At least 91 records · Page 5Linked to original sources
PubMed1996

Cross-linking of dermal sheep collagen using a water-soluble carbodiimide.

A cross-linking method for collagen-based biomaterials was developed using the water-soluble carbodiimide 1-ethyl-3-(3-dimethyl aminopropyl)carbodiimide hydrochloride (EDC). Cross-linking using EDC involves the activation of carboxylic acid groups to give O-acylisourea groups, which form cross-links after reaction with free amine groups. Treatment of dermal sheep collagen (DSC) with EDC (E-DSC) resulted in materials with an increased shrinkage temperature (Ts) and a decreased free amine group content, showing that cross-linking occurred. Addition of N-hydroxysuccinimide to the EDC-containing cross-linking solution (E/N-DSC) increased the rate of cross-linking. Cross-linking increased the Ts of non-cross-linked DSC samples from 56 to 73 degrees C for E-DSC and to 86 degrees C for E/N-DSC samples, respectively. For both cross-linking methods a linear relation between the decrease in free amine group content and the increase in Ts was observed. The tensile strength and the high strain modulus of E/N-DSC samples decreased upon cross-linking from 18 to 15 MPa and from 26 to 16 MPa, respectively. The elongation at break of E/N-DSC increased upon cross-linking from 142 to 180%.

Acrylic Resins↗
PubMed1996

In vitro degradation of dermal sheep collagen cross-linked using a water-soluble carbodiimide.

Bacterial collagenase was used to study the susceptibility of dermal sheep collagen (DSC) cross-linked with a mixture of the water-soluble carbodiimide 1-ethyl-3-(3-dimethyl aminopropyl)-carbodiimide hydrochloride and N-hydroxysuccinimide (E/N-DSC) towards enzymatic degradation. Contrary to non-cross-linked DSC (N-DSC), which had a rate of weight-loss of 18.1% per hour upon degradation, no weight loss was observed for E/N-DSC during a 24 h degradation period. The tensile strength of the E/N-DSC samples decreased during this time period, resulting in partially degraded samples having 80% of the initial tensile strength remaining. The susceptibility of E/N-DSC samples towards enzymatic degradation could be controlled by varying the degree of cross-linking of the samples. Ethylene oxide sterilization of E/N-DSC samples made the material more resistant against degradation compared with non-sterilized E/N-DSC samples. This may be explained by a decrease of the adsorption of bacterial collagenase onto the collagen owing to reaction of ethylene oxide with remaining free amine groups in the collagen matrix.

Adsorption↗
PubMed1996

Poly(ethylene oxide)-modified carboxylated polystyrene latices--immobilization chemistry and protein adsorption.

alpha,omega-Diamino poly(ethylene oxides) (PEOs) with different molecular weights (148, 1000, and 3400) were covalently immobilized onto carboxylated polystyrene latices. The immobilization of PEO was carried out with N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide (EDC) and N-hydroxysuccinimide (NHS) in aqueous media. The reaction conditions were optimized to obtain a maximal coupling of PEO. The degree of coupling was determined by the surface concentration of amino groups. The maximal surface concentrations of amino groups were close to what is expected for a complete coverage of the surface with PEO. Adsorption of albumin from a buffer solution onto PEO-containing surfaces was about 85% less than the albumin uptake by unmodified polystyrene latices. Protein adsorption from plasma dilutions was lower on surfaces containing PEO molecules with a higher molecular weight. The reduction of the protein uptake from plasma by surfaces containing PEO-3400 molecules was only 40% compared to the adsorption to unmodified surfaces. These results indicate that plasma proteins have a low affinity for surfaces modified with PEO. However the PEO modified surfaces are by no means 'protein resistant' when exposed to plasma.

Adsorption↗
PubMed1996

The interactions between antithrombin III, thrombin and surface immobilized heparin.

The interactions between antithrombin III (ATIII), thrombin, and surface immobilized heparin were investigated. Carboxylated polystyrene modified with covalently immobilized albumin-heparin conjugate contain sites which can bind ATIII from buffer and plasma solutions. Approximately 65% of the ATIII molecules present at the heparinized surface either adsorbed from a buffer or plasma solution, exchanged with ATIII in buffer solution. The exchange between surface bound ATIII and ATIII in solution was repeated several times on the same heparinized surface. The number of binding sites that could bind and release ATIII was much higher when the heparinized surface was exposed to an ATIII containing buffer solution than to a plasma solution. The reduction in binding sites available for ATIII using plasma solutions as compared to buffer solutions could be explained by the competition of other plasma proteins with ATIII for the heparinized surface. It was observed that heparin binding proteins were able to compete with ATIII for binding to the immobilized heparin. Furthermore adsorption of proteins on the heparinized surface significantly reduced the availability of binding sites for ATIII. Exposure of thrombin to the heparinized surface resulted in thrombin activity at the surface. The thrombin activity on the heparinized surfaces was lower on surfaces with a higher ATIII concentration. The activity of surface bound thrombin was not affected by the presence of other plasma proteins. Enzymatically active thrombin molecules present at the heparinized surface were completely inactivated when the surface was exposed to a solution containing ATIII. The inactivation rate of surface bound thrombin by ATIII was higher than the rate of the uncatalyzed inactivation of thrombin in solution. Part of the Thrombin-Antithrombin III (TAT) complexes (10-20%) that were formed upon inactivation of thrombin remained bound to the heparinized surface. In general it was concluded that only the surface immobilized heparin molecules that can bind ATIII in a reversible way determine the anticoagulant properties of the surface. The mechanism of inactivation of a protease on a heparinized surface depends either on the catalytic effect of heparin on the inactivation rate of proteases by ATIII or on an increased uncatalytic inactivation due to increased concentrations of ATIII near the surface as compared to the concentration of ATIII in the bulk phase.

Adsorption↗
PubMed1996

The effect of protein adsorption on the anticoagulant activity of surface immobilized heparin.

The anticoagulant activity of albumin-heparin conjugates covalently immobilized on carboxylated polystyrene beads was determined before and after exposure to different plasma/PBS dilutions using a thrombin inhibition assay, a FXa inhibition assay, and a modified aPTT assay. Exposure of albumin-heparin modified surfaces (alb-hep surfaces) to plasma dilutions resulted in surfaces with a lower anticoagulant activity than surfaces which were not exposed to plasma dilutions. The reduction of the activity increased up to +/- 80% when the surfaces were exposed to solutions containing more than 70% plasma. Alb-hep surfaces incubated in plasma which was preexposed to heparin-Sepharose retained 30% of their initial activity. These observations were attributed to non-specific adsorption of plasma proteins onto the surface and to interaction of heparin binding proteins with the immobilized heparin. Both processes result in a decreased accessibility of the immobilized heparin and thus in a reduced anticoagulant activity displayed by the heparinized surface. Identification of adsorbed proteins with SDS gel electrophoresis and immunoblotting revealed that many different proteins were present at the heparinized surface. Only small differences were observed between the gel electrophoresis pattern of adsorbed proteins obtained from heparinized surfaces and from a surface containing immobilized albumin.

Adsorption↗
PubMed1995

Changes in the mechanical properties of dermal sheep collagen during in vitro degradation.

The changes in tensile strength, elongation at break, and high strain modulus of dermal sheep collagen (DSC) during in vitro degradation using bacterial collagenase were studied. The changes in mechanical properties were compared with the change in weight of the samples as a function of degradation time. DSC was crosslinked with either glutaraldehyde (GA) or hexamethylene diisocyanate (HMDIC). During degradation, the changes in mechanical properties of the N-DSC, H-DSC or G-DSC samples were more pronounced than the changes in the weight of the samples. Of the mechanical properties studied, the tensile strength was most susceptible to degradation of the DSC samples. After 2.5 h, N-DSC samples had lost only 55% of their initial weight, but the samples had no tensile strength left. Similar results were obtained for H-DSC, which retained no tensile strength after 24 h degradation, whereas only 45% of the initial weight was lost. G-DSC lost 3.5% of its weight after 24 h degradation, but only 25% of the initial tensile strength remained.

Amines↗
PubMed1995

Influence of ethylene oxide gas treatment on the in vitro degradation behavior of dermal sheep collagen.

The influence of ethylene oxide gas treatment on the in vitro degradation behavior of noncrosslinked, glutaraldehyde crosslinked or hexamethylene diisocyanate crosslinked dermal sheep collagen (DSC) using bacterial collagenase is described. The results obtained were compared with the degradation behavior of either nonsterilized or gamma-sterilized DSC. Upon ethylene oxide sterilization, reaction of ethylene oxide with the free amine groups of DSC occurred, which resulted in a decreased helix stability, as indicated by a lowering of the shrinkage temperature of all three types of DSC. Except for the low strain modulus the mechanical properties of the ethylene oxide sterilized materials were not significantly altered. gamma-Sterilization induced chain scission in all three types of DSC, resulting in a decrease of both the tensile strength and the high strain modulus of noncrosslinked and crosslinked DSC. When exposed to a solution of bacterial collagenase, ethylene oxide sterilized materials had a lower rate of degradation compared with nonsterilized DSC. This has been explained by a reduced adsorption of the collagenase onto the collagen matrix as a result of the introduction of pendant N-2-hydroxy ethyl groups.

Animals↗
PubMed1995

Heparin release from thermosensitive polymer coatings: in vivo studies.

Biomer/poly(N-isopropylacrylamide)/[poly(NiPAAm)] thermosensitive polymer blends were prepared and their application as heparin-releasing polymer coatings for the prevention of surface-induced thrombosis was examined. The advantage of using poly (NiPAAm)-based coatings as heparin-releasing polymers is based on the unique temperature-dependent swelling of these materials. At room temperature, i.e., below the lower critical solution temperature (LCST) of poly (NiPAAm), the Biomer/(poly(NiPAAm) coatings are highly swollen. The high swelling enables fast loading of hydrophilic macromolecules (e.g., heparin) into the coating by a solution sorption technique. At a body temperature, i.e., above the LCST of poly (NiPAAm) the coatings are in a deswollen state and the absorbed macromolecules may be slowly released from a dense coating via a diffusion controlled mechanism. Biomer/poly(NiPAAm) coatings were obtained by blending and coprecipitation of the two linear polymers, Biomer and (poly(NiPAAm). The structure and water-swelling properties of the coatings were examined. Significant differences in water swelling at room temperature (RT) and 37 degrees C were observed as a result of the thermosensitivity of poly (NiPAAm). The surface structure of the coatings in dry and swollen states at RT and 37 degrees C was examined by scanning electron microscopy. Heparin was loaded into the coatings via a solution sorption at room temperature. Kinetic studies of heparin loading demonstrated that maximum loading was obtained within 1 h. The in vitro (37 degrees C) release profiles were characterized by a rapid initial release due to the squeezing effect of the collapsing polymer network, followed by a slower release phase controlled by heparin diffusion through the dense coating. The short-term antithrombogenicity of intravenous polyurethane catheters coated with heparin-releasing Biomer/poly(NiPAAm) thermosensitive coating was evaluated in a canine animal model. The results show that the heparin release from Biomer/poly(NiPAAm)-coated surfaces resulted in a significant reduction of thrombus formation on test surfaces in contact with venous blood as compared to control surfaces.

Acrylic Resins↗
PubMed1995

The influence of surface morphology and wettability on the inflammatory response against poly(L-lactic acid): a semi-quantitative study with monoclonal antibodies.

In this study, the influence of surface morphology and wettability of both degradable and nondegradable polymer films on the inflammatory response after subcutaneous implantation in the rat was investigated. Degradable non-porous, porous, and "combi" (porous with a nonporous layer on one side) poly(L-lactic acid) (PLLA) films and nondegradable polytetrafluoroethylene (PTFE) and (porous) expanded PTFE (e-PTFE) were used. Contact angles measurements indicate that PLLA is more hydrophillic than PTFE. Assessment of the inflammatory response was performed after various periods of implantation (up till 180 days), with both conventional light microscopy and immunohistochemistry using monoclonal antibodies (mAbs). The inflammatory response observed initially can largely be considered as part of the wound healing reaction, and up till day 40 the inflammatory response against PLLA was minimally more intense than against PTFE (porous as well as nonporous). From day 40 on, the PLLA films provoke a more intense inflammatory response as compared to the PTFE films. Both porous PLLA and the porous side of the "combi" PLLA film provoke a more intense inflammatory response than nonporous PLLA and the nonporous side of the "combi" PLLA film, respectively. In general, PTFE and e-PTFE films provoke an inflammatory response which is minimally more intense than the one provoked by the sham operation. Almost no ingrowth of tissue was observed in the porous e-PTFE films. In contrast, there was abundant tissue ingrowth in and an inflammatory response against porous PLLA. It can be concluded that biodegradable PLLA films provoke a more intense inflammatory response than nondegradable PTFE films. Also, porosity enhances the inflammatory response. However, porosity enhances the inflammatory response only when the wettability of a biomaterial permits cellular ingrowth.

Animals↗
PubMed1995

Contact activation during incubation of five different polyurethanes or glass in plasma.

During blood-material interaction, the enzymes factor XII fragment (factor XIIf) and kallikrein are generated (contact activation). In this study, the enzymatic activities of factor XIIf and kallikrein were examined with an assay based on the conversion of tripeptide-p-nitroanilide substrate. With the use of aprotinin to inhibit kallikrein, the proteolytic activities of factor XIIf and kallikrein could be separately determined. In this in vitro study, two commercially available polyurethanes, Pellethane and Biomer; three custom synthesized polyurethanes; a biomerlike 2000 MW polytetramethyleneoxide containing polyurethane (PU-2000); an octadecyl extended (ODCE) biomer-like 2000 MW polytetramethyleneoxide containing polyurethane (PU-2000-ODCE); a hard-segment polyurethane (HS-PU); and glass (reference material) were incubated in 25% diluted plasma. In both series of experiments, glass caused the highest amidolytic activities by factor XIIf and kallikrein compared with any of the polyurethanes. In contrast, within the polyurethane group of materials, lower amidolytic activities by factor XIIf and kallikrein were measured on the custom-made polyurethanes than on the commercially available polyurethanes, although the differences among the polyurethanes were small. In addition, the influence of different ratios of material surface to the plasma incubation volume was studied. An increased ratio of surface area over plasma volume resulted in reduced contact activation, suggesting that plasma components are the limiting factor.

Analysis of Variance↗
PubMed1995

Interaction of antithrombin III with surface-immobilized albumin-heparin conjugates.

The interaction between antithrombin III (ATIII) and albumin-heparin conjugates covalently coupled onto carboxylated polystyrene beads either in buffer containing albumin or in plasma was studied using 14C-labeled ATIII. Binding isotherms of ATIII were modeled using a summation of two Langmuir equations. These equations describe the binding of ATIII to two different sets of binding sites, one with a high, the other with a low affinity of ATIII to these sites are 9 x 10(6) L/mol and 0.3 x 10(6) L/mol, respectively. The binding of ATIII to surface binding sites with a high affinity for ATIII was correlated with the presence of specific ATIII binding sites in the immobilized heparin. Binding of ATIII from albumin solutions to binding sites with a low affinity for ATIII was dominated by nonspecific binding of ATIII to the immobilized heparin. A third small fraction of the surface bound. ATIII is probably adsorbed to sites on the surface not covered with heparin. In the case of the binding of ATIII to the heparinized surface from plasma solutions, a fraction of initially adsorbed ATIII was desorbed by other plasma proteins. This desorption in combination with direct competition between ATIII and other plasma proteins resulted in lower ATIII surface concentrations using plasma as compared to the ATIII surface concentrations obtained using albumin solutions. The binding of ATIII to nonspecific binding sites was almost completely inhibited in the presence of plasma proteins. The amount of ATIII bound to immobilized heparin via specific ATIII binding sites was 30% lower in plasma solutions as compared to the specific binding of ATIII using albumin solutions. It is concluded that the accessibility of immobilized heparin for ATIII in plasma decreases by binding of heparin-binding proteins onto the immobilized heparin and/or adsorption of other plasma proteins on the heparinized surface.

Absorption↗
PubMed1994

Biocompatibility and tissue regenerating capacity of crosslinked dermal sheep collagen.

The biocompatibility and tissue regenerating capacity of four crosslinked dermal sheep collagens (DSC) was studied. In vitro, the four DSC versions were found to be noncytotoxic or very low in cytotoxicity. After subcutaneous implantation in rats, hexamethylenediisocyanate-crosslinked DSC (HDSC) seldom induced an increased infiltration of neutrophils or macrophages, as compared with normal wound healing; whereas new formation of collagen was observed. DSC crosslinked with glutaraldehyde (GDSC) followed by reaction with NaBH4 shortly after implantation showed an increased infiltration of neutrophils with a deviant morphology. Furthermore, a high incidence of calcification was observed, which may explain the minor ingrowth of giant cells and fibroblasts, and the poor formation of new rat collagen. Acyl azide-crosslinked DSC (AaDSC) first induced an increased infiltration of macrophages, and then of giant cells, both with high lipid formation. AaDSC degraded at least twice as slowly as HDSC and GDSC, finally leaving a matrix of newly formed rat collagen. Samples crosslinked with 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride and N-hydroxysuccinimide (ENDSC) induced the same mild cellular reaction as HDSC; whereas, similar to AaDSC, the degradation rate was slow and an optimal rat collagen matrix was formed. Of the crosslinked DSC samples, ENDSC seems most promising for tissue regeneration.

Animals↗
PubMed1994

Preparation and characterization of albumin-heparin microspheres.

Albumin-heparin microspheres were prepared by a two-step process which involved the preparation of a soluble albumin-heparin conjugate, followed by formation of microspheres from this conjugate or by a double cross-linking technique involving both coupling of soluble albumin and heparin and microsphere stabilization in one step. The first technique was superior since it allowed better control over the composition and the homogeneity of the microspheres. Microspheres could be prepared with a diameter of 5-35 microns. The size could be controlled by adjusting the emulsification conditions. The degree of swelling of the microspheres was sensitive to external stimuli, and increased with increasing pH and decreasing ionic strength of the medium.

Albumins↗
PubMed1994

Supporting, microporous, elastomeric, degradable prostheses to improve the arterialization of autologous vein grafts.

Arterial reconstructions with vein grafts fail more frequently than with arterial grafts. One of the causes of graft failure is damage due to overstretching of the graft wall. Overstretching is caused because the vein graft, which has a poorly developed medium, cannot withstand the arterial blood pressures. The aim of this study is to evaluate whether damage due to overstretching can be prevented and a gradual adaptation of the vein graft to the arterial blood pressures can be induced by applying a microporous, elastomeric, degradable prosthesis around the vein graft. Therefore, autologous vein grafts (length 1.0 cm) with and without supporting prostheses (composite vein grafts and control vein grafts, respectively) were interposed into both carotid arteries of rabbits. Microporous, elastomeric, biofragmentable polyurethane-based prostheses and microporous, elastomeric, biodegradable prostheses made of poly-epsilon-caprolactone or a copolymer of epsilon-caprolactone and 3.6-dimethyl-1,4-morpholine-2,5-dione with a monomer ratio of 95.5:4.5 were prepared. The grafts were evaluated up to 6 wk after implantation. The control vein grafts showed severe destructive changes such as de-endothelialization, disruption of the media with oedema, degradation of the elastic laminae and infiltration of polymorphonuclear leucocytes into the vein graft wall, leading eventually to a fibrotic wall. In contrast, the composite vein grafts showed a preservation of the smooth muscle cell layers and the elastic laminae with only few polymorphonuclear leucocytes infiltrated into the vein graft wall.(ABSTRACT TRUNCATED AT 250 WORDS)

Animals↗
PubMed1994

In vitro leukocyte adhesion to modified polyurethane surfaces: III. Effect of flow, fluid medium, and platelets on PMN adhesion.

The operation of filters used to remove leukocytes from red cell concentrates may depend on the adhesion and mechanical trapping of leukocytes. If adhesion is a major component of filtration then filter materials which augment leukocyte adhesion will be useful. In previous leukocyte adhesion studies, done without flow, poly(ethyleneimene) (PEI) modified polyurethane (PU) films were shown to have greater adhesion when compared with unmodified PU. Since filtration is done under flow conditions, it was decided to study PMN adhesion at a number of flow rates using an established parallel plate flow cell. The influence of divalent cations, plasma and platelets were investigated in the presence of red cells, 40% Hematocrit. The number of adherent PMNs to the PEI modified films was always substantially higher than that for the unmodified ones when the shear rate was set at 30 s-1. When using Tyrode's solution containing albumin, with or without divalent cations, a maximum in PMN adhesion was found between the shear rates of 10 and 100 s-1. With Tyrode's solution containing albumin and with 10% (v/v) plasma in saline, the addition of platelets increased PMN adhesion when divalent cations were absent. Adhesion levels with 10% (v/v) plasma in saline were reduced when compared to Tyrode's solution containing albumin without divalent cations. These results support the use of filtration conditions where the concentration of plasma is reduced and the concentration of divalent cations is increased. Detailed evaluation of filter function with flow rate is also recommended. A cell adhesion promoting polymer coating, such as PEI, may be useful in improving filter efficiency.

Cell Adhesion↗
PubMed1994

Tissue regenerating capacity of carbodiimide-crosslinked dermal sheep collagen during repair of the abdominal wall.

In future, the function of collagen-based biomaterials as temporary scaffolds for the generation of new tissue may be emphasized. In this study the function of dermal sheep collagen (DSC) crosslinked with carbodiimide (ENDSC) as repair material for abdominal wall defects in rats was compared with that of commercial hexamethylenediisocyanate-crosslinked HDSC. The results indicate that early after implantation both ENDSC and HDSC functioned well as a matrix for cellular ingrowth. However during further implantation HDSC soon degraded resulting in herniations, while ENDSC showed a delay in the degradation time of at least 20 weeks. ENDSC thereby enabled collagen new-formation and functioned as a guidance for muscle overgrowth. These results are very promising concerning the problem of the ongoing foreign body reaction with continuing risk of implant rejection observed in clinical practice with non-degradable materials.

Abdominal Muscles↗
PubMed1993

Poly(ethyleneimine) modified filters for the removal of leukocytes from blood.

Polyurethane membrane filters and filters coated with poly(ethyleneimine) were used to investigate the influence of leukocyte adhesion during filtration. Treatment of the filters with an aqueous solution of 1% (w/v) poly(ethyleneimine) (PEI) led to the introduction of amine groups at the filter surfaces, as was confirmed by X-ray photoelectron spectroscopy. The modification procedure did not significantly change the porous structure in the filters, as was demonstrated by SEM and porometry. Using 14C-labeled poly(ethyleneimine) it was shown that nearly a complete coverage (approximately 0.1 mg/m2) was achieved that did not desorb from the filter surface during contact with blood plasma. When the filtration was carried out with purified leukocytes in the absence of red cells, platelets, and blood plasma, the number of cells removed by modified filters (> 95%) was significantly higher as compared to the removal with unmodified filters (approximately 80%). However, no significant differences between the filters were found when the filtration was performed with whole blood. This finding was unexpected, because it was shown before that immobilization of poly(ethyleneimine) on solid polyurethane film, surfaces promoted the adhesion of leukocytes from whole blood. Apparently, the adhesive properties of the PEI diminish during filtration. Filter coating of commercial leukocyte filters composed of polyester fibers also had no effect on the removal of leukocytes from whole blood. It was postulated that morphological factors, such as filter shape, roughness, tortuosity, and porosity rather than the physicochemical properties of the filter surface influence cell adhesion to the filter surface, and through that the filtration process.

Biocompatible Materials↗