PubMed2001

Water sorption and solubility of dental composites and identification of monomers released in an aqueous environment.

Water sorption and solubility of six proprietary composite resin materials were assessed, and monomers eluted from the organic matrix during water storage identified. Water sorption and solubility tests were carried out with the following storage times: 4 h, 24 h and 7, 60 and 180 days. After storage, water sorption and solubility were determined. Eluted monomers were analysed by high performance liquid chromatography (HPLC). Correlation between the retention time of the registered peak and the reference peak was observed, and UV-spectra confirmed the identity. The results showed an increase in water sorption until equilibrium for all materials with one exception. The solubility behaviour of the composite resin materials tested revealed variations, with both mass decrease and increase. The resin composition influences the water sorption and solubility behaviour of composite resin materials. The HPLC analysis of eluted components revealed that triethyleneglycol dimethacrylate (TEGDMA) was the main monomer released. Maximal monomer concentration in the eluate was observed after 7 days. During the test period, quantifiable quantities of urethanedimethacrylate (UEDMA) monomer were observed, whereas 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy)-phenyl]propane (Bis-GMA) was only found in detectable quantities. No detectable quantities of bisphenol-A were observed during the test period.

Analysis of Variance↗
PubMed1987

Carbon/graphite fiber reinforced poly(methyl methacrylate): properties under dry and wet conditions.

The flexural properties of poly(methyl methacrylate) (PMMA) reinforced with carbon/graphite (C/G) fibers with three different surface treatments were investigated by transverse bend testing after dry and wet storage. The fibers used were (1) commercially available fibers, (2) cleaned fibers, and (3) cleaned and sized fibers. The coating agents of commercial unidirectional and braided C/G fibers as well as impurities on C/G fibers for medical uses were characterized by means of high-performance liquid chromatography (HPLC). The agar overlay technique was used to assess the cytotoxicity of leachable elements from different fibers and processed composites. Composites with both unidirectional and braided tubular C/G fibers were investigated after storage in water. Fracture stress and flexural modulus decreased when "commercial" fibers were used as reinforcing material. Composites with cleaned and sized fibers gave only minor differences in flexural properties after dry and wet storage. By means of SEM micrographs the adhesion behavior of unsized C/G fibers, epoxy sized fibers, cleaned fibers, and cleaned and sized fibers were assessed. After water storage a substantial part of the cleaned fibers adhered to the matrix material. The adhesion capacity of the other fibers was reduced since the water absorption caused separation of fiber and matrix.

Biocompatible Materials↗