Publications and source records attributed to E Hellwig.

At least 37 records · Page 2Linked to original sources
PubMed2000

Effect of different luting procedures on the seating of ceramic inlays.

This in vitro study evaluated the effect of different luting procedures on the proper seating of ceramic inlays and on the marginal seal through microleakage testing. Sixty mesial-, occlusal-, distal- (MOD) cavities were prepared in third molars, and distributed among four groups. In the control group 1, the cavity surface was treated with dentin and enamel bonding agents; ceramic inlays were placed into the cavity and light cured. In group 2, the dentin and enamel bonding agents were cured prior to the placing of the inlays, and following the insertion. In group 3, the inlays were luted without enamel bonding. In group 4, the inlays were cemented using a one-bottle bonding and two times light curing. The groups with only one time light curing at the end of the luting process exhibited the smallest luting space following cementation. The smallest dye penetration values were obtained for the two groups with separate light curing of the dentin bonding agent. Reducing the film thickness of polymerized dentin bonding agents, i.e. by changing the composition of the bonding agents, could facilitate proper seating of ceramic inlays together with a better marginal seal.

Acid Etching, Dental↗
PubMed2000

An in vitro assessment of the strength of porcelain veneers dependent on tooth preparation.

The treatment of teeth using veneer restorations combines aesthetic and functional improvements with a low destructive technique. Different kinds of tooth preparation techniques are described in the literature for this kind of restoration. This in vitro study aimed to examine the influence of the incisal preparation on the loadability of teeth restored with porcelain laminate veneers. Thirty-six selected mandibular incisors were randomly assigned to three groups with 12 teeth per group. In the first group, only the facial surface was prepared. In the second group, the preparation included a rounded incisal edge and a distinct chamfer lingually. The third group served as an unprepared control. Empress(R) veneers were then fabricated and cemented with a low viscous luting composite material. After 120 days storage in Ringer's solution, the specimens were loaded incisally to the point of failure. Statistical analysis of the results showed significant differences between the series (P=0.0103). Group 2 (with preparation of the incisal edge) exhibited the lowest fracture resistance (466+/-99 N) (N, mean forces). When prepared only facially, the teeth restored with Empress veneers reached the strength of unprepared teeth. Compared with the biting force described for incisors in the literature, the in vitro loadability reached in this investigation seems to jusitify the clinical use of both preparation designs tested.

Aluminum Silicates↗
PubMed2000

Fluoride release from light-curing restorative materials.

PURPOSE: To measure the in vitro fluoride release from three polyacid-modified resin-based composites (Dyract AP, Compoglass F, F2000) and one resin-modified glass-ionomer cement (Vitremer VLC) for 28 days in two different buffer solutions. MATERIAL AND METHODS: 30 cylindrical specimens of each material were prepared. Subsequently, 15 samples of each material were stored in neutral (pH 6.8) and acidic (pH 4.0) buffer solution (5 mL), respectively. After 4, 8, 12 hrs and 1, 2, 4, 8, 14 days, respectively, the samples were transferred into new solutions. The fluoride content was determined with a fluoride sensitive electrode. Data were analyzed with ANOVA, followed by closed-test-procedure based on Kruskal-Wallis. RESULTS: Compared to the neutral solution, all materials showed a significantly higher release of fluoride in acidic environment within the 28-day period (P < 0.001, ANOVA). In acidic buffer solution Vitremer VLC and Compoglass F showed a significantly higher fluoride release than F2000 and Dyract AP (P < 0.001, closed-test-procedure). In neutral solution Dyract AP showed the significantly lowest release (P < 0.001, closed-test-procedure). Fluoride release from the materials tested is higher in an acidic environment than in a neutral environment.

Analysis of Variance↗
PubMed1999

Effect of toothbrushing on fluoride release of polyacid-modified composite resins.

The aim of the study was to evaluate the fluoride release of polyacid-modified composite resins (Dyr-act, Compoglass) submitted to brushing abrasion. Twenty samples were taken from each material and stored in a buffer solution (pH 4.0) for 12 days. Each day, the samples were transferred to a fresh solution. Ten samples of each material were brushed in an automatic tooth-brushing machine (250 strokes, 260-g load) every fourth day. The remaining samples were not subjected to brushing. Fluoride content of the solutions was measured with a fluoride sensitive electrode after the addition of TISAB. Statistical analysis demonstrated significant differences between the two materials with regard to cumulative fluoride release within the 12 days of the experiment. However, no difference was observed between the fluoride release of the brushed samples compared to the unbrushed specimens. This was true for both, the cumulative fluoride release and its release on the day following brushing. It is assumed that regular brushing of the tested materials did not influence their release of fluoride and that brushing of polyacid-modified composite resins does not lead to maintaining their initially high level of fluoride release.

Analysis of Variance↗
PubMed1999

Root lesions in a group of 50-60 year-old Germans related to clinical and social factors.

From a preventive point of view collection of data concerning carious and non-carious cervical tooth defects is definitely important. Consequently, the prevalence and distribution of different root lesions were studied and correlated with behavioral and biological factors in 50- to 60-year-old German individuals (n = 298). Additionally, the data were correlated with characteristics concerning oral health and known risk factors such as gender, educational level, and presence of plaque. An interview included questions on sociodemographic and socioeconomic characteristics, dental and general health status, and various behavioral parameters. During clinical examination data concerning coronal and root lesions, restorations, probing depth, gingival bleeding, and dental plaque were obtained. The participants represented a social middle class population with a high awareness of dental health. Obviously, for the participants, known risk factors for root decay such as gender, educational level and plaque index were of minor importance. Factors correlating with root caries were: (a) number of missing teeth, (b) probing depth, (c) smoking habit, (d) regular dental attendance and (e) the reason for the last dental treatment. Additionally, the prevalence of non cariogenic lesions, primarily resulting from increased but wrongly performed oral self care, seems gradually to relieve carious root destruction.

DMF Index↗
PubMed1999

Correlation of transversal microradiography and microhardness on in situ-induced demineralization in irradiated and nonirradiated human dental enamel.

The objective was to evaluate whether a correlation exists between microhardness (MH) and transversal microradiographical (TMR) data for in situ-induced caries lesions in irradiated and nonirradiated human enamel. Enamel specimens were prepared from the lingual and buccal surfaces of 20 freshly extracted, caries-free third molars. The surfaces were polished (4000 grit). Either the lingual or the buccal specimen of each tooth was irradiated with 60 Gy; the other sample was not irradiated. Two irradiated and two nonirradiated specimens were inserted into both buccal aspects of each of five intraoral mandibular appliances. The appliances were worn by five persons for 6 weeks day and night. One side was brushed daily with a fluoride-free toothpaste; on the other side, dental plaque was allowed to grow. Individual oral hygiene was performed without any fluorides. During meals, the appliance was stored in 10% sucrose solution. Then the enamel specimens were cut perpendicular to their oral surface. The cut surface was polished (4000 grit) and the Knoop hardness number (KHN) was measured across the lesions, at 25, 50 and 75 microm from the oral surface. After MH testing the samples were polished again, thereby reducing the surface by about 10 microm. Subsequently, the slabs were ground to a thickness of 90 microm, and studied by means of TMR. Mineral loss was calculated with dedicated software at the locations corresponding to the MH testing. A total of 120 paired data was submitted to linear-regression analysis. Neither MH nor TMR showed significant differences between irradiated and nonirradiated enamel lesions. A linear relation was found between square root of KHN and the mineral volume percent. In naturally induced caries lesions, MH values can be converted to mineral volume percent using the equation [21.19 + 3.66 x square root of KHN]. This equation fits the data with a reliable correlation coefficient (r2=0.915).

Adult↗
PubMed1999

Fluoride release/uptake of polyacid-modified resin composites (compomers) in neutral and acidic buffer solutions.

The aim of the present study was to evaluate the fluoride uptake/release of polyacid-modified resin composites (compomers) in neutral and acidic buffer solutions. Two compomers (Dyract and Compoglass) were tested and the conventional glass-ionomer cement (GIC) Vivaglass Base served as a control. Forty specimens were fabricated from each of the respective materials. Twenty of these specimens were placed in artificial saliva and the other 20 specimens in a fluoridated dentifrice slurry for 5 min. Then, 10 fluoridated and 10 non-fluoridated specimens were immersed in a neutral buffer solution (pH 6.8), and the other specimens were immersed in an acidic solution (pH 4.0). After 1, 2, 3, 4, and 5 days the samples were again placed in either a fluoridated dentifrice slurry or saliva for 5 min, after which time they were transferred to fresh buffer solutions. The fluoride content of the solutions was assessed with a fluoride sensitive electrode. Fluoride release from all the materials decreased continuously during the experiment, with a significantly higher release in the acidic solution compared to the neutral buffer solution. Fluoridation did not result in an increased fluoride release for the compomers. However, the conventional GIC revealed a significantly higher fluoride release after fluoridation. It is concluded that Dyract and Compoglass can not be replenished with fluoride, irrespective of the pH value of the environment.

Analysis of Variance↗
PubMed1999

Influence of acidified fluoride gel on abrasion resistance of eroded enamel.

The objective of the study was to evaluate the abrasion resistance of eroded enamel brushed with an acidified fluoride gel. Each enamel specimen was prepared from one of 64 bovine incisors. The specimens were embedded in acrylic resin, ground flat, polished and subsequently covered with a tape exposing an area of 1.8x10.0 mm in the center of the enamel specimens. The samples were alternatingly stored in a demineralizing solution (5 min) and a remineralizing solution (1min) four times. An acidic soft drink (Sprite Light(R)) served as a demineralizing solution and artificial saliva was used as a remineralizing solution. After each remineralization the specimens were brushed in an automatic brushing machine (2,000 strokes, 2.5 N load) and subsequently stored again in saliva (1 min). A mixture of artificial saliva (5 ml) with a gel (1 ml) based on the formulation of Elmex(R) gelée (Wybert, Lörrach, Germany) served as an abrasive slurry. Thirty seconds after brushing, the slurry was removed from the specimens by rinsing with destilled water. For each of 16 specimens the following gels (A-D) were used: gels A (pH 7.0) and B (pH 4.5) were unfluoridated; gels C (pH 7.0) and D (Elmex gelée; pH 4.5) contained 1.25% F-. After two cycles the specimens were kept in the saliva for 8 h. Finally the tape was removed and the abrasion was determined profilometrically. The following values (mean +/- SD) were obtained and statistically analyzed by analysis of variance and Wilcoxon two-sample tests (p</=0.01): gel A, 0.96+/-0.24 microm; B, 1.58+/-0.32 microm; C, 0. 71+/-0.23 microm; D, 0.25+/-0.08 microm. The differences between all experimental groups were statistically significant. It is assumed that treatment of enamel erosions with an acidified fluoride gel results in a higher abrasion resistance compared to gels which are either unfluoridated or neutral.

Amines↗
PubMed1999

Dental status of schoolchildren from a rural community in Cameroon.

This study assessed the dental health status of children in a rural community in Cameroon. The investigation was carried out in 1996 on a total of 403 pupils aged between 5-17 years. The children were divided into 3 age groups, (I-III): I: 5-8 years (n = 157), II: 9-12 years (n = 191), II: 13-17 years (n = 55). The teeth were examined for dmft/DMFT, CPI, opacities and treatment needs. 22.6 per cent of the pupils were caries free, and the following mean dmft/DMFT-values were obtained: Age group I, dmft: 2.26 + 2.84, DMFT: 0.85 + 1.39. Group II, dmft: 0.60 + 1.35, DMFT: 2.76 + 2.74. Group III, dmft: 0.05 + 0.22; DMFT: 5.12 + 3.04. Opacities or other enamel disorders were observed in 16.9 per cent of the children. 68.7 per cent of them needed invasive dental treatment and 61.3 per cent required restorative treatment only. 7.4 per cent needed extractions and 25.6 per cent required prevention/sealant care as sole measure. 6.6 per cent of the children showed CPI-grade 0. The majority scored CPI-grade 1 (37.7 per cent) and grade 2 (49.9 per cent). The reported data suggest that improved dental health mindedness and availability of oral health care services are required in order to reduce oral health diseases.

Adolescent↗
PubMed1998

Clinical evaluation of a hybrid composite and a polyacid-modified composite resin in Class-II restorations in deciduous molars.

The aim of this prospective study, conducted in a dental practice was to evaluate the success rate of a hybrid composite material (TPH-Spectrum; Dentsply DeTrey, Konstanz, Germany) and a polyacid-modified composite resin (Compoglass; Vivadent, Schaan, Liechtenstein) in Class II restorations in primary molars after 1 year. A total of 190 restorations (96 with TPH-Spectrum and 94 with Compoglass) were inserted in 52 children. TPH-Spectrum was applied using the total etching technique, whereas Compoglass was inserted without acid etching prior to application of the bonding adhesive. The restorations were assessed according to the Ryge criteria, directly after placement and after 1 year. After 12 months, 6.4% of the Compoglass and 3.1% of the TPH-Spectrum restorations were clinically unacceptable and had to be renewed. The fillings with Compoglass revealed a tendency to lower evaluation scores with respect to color matching, cavosurface discoloration, anatomic form, margin integrity and caries assessment than the restorations with TPH-Spectrum. However, these differences were statistically not significant. The results of the present investigation show that, at least for a period of 1 year, both the hybrid composite TPH-Spectrum and the polyacid-modified composite resin Compoglass are suitable materials for restoration of deciduous molars. However, owing to the fewer treatment steps required for application of a polyacid-modified composite resin, this type of material may be more favorable for restoring primary molars.

Chi-Square Distribution↗
PubMed1998

Toothbrushing abrasion of polyacid-modified composites in neutral and acidic buffer solutions.

STATEMENT OF PROBLEM: Polyacid-modified composites are recommended for use in lesions that are subjected to toothbrushing abrasion and acidic challenges, such as cervical lesions. There is little information whether these materials are able to withstand degradation due to erosive attacks and toothbrushing abrasion. PURPOSE: This study evaluated the resistance of polyacid-modified composites against toothbrushing abrasion under acidic and neutral conditions. METHODS: Forty specimens fabricated of each of two polyacid-modified composites (Dyract, Compoglass) were investigated. For each composite group, 20 specimens were placed in a neutral solution (pH: 6.8) and 20 specimens were placed in an acidic solution (pH: 3.0) for 24 hours. All specimens were brushed in an automatic toothbrushing machine, then subjected to storage in the respective buffer solution (8 hours), followed by brushing three times. Abrasion was determined profilometrically. RESULTS: For both materials, abrasion in the acidic environment was significantly higher compared with neutral conditions. Thus, Compoglass composite demonstrated a lower abrasion resistance than Dyract composite. CONCLUSION: The abrasion resistance of the investigated materials was reduced under acidic conditions.

Acids↗
PubMed1998

Evaluation of the apical seal of root canal fillings with different methods.

The purpose of the study was to compare dye penetration methods conducted passively, under negative pressure, or under high pressure conditions. Ninety human maxillary incisors were instrumented and obturated with either the lateral condensation or single cone technique. India ink was used as a dye for passive and negative pressure (60 Torr) penetration methods. For dye penetration under high pressure conditions (200 MPa), a colored epoxy resin was used. Apical leakage was linearly measured evaluating both the root surface that showed the highest degree of penetration and all four surfaces of each root. The results revealed no significant difference between passive and negative pressure penetration methods. The amount of apical leakage obtained using dye penetration under high pressure conditions was significantly lower. Lateral condensation and single cone techniques yielded similar sealing abilities. It is concluded that there is no need to use negative pressure for evaluating the sealing ability of root canal fillings in vitro.

Carbon↗
PubMed1998

Marginal leakage in class II-restorations after use of ceramic-inserts luted with different materials.

The efficiency of using prefabricated ceramic inlays to prevent microleakage has been discussed in different investigations. The purpose of this study was to evaluate the marginal microleakage of a new glass ceramic inlay system in combination with two different composite luting materials and one polyacid-modified composite, respectively. Standardized class II cavities (n = 60) were filled with (1) Empress inlays fixed with a highly viscous luting composite as a control group, and with glass ceramic inlays (Cerana) in combination with (2) a highly viscous luting composite, (3) a low-viscous luting composite and (4) a polyacid-modified composite, respectively. After thermocycling the marginal quality was analysed with scanning electron microscopy, and the dye penetration along the cavity walls was measured. The use of the Cerana inlays with a polyacid-modified composite resin did not reveal a good marginal adaptation. However, the combination of the Cerana and the Empress inlays with the highly viscous composite exhibited a comparable marginal fit. Within the limitations of an in vitro study it is concluded that the combination of the new glass ceramic inlays with a polyacid-modified composite cannot be recommended for clinical use.

Aluminum Silicates↗
PubMed1998

Brushing abrasion of eroded dentin after application of sodium fluoride solutions.

The aim of the present in vitro study was to evaluate the influence of sodium fluoride solutions on brushing abrasion of eroded dentin. Dentin specimens were prepared from 60 bovine incisors. The specimens were embedded in acrylic resin, ground flat, polished and subsequently covered with tape exposing an area of 1.8 mm x 10.0 mm in the center of the exposed dentin. The samples were alternatingly stored in a demineralizing solution (5 min) and a remineralizing solution (1 min) for 5 times. The erosive soft drink Sprite light(R) served as a demineralizing solution and artificial saliva was used as a remineralizing solution. Prior to storage in artificial saliva 15 specimens were each treated for 1 min with 250 and 2,000 ppm fluoride solution, respectively. Fifteen specimens were treated with distilled water instead of the fluoride solution (= eroded controls). The remaining samples were neither eroded with the soft drink nor fluoridated (= uneroded controls). After each immersion in artificial saliva the specimens were submitted to abrasion in a toothbrushing machine. After 5 demineralization-remineralization brushing cycles the total amount of tooth wear due to erosion and subsequent abrasion was profilometrically evaluated. Statistical analysis revealed the significantly lowest wear in the uneroded controls and the highest amount of abrasion in the eroded controls. Application of the fluoride solutions increased the wear resistance of the eroded dentin specimens, showing significantly better protection by the high-concentration compared to the low-concentration solution. The susceptibility to abrasion of the eroded dentin specimens treated with the high-concentration fluoride solution did not differ significantly from the uneroded dentin samples. It is concluded that application of 2,000 ppm sodium fluoride solutions immediately before toothbrushing significantly reduces abrasion of eroded dentin in vitro.

Animals↗
PubMed1997

In vivo study on the effectiveness of a lacquer containing CaF2/NaF in treating dentine hypersensitivity.

The purpose of this double-blind study was to evaluate the effectiveness of a commercially available fluoride lacquer (Bifluorid 12) containing CaF2 (6%) and NaF (6%) in reducing dentine hypersensitivity. A fluoride lacquer containing only NaF (6%) served as a control. Twenty-five adult patients complaining about at least two hypersensitive teeth participated in this study. In each patient and at each appointment, one tooth was treated with Bifluorid 12, while the other was treated with the control substance. Sensitivity levels were determined before and after the application of each lacquer at baseline as well as at 1, 2 and 3 weeks after the start of study. The final evaluation of hypersensitivity was performed at 4 weeks, and follow-ups were undertaken at 6 and 12 months. A reproducible air blast stimulus and a visual analogue scale were used for evaluation. Results demonstrated a distinct reduction of hypersensitivity after 1, 2 and 3 weeks in the Bifluorid 12 group. Initially, no obvious effects could be observed in the control group. However, a clear alleviation could be observed after 2 and 3 weeks with the control. After 4 weeks, the overall sensitivity scores were comparably low, without any significant differences between the two fluoride lacquers. In both groups, the effects of treatment were seen over the 12-month observation period. Bifluorid 12 was considered at least comparable to the control. It is concluded from this study that Bifluorid 12 is effective in the initial reduction of dentine hypersensitivity. The combination of CaF2/NaF can be recommended for clinical use.

Adult↗
PubMed1997

Fluoride uptake in dentin with and without simulating dentinal fluid flow.

The aim of the present study was to compare fluoride uptake of dentin with and without simulating dentinal fluid flow. Eighty-five dentinal discs were prepared from retained human molars. Seventeen discs were used to assess baseline fluoride content (controls). Sixty-eight discs were evenly distributed among two experimental groups and were fixed for 24 h in a two-chamber device allowing for simulating dentinal fluid flow. Thirty-four samples were treated with dentifrice slurry containing a low fluoride concentration (Elmex, dilution 1:5); the remaining discs were treated with a solution of a high fluoride concentration (Elmex Fluid). For the perfused group, each of the 17 discs of the high and low concentration fluoride groups were constantly perfused during the experiment. The remaining fluoridated specimens were not perfused. All specimens were assayed for KOH-soluble fluoride and structurally bound fluoride. Structurally bound fluoride was determined in three successive layers of 20 microns each. Uptake of KOH-soluble fluoride was significantly higher in the specimens fluoridated with Elmex Fluid compared to the samples treated with the dentifrice slurry. The uptake of KOH-soluble fluoride was not influenced by perfusion of the dentinal discs. However, perfusion resulted in lower acquisition of structurally bound fluoride in the samples treated with the dentifrice slurry. After application of Elmex Fluid, no significant difference was found in the amount of structurally bound fluoride between the perfused specimens and non-perfused samples. It is suggested that further studies on fluoride uptake in dentin should use a model simulating outward dentinal fluid flow.

Analysis of Variance↗
PubMed1997

Correlation of microhardness and wear in differently eroded bovine dental enamel.

The purpose of the study was to compare the microhardness data of differently eroded enamel surfaces with the wear caused by toothbrushing. Sixty bovine enamel specimens were polished and prepared for microhardness determination. The polished surfaces were covered with tape except for a 1.3 x 10.0 mm window. Fifteen specimens each were stored in an erosive beverage (Sprite Light) for either 1, 5 or 15 min. Each specimen was immersed in 10 ml of the beverage. The remaining 15 specimens were not eroded. Interferometrical analysis revealed that substance loss after 15 min of erosion was negligibly low (about 75 mm). In all specimens Vickers microhardness determinations were conducted on eroded (= final hardness) and non-eroded (= initial hardness) enamel surfaces. The specimens were subsequently submitted to toothbrushing abrasion using a slurry consisting of 1 g non-fluoridated dentifrice in 5 ml artificial saliva. The total amount of tooth wear due to erosion and subsequent abrasion was profilometrically evaluated. Statistical analysis revealed a significant decrease in hardness and a significant increase in wear with increasing time of storage in the erosive beverage. Overall regression analysis yielded a statistically significant correlation between both initial and final hardness and the amount of tooth wear. The correlation of abrasion and final hardness could be described by a quadratic mathematical function. It is concluded that the susceptibility of eroded enamel to toothbrushing abrasion can be correlated with Vickers microhardness values, thereby suggesting an overproportionate increase of abrasion with decreasing hardness values.

Animals↗