Jane Frommer

Publications and source records attributed to Jane Frommer.

4 recordsLinked to original sources

PubMed2006

Atomically flat gold on elastomeric substrate.

We present a procedure to fabricate extremely smooth Au films supported on thin elastomeric (PDMS) substrates. Minimum rms roughness and largest grain size are obtained using Si wafers, coated with native oxide and release layers, as templates for the growth of thermally evaporated Au films. The wafers are held at a temperature of 300 degrees C during deposition. The Au films, up to 200 nm thick, are then transferred onto poly(dimethylsiloxane) substrates which have been previously surface-functionalized with a (3-mercaptopropyl)trimethoxysilane adhesion layer. The resulting Au films have been found by AFM to be extremely smooth with rms-roughness 2.5-4 angstroms and to exhibit a crystalline morphology with flat grains >500 nm in size. Thinner films, down to 20 nm, are grown at lower temperature and are comparably smooth, but with a loss in crystalline morphology. We compare the results of this optimized procedure with other gold films grown on mica sheets as templates and to those produced using Ti-O-Si interfacial chemistry.

Journal Article↗

PubMed2006

Controlling nanowear in a polymer by confining segmental relaxation.

Molecular relaxation of a copolymer designed for nano-electromechanical systems was chemically confined by varying the spacing between cross-links, delta(c). A critical cross-link spacing of 1-3 nm marks a transition in the nano-mechanical properties evaluated by atomic force microscopy. The transition reveals an interplay between the cross-link spacing and the length scale for backbone relaxation, xi(alpha), in cooperatively rearranging regions. For delta(c) >> xi(alpha), the natural backbone relaxation process is relatively unaffected by the cross-links and a ductile, low hardness behavior results. For delta(c) < xi(alpha), the cross-links directly interfere with backbone relaxation and confine segmental mobility, leading to a brittle, high hardness response.

Microscopy, Atomic Force↗

PubMed2006

Monolayered organosilicate toroids and related structures: A phase diagram for templating from block copolymers.

Here we report the controlled generation of micelle-templated organosilicate nanostructures resulting from self-assembly of a block copolymer/organosilicate mixture followed by organosilicate vitrification and copolymer thermolysis. Variation of solution condition and the copolymer/organosilicate mixture composition generates widely different film morphologies ranging from toroids to linear features to contiguous nanoporous monolayers. The use of reactive organosilicates for block copolymer templation generates functional inorganic nanostructures with thermal and mechanical stability.

Acrylamides↗

PubMed2004

Interfacial glass transition profiles in ultrathin, spin cast polymer films.

Interfacial glass transition temperature (T(g)) profiles in spin cast, ultrathin films of polystyrene and derivatives were investigated using shear-modulated scanning force microscopy. The transitions were measured as a function of film thickness (delta), molecular weight, and crosslinking density. The T(g)(delta) profiles were nonmonotonic and exhibited two regimes: (a) a sublayer extending about 10 nm from the substrate, with T(g) values lowered up to approximately 10 degrees C below the bulk value, and (b) an intermediate regime extending over 200 nm beyond the sublayer, with T(g) values exceeding the bulk value by up to 10 degrees C. Increasing the molecular weight was found to shift the T(g)(delta) profiles further from the substrate interface, on the order of 10 nm/kDa. Crosslinking the precast films elevated the absolute T(g) values, but had no effect on the spatial length scale of the T(g)(delta) profiles. These results are explained in the context of film preparation history and its influence on molecular mobility. Specifically, the observed rheological anisotropy is interpreted based on the combined effects of shear-induced structuring and thermally activated interdiffusion.

Journal Article↗