PubMed2006

Magnetic properties of BiMnO3 studied with Dc and Ac magnetization and specific heat.

Magnetic and specific heat measurements were performed in a single-phased powder BiMnO3 sample prepared at 6 GPa and 1383 K. The imaginary part of the ac susceptibilities showed strong frequency dependence below the ferromagnetic Curie temperature of 98 K. The relaxation measurements revealed time-dependent magnetic properties below 98 K. These data indicate the appearance of a "spin-glass-like" state in BiMnO3. Specific heat measurements showed the existence of ferromagnetic spin waves. However, no simple term Cm [directly proportional] T3/2 was found indicating an unconventional behavior of the magnetic specific heat. The Debye temperature was estimated to be 410 K using isostructural compounds BiScO3 and BiCrO3.

Journal Article↗

PubMed2006

Spinel-to-CaFe2O4-type structural transformation in LiMn2O4 under high pressure.

A new form of LiMn2O4 is reported. The structure is the CaFe2O4-type and 6% denser than the spinel. The structure transformation was achieved by heating at 6 GPa. Analysis of the neutron diffraction pattern confirmed an average of the structure; the unit cell was orthorhombic at a = 8.8336(5) angstroms, b = 2.83387(18) angstroms, and c = 10.6535(7) angstroms (Pnma). Electron diffraction patterns indicated an order of superstructure 3a x b x c, which might be initiated by Li vacancies. The exact composition is estimated at Li(0.92)Mn2O4 from the structure analysis and quantity of intercalated Li. The polycrystalline CaFe2O4-type compound showed semiconducting-like characters over the studied range above 5 K. The activation energy was reduced to approximately 0.27 eV from approximately 0.40 eV at the spinel form, suggesting a possible enhancement of hopping mobility. Magnetic and specific-heat data indicated a magnetically glassy transition at approximately 10 K. As the CaFe2O4-type transition was observed for the mineral MgAl2O4, hence the new form of the lithium manganese oxide would provide valuable opportunities to study not only the magnetism of strongly correlated electrons but also the thermodynamics of the phase transition in the mantle.

Journal Article↗

PubMed2006

BiScO3: centrosymmetric BiMnO3-type oxide.

With neutron powder diffraction, electron diffraction, and second-harmonic generation, we have shown that BiScO3 has a structure closely related to that of multiferroic BiMnO3, but BiScO3 crystallizes in the centrosymmetric space group of C2/c. These results bring up a question about the origin of ferroelectricity in BiMnO3. BiScO3 may serve as a model system to understand the role of Mn3+ ions in the ferroelectricity of BiMnO3.

Journal Article↗

PubMed2004

Electron microscope studies of nano-domain structures in Ru-based magneto-superconductors: RuSr(2)Gd(1.5)Ce(0.5)Cu(2)O(10-delta) (Ru-1222) and RuSr(2)GdCu(2)O(8) (Ru-1212).

Microstructures of the RuSr(2)Gd(1.5)Ce(0.5)Cu(2)O(10-delta) (Ru-1222) and RuSr(2)GdCu(2)O(8) (Ru-1212) magneto-superconductors have been investigated by using selected-area electron diffraction, convergent-beam electron diffraction, dark-field electron microscopy and high-resolution electron microscopy at room temperature. Both Ru-1212 and Ru-1222 consist of nm-size domains stacked along the [Formula: see text] direction, where the domains are formed by two types of superstructures due to ordering of rotated RuO(6) octahedra about the c-axis. In Ru-1212, both primitive-and body-centered tetragonal superstructures (the possible space groups: P4/mbm and I4/mcm) are derived to form the corresponding nm-domains. It is of great interest that Ru-1212 consists of domains of two crystallographically different superstructures, while the similar domains observed in Ru-1222 have crystallographically identical superstructure with an orthorhombic symmetry (possible space group: Aeam), related by 90 degrees rotation around the c-axis (Yokosawa et al., 2003, submitted for publication).

Journal Article↗

PubMed2003

Superconductivity in two-dimensional CoO2 layers.

Since the discovery of high-transition-temperature (high-T(c)) superconductivity in layered copper oxides, many researchers have searched for similar behaviour in other layered metal oxides involving 3d-transition metals, such as cobalt and nickel. Such attempts have so far failed, with the result that the copper oxide layer is thought to be essential for superconductivity. Here we report that Na(x)CoO2*yH2O (x approximately 0.35, y approximately 1.3) is a superconductor with a T(c) of about 5 K. This compound consists of two-dimensional CoO2 layers separated by a thick insulating layer of Na+ ions and H2O molecules. There is a marked resemblance in superconducting properties between the present material and high-T(c) copper oxides, suggesting that the two systems have similar underlying physics.

Journal Article↗