PubMed1991

The bonding behavior of calcite to bone.

Plates of calcite (CaCO3) were implanted in rabbit tibiae, and their biocompatibility and bonding ability to bone were studied. The plates were also implanted subfascially in rabbit muscle for 8 weeks, and changes on their surfaces in the body were examined. Contact microradiography and Giemsa surface stain demonstrated direct bonding between calcite and bone without interpositions. The average failure load of the interface between calcite and bone was 4.11 kg, indicating an adequate strength of bonding. However, a Ca-P-rich layer, which formed on the surfaces of other bioactive ceramics in vivo, was not detected by a scanning electron microscope-electron probe x-ray microanalyzer. Scanning electron micrographs of the surface of calcite implanted subfascially for 8 weeks showed marked degradation and a rough surface. However, the surface apatite layer was not detected by thin-film x-ray diffraction analysis and Fourier transform infrared reflection spectroscopy. Calcite is a biodegradable material that bonds to bone without a surface apatite layer. The mechanical bonding provided by the anchoring effect of the newly formed bone into the surface roughness of calcite is considered to be a major factor in calcite-bone bonding.

Animals↗

PubMed1991

Bone bonding mechanism of beta-tricalcium phosphate.

It has been proposed that the formation of a surface apatite layer in vivo on surface active ceramics is an essential condition for chemical bonding between ceramics and bone tissue. To clarify the difference in bone-bonding mechanisms between surface active ceramics and bioresorbable ceramics, two experiments were performed using plates of dense beta-tricalcium phosphate (beta-TCP). First, plates of beta-TCP were implanted subcutaneously in rats for 8 weeks. Surface change due to bioresorption was observed with scanning electron microscopy. Formation of the apatite layer on the surface was investigated using thin-film x-ray diffraction and Fourier transform infrared reflection spectroscopy. Second, plates of beta-TCP were implanted in tibiae of rabbits for 8 and 25 weeks and subjected to the detaching test to measure bone-bonding strength. beta-TCP bonded strongly to bone. Undecalcified sections of the interface of bone and beta-TCP were examined with SEM-EPMA. However, by physicochemical methods, no formation of surface apatite layer was observed. These results suggest that beta-TCP bonds to bone through microanchoring between bone and rough surface of resorbed beta-TCP.

Animals↗

PubMed1991

Apatite formation on the surface of Ceravital-type glass-ceramic in the body.

Previous studies on surface structural changes in vitro as well as in vivo of bioactive A-W-type glass-ceramics and Bio-glass-type glasses showed that the essential condition for glasses and glass-ceramics to bond to living bone is formation of a bonelike apatite layer on their surfaces in the body. Gross et al., however, had explained the bone-bonding mechanism of Ceravital-type apatite-containing glass-ceramic without mentioning formation of the surface apatite layer. In the present study, apatite formation on the surface of one of Ceravital-type glass-ceramics was investigated in vitro as well as in vivo. An apatite-containing glass-ceramic of the composition Na2O 5, CaO 33, SiO2 46, Ca(PO3)2 16 wt%, which was named KGS by Gross et al., was soaked in an acellular simulated body fluid which had ion concentrations almost equal to those of the human blood plasma. The same kind of glass-ceramic was implanted into a rabbit tibia. Thin-film x-ray diffraction, Fourier transform infrared reflection spectroscopy, and scanning electron microscopic observation of the surfaces of the specimens soaked in the simulated body fluid showed that Ceravital-type glass-ceramic also forms a layer of carbonate-containing hydroxyapatite of small crystallites and/or a defective structure on its surface in the fluid. Electron probe x-ray microanalysis of the interface between the glass-ceramic and the surrounding bone showed that a thin layer rich in Ca and P is present at the interface. These findings indicated that Ceravital-type glass-ceramics also form the bonelike apatite layer on its surface in the body and bond to living bone through the apatite layer.

Animals↗

PubMedDate not supplied

Development of bioactive PMMA-based cement by modification with alkoxysilane and calcium salt.

Poly (methyl methacylate) (PMMA) bone cement is one of the popular bone-repairing materials for fixation of artificial hip joints. Significant problems on the PMMA bone cement are caused by loosening at the interface between bone and the cement, since the cement does not show bone-bonding, i.e. bioactivity. Development of PMMA bone cement capable of bone-bonding has been therefore long desired. The prerequisite for an artificial material to show bone-bonding is the formation of a biologically active bone-like apatite layer on its surface when implanted in the body. The same type of apatite formation can be observed on bioactive materials even in a simulated body fluid (Kokubo solution) with ion concentrations nearly equal to those of human blood plasma. Fundamental researches for bioactive glasses and glass-ceramics revealed that the apatite deposition is initiated by release of Ca2+ ions from the material into the body fluid, and by catalytic effect of Si-OH groups formed on the surface of the material. These findings lead an idea that novel bioactive cement can be designed by incorporation of Si-OH groups and Ca2+ ion into PMMA bone cement. In the present study, PMMA bone cement is modified with 20 mass % of various kinds of alkoxysilanes and calcium salts, and its apatite-forming ability was evaluated in Kokubo solution. The apatite formation was observed on the surface of the modified cements containing 20 mass % of CaCl2, irrespective of the kind of the examined alkoxysilane. On the other hand, the apatite formation was observed on the cement containing CaCl2, Ca(CH3COO)2 or Ca(OH)2, but not on the cement containing CaCO3 or beta-Ca3(PO4)2, even when the cement contains 3-methacryloxypropyltrimethoxysilane (MPS). The results indicate that modification with alkoxysilane and calcium salts showing high water-solubility is effective for providing PMMA bone cement with bioactivity.

Journal Article↗

PubMedDate not supplied

Synthetic nucleosides and nucleotides. 40. Selective inhibition of eukaryotic DNA polymerase alpha by 9-(beta-D-arabinofuranosyl)-2-(p-n-butylanilino) adenine 5'-triphosphate (BuAaraATP) and its 2'-up azido analog: synthesis and enzymatic evaluations.

Starting from 2',3',5'-tri-O-acetyl-2-iodoadenosine, 9-(beta-D-arabinofuranosyl)-2-(p-n-butylanilino)adenine and its 2'(S)-azido counterparts were synthesized in seven steps. These exhibited only moderate growth-inhibitory effects against mouse leukemic P388 cells (IC50 = 13-24 microM), although 5'-triphosphate derivatives showed strong and selective inhibitory action on calf thymus DNA polymerase alpha, but not on beta- and epsilon-polymerases from eukaryotes.

Adenine↗