Organometallic[bond]polyoxometalate hybrid compounds: metallosalen compounds modified by Keggin type polyoxometalates.

Hybrid compounds with two functional centers consisting of a metallosalen moiety (M[bond]salen; M = Mn, Co, Ni, and Pd) connected by an alkylene bridging group to a lacunary Keggin type polyoxometalate were synthesized and characterized. In these metallosalen-polyoxometalate compounds (M[bond]salen[bond]POM) it was shown by the use of a combination of UV[bond]vis, (1)H NMR, EPR, XPS, and cyclic voltammetry measurements that the polyoxometalate exerts a significant intramolecular electronic effect on the metallosalen moiety leading to formation of an oxidized metallosalen moiety. For the Mn[bond]salen[bond]POM, the metallosalen center is best described as a metal[bond]salen cation radical species; that is, a localized "hole" is formed on the salen ligand. For the other M[bond]salen[bond]POM compounds, the metallosalen moiety can be described as a hybrid of a metal[bond]salen cation radical species and an oxidized metal[bond]salen species, that is, a delocalized "hole" is formed at the metallosalen center. It is proposed that these oxidized metallosalen centers are best characterized as stabilized charge transfer (metallosalen donor[bond]polyoxometalate acceptor) complexes despite the relatively large distance between the two functional centers.

Journal Article↗

PubMed2003

Solution-processed anodes from layer-structure materials for high-efficiency polymer light-emitting diodes.

The development of low-cost, large-area electronic applications requires the deposition of active materials in simple and inexpensive techniques at room temperature, properties usually associated with polymer films. In this study, we demonstrate the integration of solution-processed inorganic films in light-emitting diodes. The layered transition metal dichalcogenide (LTMDC) films are deposited through Li intercalation and exfoliation in aqueous solution and partially oxidized in an oxygen plasma generator. The chemical composition and thickness of the LTMDC and corresponding transition metal oxide (TMO) films are investigated by X-ray photoelectron spectroscopy. The morphology and topography of the films are studied by atomic force microscopy. X-ray powder diffraction is used to determine the orientation of the LTMDC film. Finally, the LTMDC and their corresponding oxides are utilized as hole-injecting and electron-blocking materials in polymer light-emitting diodes with the general structure ITO/LTMDC/TMO/polyfluorene/Ca/Al. Efficient hole injection and electron blocking by the inorganic layers result in outstanding device performance and high efficiency.

Journal Article↗

PubMed2002

Alkali metal intercalated fullerene-like MS(2) (M = W, Mo) nanoparticles and their properties.

Layered metal disulfides-MS(2) (M = Mo, W) in the form of fullerene-like nanoparticles and in the form of platelets (crystallites of the 2H polytype) have been intercalated by exposure to alkali metal (potassium and sodium) vapor using a two-zone transport method. The composition of the intercalated systems was established using X-ray energy dispersive spectrometer and X-ray photoelectron spectroscopy (XPS). The alkali metal concentration in the host lattice was found to depend on the kind of sample and the experimental conditions. Furthermore, an inhomogeneity of the intercalated samples was observed. The product consisted of both nonintercalated and intercalated phases. X-ray diffraction analysis and transmission electron microscopy of the samples, which were not exposed to the ambient atmosphere, showed that they suffered little change in their lattice parameters. On the other hand, after exposure to ambient atmosphere, substantial increase in the interplanar spacing (3-5 A) was observed for the intercalated phases. Insertion of one to two water molecules per intercalated metal atom was suggested as a possible explanation for this large expansion along the c-axis. Deintercalation of the hydrated alkali atoms and restacking of the MS(2) layers was observed in all the samples after prolonged exposure to the atmosphere. Electric field induced deintercalation of the alkali metal atoms from the host lattice was also observed by means of the XPS technique. Magnetic moment measurements for all the samples indicate a diamagnetic to paramagnetic transition after intercalation. Measurements of the transport properties reveal a semiconductor to metal transition for the heavily K intercalated 2H-MoS(2). Other samples show several orders of magnitude decrease in resistivity and two- to five-fold decrease in activation energies upon intercalation. These modifications are believed to occur via charge transfer from the alkali metal to the conduction band of the host lattice. Recovery of the pristine compound properties (diamagnetism and semiconductivity) was observed as a result of deintercalation.

Journal Article↗

PubMed2002

Hybrid composites of monodisperse pi-conjugated rodlike organic compounds and semiconductor quantum particles.

Composite materials of quantum particles (Q-particles) arranged in layers within crystalline powders of pi-conjugated, rodlike dicarboxylic acids are reported. The synthesis of the composites, either as three-dimensional crystals or as thin films at the air-water interface, comprises a two-step process: 1) The preparation of the Cd salts 6 (Cd), 8 (Cd) or Pb salts 6 (Pb), 8 (Pb) of the oligo(p-phenyleneethynylene)dicarboxylic acids 6 (H), 8 (H), in which the metal ions are arranged in ribbons and are separated by the long axis of the organic molecules, as demonstrated by X-ray powder diffraction analysis of the solids and grazing incidence X-ray diffraction analysis of the films on water. 2) Topotactic solid/gas reaction of these salts with H(2)S to convert the metal ions into Q-particles of CdS or PbS embedded in the organic matrix that consists of the acids 6 (H) and 8 (H). These hybrid materials have been characterized by X-ray photoelectron spectroscopy and transmission electron microscopy.