Jay R Goldberg

Publications and source records attributed to Jay R Goldberg.

11 recordsLinked to original sources

PubMed2004

The electrochemical and mechanical behavior of passivated and TiN/AlN-coated CoCrMo and Ti6Al4V alloys.

The mechanical and electrochemical behavior of the surface oxides of CoCrMo and Ti6Al4V alloys during fracture and repassivation play an important role in the corrosion of the taper interfaces of modular hip implants. This behavior was investigated in one group of CoCrMo and Ti6Al4V alloy samples passivated with nitric acid and another group coated with a novel TiN/AlN coating. The effects of mechanical load and sample potential on peak currents and time constants resulting from fracture of the surface oxide or coating, and the effects of mechanical load on scratch depth were investigated to determine the mechanical and electrochemical properties of the oxides or coating. The polarization behavior of the samples after fracture of the oxide or coating was also investigated. CoCrMo had a stronger surface oxide and higher interfacial adhesion strength, making it more resistant to fracture than Ti6Al4V. If undisturbed, the oxide on the surface of Ti6Al4V significantly reduced dissolution currents at a wider range of potentials than CoCrMo, making Ti6Al4V more resistant to corrosion. The TiN/AlN coating had a higher hardness and modulus of elasticity than CoCrMo and Ti6Al4V. It was much less susceptible to fracture, had a higher interfacial adhesion strength, and was a better barrier to ionic diffusion than the surface oxides on CoCrMo and Ti6Al4V. The coating provided increased corrosion and fretting resistance to the substrate alloys.

Alloys↗

PubMed2003

In vitro corrosion testing of modular hip tapers.

The in vivo fretting behavior of modular hip prostheses was simulated to determine the effects of material combination and a unique TiN/AlN coating on fretting and corrosion at the taper interface. Fretting current, open-circuit potential (OCP), and quantities of soluble debris were measured to determine the role of mechanically assisted crevice corrosion on fretting and corrosion of modular hip tapers. Test groups consisting of similar-alloy (Co-Cr-Mo head/Co-Cr-Mo neck), mixed-alloy (Co-Cr-Mo head/Ti-6Al-4V neck), and TiN/AlN-coated mixed-alloy modular hip taper couples were used. Loads required to initiate fretting were similar for all test groups and were well below loads produced by walking and other physical activities. Decreases in OCP and increases in fretting current observed during long-term cyclic loading were indicative of fretting and corrosion. Current measured after cessation of cyclic loading suggests that once the conditions for crevice corrosion are established, corrosion can continue in the absence of loading. The chemical, mechanical, and electrochemical measurements, along with microscopic inspections of the taper surfaces indicate that the fretting and corrosion behavior of similar- and mixed-alloy taper couples are similar and that the coated samples are more resistant to fretting and corrosion. The results of this study clearly indicate the role of mechanical loading in the corrosion process, and support the hypothesis of mechanically assisted crevice corrosion.

Alloys↗

PubMed2002

A multicenter retrieval study of the taper interfaces of modular hip prostheses.

A multicenter retrieval analysis of 231 modular hip implants was done to investigate the effects of material combination, metallurgic condition, flexural rigidity, head and neck moment arm, neck length, and implantation time on corrosion and fretting of modular taper surfaces. Scores for corrosion and fretting were assigned to medial, lateral, anterior, and posterior quadrants of the necks, and proximal and distal regions of the heads. Neck and head corrosion and fretting scores were found to be significantly higher for mixed alloy versus similar alloy couples. Moderate to severe corrosion was observed in 28% of the heads of similar alloy couples and 42% of the heads of mixed alloy couples. Differences in corrosion scores were observed between components made from the same base alloy, but of different metallurgic conditions. Corrosion and fretting scores tended to be higher for heads than necks. Implantation time and flexural rigidity of the neck were predictors of head and neck corrosion and head fretting. The results of this study suggest that in vivo corrosion of modular hip taper interfaces is attributable to a mechanically-assisted crevice corrosion process. Larger diameter necks will increase neck stiffness and may reduce fretting and subsequent corrosion of the taper interface regardless of the alloy used. Increasing neck diameter must be balanced, however, with the resulting loss of range of motion and joint stability.

Adult↗