Biomedical subjects
Publications and source records attributed to Hailin Cong.
Binary colloidal crystals (BCCs) were prepared from two kinds of poly(styrene-methyl methacrylate-acrylic acid) colloids approximately 190 and approximately 380 nm in diameter by the codeposition method. A variety of array patterns of BCCs were observed and characterized by AFM and SEM. The significance of these colloidal arrays in crystallography has been discussed preliminarily.
In this article, a series of ionene polymers were synthesized and used to coat fused-silica capillaries for the separation of recombinant and urinary human erythropoietin (rhEPO and uEPO) standards by CE. The influence of the charge density of coatings on the separation of rhEPO and uEPO glycoforms was investigated. Then, we further studied the method for fast separation and detection of rhEPO and uEPO standards by CE-ESI-MS. The influence of several CE and MS operating parameters, such as the concentration of CE running buffer, applied external pressure, and the composition and flow rate of sheath liquid on CE-ESI-MS was studied. The results demonstrated that when the capillary was permanently coated with 6,6-ionene and the pH value of acetic acid-ammonium acetate running buffer was 4.80 and 5.50, respectively, a significantly reproducible separation was achieved for rhEPO and uEPO glycoforms. In the online CE-ESI-MS experiments, we not only achieved the online MS signal of uEPO, but also obtained baseline separation of three major rhEPO glycoforms successfully and reproducibly on the 6,6-ionene-coated capillaries. Furthermore, the standard mixture of rhEPO and uEPO was separated, and two incompletely resolved peaks that were identified to be rhEPO and uEPO by the unique MS "fingerprint" were obtained. Additionally, the molecular weight of rhEPO and uEPO were verified and compared to the results by MALDI-TOF-MS. It can be concluded that, in contrast to other indirect methods, the online CE-ESI-MS technique with the combination of the advantages of both CE and MS shows great potential for the separation and detection of rhEPO doping directly in competitive sports.
The microheterogeneity of recombinant human erythropoietin (rhEPO) was analyzed by capillary electrophoresis (CE) using a capillary coated with 6,6-ionene. The applicability of a volatile electrolyte for fast analysis of tryptic fragments of rhEPO with online CE-electrospray ionization-mass spectrometry (ESI-MS) was investigated, resulting in a reproducible separation of eleven rhEPO tryptic fragments within 22 min under the following conditions: running buffer 300 mmol/L acetic acid-ammonium acetate (HAc-NH4Ac), pH 4.80, separation voltage -15 kV and capillary temperature 25 degrees C. The proposed method is rapid and effective, and can be used for the structural analysis of related proteins.
In this paper, we reported the preparation of macroporous Au materials using organic colloidal crystals as templates and their catalytic activity for electroless copper deposition. The poly(styrene-methyl methacrylate-acrylic acid) (P(St-MMA-AA)) copolymer colloids were deposited in an orderly manner onto the silicon surface, together with the infiltration of the Au nanoparticles into the interspaces of the colloids. The formed hybrid colloidal crystal subsequently was sintered at approximately 550 degrees C to remove the organic components fully to obtain a macroporous Au framework with three-dimensional ordered porous structure. The pore diameter was around 310 nm and almost monodisperse. It was demonstrated that the macroporous Au materials exhibit catalytic activity and can induce electroless copper deposition.
A stairlike colloidal crystal thin film composed of poly(styrene-methyl methacrylate-acrylic acid) (P(St-MMA-AA)) monodispersed colloids was fabricated on an inclined silicon substrate. Different bright colors were observed on the various parts of the film with different layers as white light irradiated perpendicularly on it. The relationship between the colors and layers of the film was investigated and discussed according to the principle of thin film interference. On the basis of the phenomenon of thin film interference, a one-layer colloidal film having uniform color was researched and it would display diverse colors before and after swollen by styrene (St). A circular stairlike colloidal film was achieved to mimic the colors of the peacock tail feather.
A covalently attached sandwich structure between layers and particles has been fabricated from z.sbnd;COOH-containing copolymer latex particles and z.sbnd;N(2)(+)-containing polymers by self-assembly combined with a UV irradiation technique. The ionic bonds involving the layers and particles change to covalent bonds under UV irradiation and the sandwich structure become very stable toward polar organic solvents and electrolyte aqueous solutions.