Publications and source records attributed to Glen L Niebur.

7 recordsLinked to original sources

PubMed2006

Microdamage propagation in trabecular bone due to changes in loading mode.

Microdamage induced by falls or other abnormal loads that cause shear stress in trabecular bone could impair the mechanical properties of the proximal femur or spine. Existing microdamage may also increase the initiation and propagation of further microdamage during subsequent normal, on-axis, loading conditions, resulting in atraumatic or "spontaneous" fractures. Microdamage formation due to shear and compressive strains was studied in 14 on-axis cylindrical bovine tibial trabecular bone specimens. Microdamage was induced by a torsional overload followed by an on-axis compressive overload and quantified microscopically. Fluorescent agents were used to label microdamage and differentiate damage due to the two loading modes. Both the microcrack density and diffuse damage area caused by the torsional overload increased with increasing shear strain from the center to the edge of the specimen. However, the mean microcrack length was uniform across the specimen, suggesting that microcrack length is limited by microstructural features. The mean density of microcracks caused by compressive overloading was slightly higher near the center of the specimen, and the diffuse damage area was uniform across the specimen. Over 20% of the microcracks formed in the initial torsional overloading propagated during compression. Moreover the propagating microcracks were, on average, longer than microcracks formed by a single overload. As such, changes in loading mode can cause propagation of microcracks beyond the microstructural barriers that normally limit the length. Damage induced by in vivo off-axis loads such as falls may similarly propagate during subsequent normal loading, which could affect both remodeling activity and fracture susceptibility.

Animals↗

PubMed2004

Comparison of the elastic and yield properties of human femoral trabecular and cortical bone tissue.

The ability to determine trabecular bone tissue elastic and failure properties has biological and clinical importance. To date, trabecular tissue yield strains remain unknown due to experimental difficulties, and elastic moduli studies have reported controversial results. We hypothesized that the elastic and tensile and compressive yield properties of trabecular tissue are similar to those of cortical tissue. Effective tissue modulus and yield strains were calibrated for cadaveric human femoral neck specimens taken from 11 donors, using a combination of apparent-level mechanical testing and specimen-specific, high-resolution, nonlinear finite element modeling. The trabecular tissue properties were then compared to measured elastic modulus and tensile yield strain of human femoral diaphyseal cortical bone specimens obtained from a similar cohort of 34 donors. Cortical tissue properties were obtained by statistically eliminating the effects of vascular porosity. Results indicated that mean elastic modulus was 10% lower (p<0.05) for the trabecular tissue (18.0+/-2.8 GPa) than for the cortical tissue (19.9+/-1.8 GPa), and the 0.2% offset tensile yield strain was 15% lower for the trabecular tissue (0.62+/-0.04% vs. 0.73+/-0.05%, p<0.001). The tensile-compressive yield strength asymmetry for the trabecular tissue, 0.62 on average, was similar to values reported in the literature for cortical bone. We conclude that while the elastic modulus and yield strains for trabecular tissue are just slightly lower than those of cortical tissue, because of the cumulative effect of these differences, tissue strength is about 25% greater for cortical bone.

Aged↗

PubMed2004

Preparation of on-axis cylindrical trabecular bone specimens using micro-CT imaging.

The Orientation of trabecular bone specimens for mechanical testing must be carefully controlled. A method for accurately preparing on-axis cylindrical specimens using high-resolution micro-CT imaging was developed. Sixteen cylindrical specimens were prepared from eight bovine tibiae. High-resolution finite element models were generated from micro-CT images of parallelepipeds and used to determine the principal material coordinate system of each parallelepiped. A cylindrical specimen was then machined with a diamond coring bit. The resulting specimens were scanned again to evaluate the orientation. The average deviation between the principal fabric orientation and the longitudinal axis of the cylindrical specimen was only 4.70 +/- 3.11 degrees.

Animals↗

PubMed2003

Effects of damage on the orthotropic material symmetry of bovine tibial trabecular bone.

The macroscopic mechanical properties of trabecular bone can be predicted by its architecture using theoretical relationships between the elastic and architectural properties. Microdamage caused by overloading or fatigue decreases the apparent elastic moduli of trabecular bone requiring these relationships to be modified to predict the damaged elastic properties. In the case of isotropic damage, the apparent level elastic properties could be determined by multiplying all of the elastic constants by a single scalar factor. If the damage is anisotropic, the elastic constants may change by differing factors and the material coordinate system could become misaligned with the fabric coordinate system. High-resolution finite element models were used to simulate damage overloading on seven trabecular bone specimens subjected to pure shear strain in two planes. Comparison of the apparent elastic moduli of the specimens before and after damage showed that the reduction of the elastic moduli was anisotropic. This suggests that the microdamage within the specimens was inhomogeneous. However, after damage the specimens exhibited nearly orthotropic material symmetry as they did before damage. Changes in the orientation of the orthotropic material coordinate system were also small and occurred primarily in the transverse plane. Thus, while damage in trabecular bone is anisotropic, the material coordinate system remains aligned with the fabric tensor.

Animals↗

PubMed2002

Biomechanical effects of intraspecimen variations in tissue modulus for trabecular bone.

Although recent nanoindentation studies have revealed the existence of substantial variations in tissue modulus within single specimens of trabecular bone, little is known regarding the biomechanical effects of such intraspecimen variations. In this study, high-resolution finite element modeling was used to investigate these effects. With limited literature information on the spatial distribution of intraspecimen variations in tissue modulus, two plausible spatial distributions were evaluated. In addition, three specimens (human femoral neck, human vertebral body, and bovine proximal tibia) were studied to assess the role of trabecular architecture. Results indicated that for all specimen/distribution combinations, the apparent modulus of the whole specimen decreased nonlinearly with increasing coefficient of variation (COV) of tissue modulus within the specimen. Apparent modulus decreased by <4% when tissue modulus COV was increased from 0% to 20% but decreased by 7-24%, depending on the assumed spatial distribution, for an increase in tissue modulus COV from 20% to 50%. For compressive loading to the elastic limit, increasing tissue modulus COV from 20% to 50% caused up to a 28-fold increase in the amount of failed tissue, depending on assumed spatial distribution and trabecular architecture. We conclude that intraspecimen variations in tissue modulus, if large, may have appreciable effects on trabecular apparent modulus and tissue-level failure. Since the observed effects depended on the assumed spatial distribution of the tissue modulus variations, a description of such distributions, particularly as a function of age, disease, and drug treatment, may provide new insight into trabecular bone structure-function relationships.

Adult↗

PubMed2002

Biaxial failure behavior of bovine tibial trabecular bone.

Multiaxial failure properties of trabecular bone are important for modeling of whole bone fracture and can provide insight into structure-function relationships. There is currently no consensus on the most appropriate form of multiaxial yield criterion for trabecular bone. Using experimentally validated, high-resolution, non-linear finite element models, biaxial plain strain boundary conditions were applied to seven bovine tibial specimens. The dependence of multiaxial yield properties on volume fraction was investigated to quantify the interspecimen heterogeneity in yield stresses and strains. Two specimens were further analyzed to determine the yield properties for a wide range of biaxial strain loading conditions. The locations and quantities of tissue level yielding were compared for on-axis, transverse, and biaxial apparent level yielding to elucidate the micromechanical failure mechanisms. As reported for uniaxial loading of trabecular bone, the yield strains in multiaxial loading did not depend on volume fraction, whereas the yield stresses did. Micromechanical analysis indicated that the failure mechanisms in the on-axis and transverse loading directions were mostly independent. Consistent with this, the biaxial yield properties were best described by independent curves for on-axis and transverse loading. These findings establish that the multiaxial failure of trabecular bone is predominantly governed by the strain along the loading direction, requiring separate analytical expressions for each orthotropic axis to capture the apparent level yield behavior.

Animals↗

PubMedDate not supplied

Axial-shear interaction effects on microdamage in bovine tibial trabecular bone.

Because many osteoporotic fractures occur during a fall, understanding the effect of off-axis loads on initiation and propagation of microdamage in trabecular bone should provide further insight into the biomechanics of age-related fractures. Fourteen on-axis cylindrical specimens were prepared from 12 bovine tibiae. Fluorescent stains were used to label the microdamage due to a sequence of compressive and torsional damaging loads. The mean decrease in Young's modulus was over four times greater than that in the shear modulus after the compressive overload, while there was no difference between the decrease in the axial and torsional stiffnesses after the torsional overload. The total microcrack density due to compression was uniform across the radius of the cylindrical specimens, while the mean density of microcracks due to torsional overloading increased from the axis of the cylindrical specimen to the circumference. The high density of microcracks near the axis of the specimen following torsional overloading was unexpected because of the low strains. Nearly 40% of the microcracks due to torsion propagated from pre-existing microcracks caused by axial compression, indicating that existing microcracks may extend at relatively low strain if the loading mode changes. The propagating microcracks were, on average, longer than the initiating microcracks due to either compressive or torsional loading. Damage due to axial compression appears to increase the susceptibility of trabecular bone to damage propagation during subsequent torsional loads, but it has little effect on the elastic properties in shear.

Animals↗