Biomedical subjects
Publications and source records attributed to Ilhan A Aksay.
We study the dynamics of surfactant micelles at the solid-liquid interface using a new atomic force-microscopic imaging mode to visualize the nanometer-level structural features of the micelles and the picometer-level lattice of the substrate simultaneously. We find that defects created in a crystalline micellar array by the scanning probe tip self-heal flawlessly in less than 6 ms.
Orientational order of surfactant micelles and proteins on crystalline templates has been observed but, given that the template unit cell is significantly smaller than the characteristic size of the adsorbate, this order cannot be attributed to lattice epitaxy. We interpret the template-directed orientation of rodlike molecular assemblies as arising from anisotropic van der Waals interactions between the assembly and crystalline surfaces where the anisotropic van der Waals interaction is calculated using the Lifshitz methodology. Provided the assembly is sufficiently large, substrate anisotropy provides a torque that overcomes rotational Brownian motion near the surface. The probability of a particular orientation is computed by solving a Smoluchowski equation that describes the balance between van der Waals and Brownian torques. Torque aligns both micelles and protein fibrils; the interaction energy is minimized when the assembly lies perpendicular to a symmetry axis of a crystalline substrate. Theoretical predictions agree with experiments for both hemi-cylindrical micelles and protein fibrils adsorbed on graphite.
A process is described to produce single sheets of functionalized graphene through thermal exfoliation of graphite oxide. The process yields a wrinkled sheet structure resulting from reaction sites involved in oxidation and reduction processes. The topological features of single sheets, as measured by atomic force microscopy, closely match predictions of first-principles atomistic modeling. Although graphite oxide is an insulator, functionalized graphene produced by this method is electrically conducting.
Optical microscope images of graphite oxide (GO) reveal the occurrence of fault lines resulting from the oxidative processes. The fault lines and cracks of GO are also responsible for their much smaller size compared with the starting graphite materials. We propose an unzipping mechanism to explain the formation of cracks on GO and cutting of carbon nanotubes in an oxidizing acid. GO unzipping is initiated by the strain generated by the cooperative alignment of epoxy groups on a carbon lattice. We employ two small GO platelets to show that through the binding of a new epoxy group or the hopping of a nearby existing epoxy group, the unzipping process can be continued during the oxidative process of graphite. The same epoxy group binding pattern is also likely to be present in an oxidized carbon nanotube and cause its breakup.
In the synthesis of the disordered lyotropic liquid crystalline L3 sponge phase prepared with the cosurfactants cetylpyridinium chloride and hexanol, aqueous NaCl solution is used as the solvent. When this sponge phase is used as the template for L3 silica-phase processing, we replace NaCl with HCl to facilitate the acid catalysis of tetramethoxysilane in forming a templated silica gel, assuming that changing the solvent from NaCl(aq) to HCl(aq) of equivalent ionic strength does not affect the stability range of the L3 phase. In this work, we confirm that changing the pH of the solvent from neutral to acidic (with HCl) has negligible effect on the L3 phase region. Equivalent ionic strength is provided by either NaCl(aq) or HCl(aq) solvent; therefore, a similar phase behavior is observed regardless of which aqueous solvent is used.
Dimensionally stable, optically clear, highly porous (approximately 65% of the apparent volume), and high surface area (up to 1400 m(2)/g) silica monoliths were fabricated as thick disks (0.5 cm) by templating the isotropic liquid crystalline L(3) phase with silica through the hydrolysis and condensation of a silicon alkoxide and then removing the organic constituents by supercritical ethanol extraction. The L(3) liquid crystal is a stable phase formed by the cosurfactants cetylpyridinium chloride monohydrate and hexanol in HCl(aq) solvent. Extracted 0.5 cm thick disks exhibited a low ratio of scattered to transmitted visible light (1.5 x 10(-)(6) at 22 degrees from the surface normal). The degree of silica condensation in the monoliths was high, as determined by (29)Si NMR measurements of Q(3) and Q(4) peak intensities (0.53 and 0.47, respectively). As a result, the extracted and dried monoliths were mechanically robust and did not fracture when infiltrated by organic solvents. Photoactive liquid monomers were infiltrated into extracted silica monoliths and polymerized in situ, demonstrating the possible application of templated silica to optical storage technology.
Citric acid has been shown to act as an agent for increasing the solubility of aluminum oxyhydroxides in aqueous solutions of high (>2.47 mol/mol) hydroxide-to-aluminum ratios. Conversely, citric acid also colloidally stabilizes particles in aqueous suspensions of aluminum-containing particles. Solutions of aluminum chloride, with and without citric acid added, were titrated with NaOH(aq). The presence and size of particles were determined using quasi-elastic light scattering. In solutions that contained no citric acid, particles formed instantaneously when NaOH(aq) was added but these were observed to rapidly diminish in size, disappearing at OH/Al ratios below 2.5 mol/mol. When the OH/Al ratio was raised beyond 2.5 by adding more NaOH(aq), suspensions of colloidally stable particles formed. Large polycations containing 13 aluminum atoms were detected by (27)Al solution NMR in citric-acid-free solutions with OH/Al ratios slightly lower than 2.5. In comparison, adding citric acid to solutions of aluminum chloride inhibited the formation of large aluminum-containing polycations. The absence of the polycations prevents or retards the subsequent formation of particles, indicating that the polycations, when present, act as seeds to the formation of new particles. Particles did not form in solutions with a citric acid/aluminum ratio of 0.8 until sufficient NaOH(aq) was added to raise the OH/Al ratio to 3.29. By comparison, lower amounts of citric acid did not prevent particles from forming but did retard the rate of growth.
Many naturally occurring biomaterials are composed of laminated structures in which layers of beta-sheet proteins alternate with layers of inorganic mineral. These ordered laminates often have structural and mechanical properties that differ significantly from those of nonbiological materials. An important step in the construction of novel biomaterials is the creation of composites wherein a de novo designed protein assembles into an ordered structure. To achieve this goal, we layered a de novo protein onto the surface of highly ordered pyrolytic graphite (HOPG). The protein was derived from a combinatorial library of novel sequences designed to fold into amphiphilic beta-sheet structures. Atomic force microscopy reveals that the protein assembles on the HOPG surface into ordered fibers aligned in three orientations at 120 degrees to each other. The symmetry and extent of the ordered regions indicate that the hexagonal lattice underlying the graphite surface templates assembly of millions of protein molecules into a highly ordered structure.