heat at 40 degrees C or immersing her hands in water at 40 degrees C produced urticarial lesions and increased her plasma histamine level. Desensitization with hot water improved her symptoms and normalized her plasma histamine level after heat challenge. An intracutaneous injection of her serum produced no reaction, while an injection of her serum that had been heated at 40 degrees C for 15 min induced a weal flare response. Further examination revealed that the weal-inducing activity of her heated serum remained for at least for 6 h and that treatment of her serum at 60 degrees C for 2 h did not abrogate its weal-inducing activity. These findings indicate that certain materials in her serum that are activated by heat are responsible for the development of her anaphylactic and urticarial reactions and that these reactions may be mediated by histamine.

Aged↗
PubMed2001

A comparative study of in vitro apatite deposition on heat-, H(2)O(2)-, and NaOH-treated titanium surfaces.

Commercially pure titanium specimens are subjected to three different treatments, and their bioactivity are evaluated by immersing the specimens in a simulated body fluid (SBF, Kokubo's recipe) for various periods up to 7 days, with particular attention being paid to the differences in apatite deposition between surfaces open to SBF and surfaces in contact with the container's bottom. The treatment with a H(2)O(2)/HCl solution at 80 degrees C for 30 min followed by heating at 400 degrees C for 1 h produces an anatase titania gel layer on the specimen surface. This gel layer deposits apatite both on the contact and on open surfaces, and apatite deposition ability does not change with pre-staking in distilled water. The treatment with a NaOH solution at 60 degrees C for 3 days produces a sodium titanate gel layer. This gel layer can deposit apatite only on the contact surface, and the apatite deposition ability is completely lost after 1 day of pre-staking in distilled water. It is concluded, therefore, that the bioactivity of the titania gel originates from the favorable structure of the gel itself while the bioactivity of the sodium titanate gel depends heavily on ion release from the gel. The third treatment, a simple heat treatment at 400 degrees C for 1 h, produces a dense (not porous) oxide layer on the specimen surface. The specimens can deposit apatite on the contact surface after only 3 days of staking in SBF, but they cannot deposit apatite on the open surface for up to 2 months of staking. The implications of such apatite deposition behavior have been discussed in relation to the environments of titanium implants in bone as well as to the methodology of the SBF staking experiment.

Apatites↗
PubMed2001

In vivo evaluation of bone-bonding of titanium metal chemically treated with a hydrogen peroxide solution containing tantalum chloride.

Apatite formation on implants is important in achieving a direct bonding to bone tissue. We recently showed that titanium metal chemically treated with a hydrogen peroxide solution containing tantalum chloride has the ability to form a hydroxyapatite layer in simulated body fluid which had inorganic ion composition similar to human blood plasma. In this study, a pure titanium cylinder (4.0 mm in diameter, 20.0 mm in length) treated with this method was implanted into a hole (4.2 mm in diameter) in a rabbit's tibia. After implantation for predetermined periods up to 16 weeks, the specimens were extracted with bone tissue, and were examined by push-out test to evaluate the shearing force between the implant and bone tissue. The results were compared with those of non-treated pure titanium. Eight weeks after surgery, the shearing force of the treated titanium implanted in the 4.2 mm-hole was significantly higher than that of non-treated titanium, although the surface roughness was not changed after the treatment. Scanning electron microscopic (SEM) observation and energy-dispersive X-ray (EDX) microanalysis showed that the bone comes very close to the surface of the treated titanium. Moreover, the shearing force was higher for the implanted sample in the 4.0 mm-hole than that in the 4.2 mm-hole. Thus, it is confirmed that the treatment with hydrogen peroxide solution containing tantalum chloride provides higher bonding ability on titanium implants in vivo.

Animals↗
PubMed2001

Low-dose ultraviolet B radiation synergizes with TNF-alpha to induce apoptosis of keratinocytes.

High-dose ultraviolet B (UVB) irradiation is known to induce apoptosis of keratinocytes, but low-dose UVB dose not. In this paper we present evidence that low-dose UVB can induce TNF-alpha-dependent apoptosis of keratinocytes. In our study, 5 mJ/cm(2) doses of UVB were not sufficient by themselves to induce apoptosis of cultured human keratinocytes, but 20 mJ/cm(2) doses of UVB were. The combination of 5 mJ/cm(2) doses of UVB and exogenous TNF-alpha (15 ng/ml) induced significant apoptosis of keratinocytes, although exogenous TNF-alpha without UVB did not. This phenomenon was accompanied by enhanced clustering of tumor necrosis factor receptor 1 (TNFR1). TNF-alpha's promotion of the induction of apoptosis by low-dose UVB was seen until 30 min after irradiation but not at 1 h. We confirmed this finding using a skin organ culture system. UVB (20 mJ/cm(2)), which did not induce transformation of epidermal keratinocytes into sunburn cells, induced apoptosis when TNF-alpha was added to the culture medium. These results suggest that one of the possible mechanisms of inducing keratinocyte apoptosis by low-dose UVB and TNF-alpha is that low-dose UVB augments ligand-binding-induced TNFR1 clustering, resulting in increased apoptotic cell death.

Antigens, CD↗
PubMed2001

Expression of peroxisome proliferator-activated receptor subtypes in human atherosclerosis.

To clarify the involvement of peroxisome proliferator-activated receptors (PPARs) in atherosclerotic plaque formation, we investigated the expression patterns of mRNA and protein of PPARalpha and PPARgamma in human aorta. Atheromatous plaque, fatty streak, and diffuse intimal thickening (DIT) were separated macroscopically, and each sample was divided into halves. Half of them were used for analysis of mRNA expression with reverse transcription-polymerase chain reaction and the others were used for histologic analysis. Both PPARalpha and PPARgamma mRNA were detected in all atheromatous plaques, all fatty streaks, and in some DIT. However, expressions of PPARalpha and PPARgamma were obviously less frequently found in DIT than in atheromatous plaques, and the intensity of these expressions was stronger in the atheromatous plaques than in the DIT. Compared with PPARalpha, PPARgamma mRNA was expressed more frequently in atheromatous plaques. In atheromatous plaques, PPARgamma mRNA was expressed independently, whereas PPARalpha mRNA was coexpressed with PPARgamma. PPARgamma protein was obviously found in the nuclei of endothelial cells, macrophages, mononuclear cells, and smooth muscle cells in the aortic intima. These results suggest that expressions of PPARalpha and PPARgamma in human aortic wall are involved in atherogenesis from the early stages.

Arteriosclerosis↗
PubMed2000

Improvement of bioactivity of H(2)O(2)/TaCl(5)-treated titanium after subsequent heat treatments.

Commercially pure titanium was treated with a H(2) O(2)/3mM TaCl(5) solution at 80 degrees C for various periods and a titania gel layer was formed on the surface. This gel remained amorphous when heating for 1 h below 200 degrees C and transformed to anatase after heating between 300 degrees and 600 degrees C. The anatase titania gel layers were found to be bioactive as to deposit carbonate ion-incorporated apatite within 1 day of immersion in the Kokubo solution, whereas the amorphous layers did not deposit apatite within 7 days. The apatite particles were found to nucleate preferentially inside the cracks prevailing in the thicker gel layers of 1-h chemically treated specimens. After immersing for 2 days, the titanium specimens were almost completely covered by apatite. Elimination of peroxide radicals from the titania gel and formation of anatase upon subsequent heating are considered to be responsible for the enhanced ability of apatite deposition.

Apatites↗
PubMed2000

Impression pressures against teeth in a partially edentulous model with a mobile tooth: influence of impression tray design.

The purpose of the present study was to examine the effect of custom tray designs on local pressures against teeth during the impression procedure. In a previous study, a partially edentulous simulation model with a mobile tooth was used, and the effect of custom tray designs on the displacement of the mobile tooth was examined during the impression procedure. Based on that study's results, we have assumed that the differences in impression pressures between the labial and the lingual sides of a mobile tooth could either cause or affect displacement. The present study was undertaken to determine the local impression pressures against each side of three anterior teeth, including one mobile tooth, using the same simulation model and the same custom trays as in the previous study. It was found that the local pressures exerted against teeth during the impression procedure were affected by the custom tray designs and varied according to the coronal shape, axis inclination and location of the teeth.

Analysis of Variance↗
PubMed2000

Collaborative work to evaluate toxicity on male reproductive organs by repeated dose studies in rats 23). A comparative 2- and 4-week repeated oral dose testicular toxicity study of boric acid in rats.

To assess the validity and limitations of 2-week repeated daily dosing to detect toxic effects on male reproductive organs in rodents, a comparative 2- and 4-week oral repeated dosing study of boric acid, a known testicular toxicant, was given to 6- or 8-week-old Crj:Wistar rats at daily levels of 0, 125, 250 and 500 mg/kg. The ages of the rats were selected so that they were all sacrificed at 10 weeks of age. The testes and epididymides were weighed at necropsy; histopathological specimens were prepared in a routine manner and stained with H&E or PAS-H. In addition, the sperm number and motility rates were evaluated. There were no boric acid-induced effects on reproductive organ weights and on gross behavior/appearance in any groups in either the 2- or 4-week studies. The sperm number and motility rate were not decreased in any group after 2 weeks, while both decreased in the 250 and 500 mg/kg groups after 4 weeks. Histopathologically, as evidence of toxicity at the early stage of boric acid exposure, retention of step 19 spermatids of stages IX-XI was observed in the testes of almost all rats treated with 500 mg/kg after both 2 weeks and 4 weeks. Degenerative/necrotic germ cells and multinucleated giant cell formation were observed in 2 weeks, though to a lesser extent than in 4 weeks. On stage analysis of germinal cells in 2 weeks, spermatogonia and spermatids of stage VII were found to be decreased, and pachytene spermatocytes of stage X were increased. In conclusion, the results indicate that if the selection of doses is appropriate, testicular toxicity of boric acid can be detected even after only 2 weeks of repeated daily oral treatment.

Administration, Oral↗
PubMed1998

Ultrasonic implantation of calcium metasilicate glass particles into PMMA.

Polymer materials for clinical applications should be bioactive and have a bone-bonding ability. In order to provide poly(methyl methacrylate) (PMMA) with bioactivity, granules (<45 microm) of a bioactive glass 50CaO.50SiO2 (mol %) were implanted into PMMA: they were suspended together with a piece of PMMA in a 40 tetrahydrofuran-60 ethanol (vol %) solution and ultrasonically agitated. The granules of <10 microm in size were impregnated at approximately 40-20 microm depth below the substrate surface. Two types were detected on the PMMA surface: (a) a glass-granule layer on PMMA, and (b) an inner granule layer, a PMMA layer, and an outer granule layer on the PMMA. The bioactivity of the implanted PMMA substrates was examined in vitro with a simulated body fluid (Kokubo solution). Apatite was precipitated on all glass granules and the whole substrate surfaces within 1 d. After 4 h soaking in the Kokubo solution, aggregates of apatite particles appeared on the substrate surface, independently of those on the glass granules, and they grew and proliferated on the whole subtrate surface in 7 d. Silica gel islands on PMMA due to the silicate anions from the glass were considered to induce nucleation of the apatite particles.

Journal Article↗
PubMed1997

Bioactivity of sol-gel derived organically modified silicates: part i: in vitro examination.

Bioactivity was investigated for several organically modified silicates (Ormosils) prepared through sol-gel processes. Ca(II)-free samples were biocompatible only, but Ca(II)containing samples were bioactive and deposited apatite during immersion in a simulated body fluid. The ease of silanol (Si-OH) group formation on the ormosils was considered a predominant factor controlling the bioactivity, while the effect of dissolved Ca(II) ions to increase the degree of supersaturation in the simulated body fluid is secondary.

Journal Article↗
PubMed1995

Secretion of TNF-alpha from macrophages following induction with a lignin derivative.

Macrophages derived from rat bone marrow were treated with macrophage colony stimulating factor (M-CSF) to obtain a sufficient number of cells for the tumor necrosis factor (TNF-alpha) assay. The present study has been designed to investigate whether the production of TNF-alpha, which induces multinucleated giant cell formation, is regulated by polyanions such as lignin derivatives. ELISA for TNF-alpha showed that the polyanion induced TNF-alpha production by macrophages. The secretion of TNF-alpha from the cells reached a maximum at 3-6 h, and then showed a slight decline. Northern blotting of TNF-alpha mRNA showed that the amount of TNF-alpha reached a maximum within 1 h of macrophage culture in the presence of a lignin derivative. On the other hand, TNF-alpha mRNA was undetectable in the control cells. It was concluded that stimuli such as that provided by lignin derivatives increases the amount of TNF-alpha mRNA, which is then followed by translation of TNF-alpha.

Animals↗
PubMed1995

Effect of tumor cell conditioned media on secretion of TNF-alpha by macrophages.

Conditioned medium obtained from rat liver (M cells) induced a greater than 3 fold increase in the proliferation of rat bone marrow macrophages. Non-specific esterase staining of the proliferated cells gave a positive result. The conditioned media obtained from 8 other established cell lines and 2 primary human cell cultures were also examined for their effects on cultured macrophages. All of the conditioned media tested increased macrophage proliferation. In addition, the conditioned media were examined to determine whether they induced TNF-alpha production in macrophages. TNF-alpha was not detected in the culture medium of the macrophages in the absence of conditioned medium derived from other cell cultures, but TNF-alpha production could be induced by the addition of these conditioned media. Conditioned media obtained from the cells of different species or tumor cell lines were more effective in inducing TNF-alpha production than those obtained from rat cell lines or normal tissue cell lines.

Animals↗
PubMed1994

Regulation of Ca2+ concentration by second messengers in newt olfactory receptor cell.

The role of IP3 in olfactory transduction is controversial. This issue was addressed by measuring intracellular Ca2+ concentration under voltage clamp in newt olfactory receptor cells. Odorant stimulation and dialysis of cells with cyclic AMP (cAMP) caused an increase in intracellular Ca2+ concentration that originated in the cilia, as expected from previous works. However, dialysis with IP3 caused a slower rise in Ca2+ concentration that originated in the cell body. Our results suggest that IP3 influences transduction by regulating the intracellular Ca2+ concentration, rather than by carrying the transduction current.

Animals↗