Investigations on the wear behaviour of the temporary PMMA-based hip Spacer-G.

Total hip replacement has become one of the most successful orthopaedic procedures. However, complications due to infections may give serious problems and have devastating consequences for the hip implant. The use of a temporary three-dimensional polymethylmethacrylate (PMMA) cement spacer may be an alternative to solve infections in hip implants, improving the lives of patients awaiting reimplantation. In order to evaluate their wear behaviour, five PMMA Spacer-G femoral heads were tested against five post-mortem pelves in a hip joint simulator with bovine calf serum as lubricant. The surface of the worn spacers was characterized by scanning electron microscopy (SEM) analysis; all the samples revealed a similar morphology, showing areas characterized by different degrees of wear. Particle debris was isolated from the lubricant and PMMA particles and bone fractions were quantified. The amount of debris was found to be higher than where no-temporary prostheses were used. However, this result is acceptable since wear debris is removed by lavage irrigation when the Spacer-G is explanted. On the basis of these data, it is considered that the use of the cement Spacer-G could be a promising approach to the treatment of complicated infections of the hip joint. Therefore, Spacer-G is worthy of further research.

Arthroplasty, Replacement, Hip↗
PubMed2003

Fatigue strength of PMMA bone cement mixed with gentamicin and barium sulphate vs pure PMMA.

Barium sulphate is added to polymethylmethacrylate (PMMA) bone cement as a radiopacifier. Gentamicin is an antibiotic added to bone cement to treat or prevent infection in arthroplasty. This study investigated the combined effect of barium sulphate and gentamicin sulphate on the fatigue strength of PMMA bone cement. Three different formulations were studied: pure PMMA, PMMA with barium sulphate added and PMMA with barium sulphate and gentamicin sulphate added. Before testing all specimens were stored in water at 37 degrees C for at least 15 days to season the PMMA and to elute the antibiotic. Fatigue tests were performed following a previously validated procedure. The slope part of the Wöhler diagram was obtained and a rough endurance limit was estimated for all three formulations. The experimental data showed that the addition of barium sulphate to PMMA bone cement affected the fatigue strength of the material, whereas addition of gentamicin sulphate to the radiopaque PMMA had no effect on the fatigue properties of the bone cement. While PMMA with barium sulphate added was confirmed to have a reduced fatigue strength when compared with plain PMMA, no detrimental effect was found for the addition of gentamicin sulphate to radiopaque PMMA.

Anti-Bacterial Agents↗
PubMed2003

The influence of stem insertion rate on the porosity of the cement mantle of hip joint replacements.

This study investigates the effect of stem insertion rate on the porosity of the cement mantle. An experimental protocol was developed to simulate the surgical technique of cementing a prosthetic stem into the medullary canal of the femur. Cement mantle specimens were produced for three different stem insertion rates. The presence of porosity in the cement mantle was investigated. Additionally, the mechanical strength of the bone cement was assessed. Increasing the stem insertion rate did not have a significant effect on the porosity distribution within the bulk cement mantle. However, for all stem insertion rates investigated, the porosity concentration increased significantly moving from the cement/pseudofemur interface through to the stem/cement interface. In all cases, the presence of porosity significantly decreased the mechanical behaviour of the bone cement. High porosity concentration at the stem/cement interface seems to be attributed also to the rheology of the cement during implant insertion. Nevertheless, the surgeon cannot influence the formation of porosity by changing the stem insertion rate.

Arthroplasty, Replacement, Hip↗
PubMed2002

Finite element and experimental models of cemented hip joint reconstructions can produce similar bone and cement strains in pre-clinical tests.

Finite element (FE) models could be used for pre-clinical testing of cemented hip replacement implants against the damage accumulation failure scenario. To accurately predict mechanical failure, the models should accurately predict stresses and strains. This should be the case for various implants. In the current study, two FE models of composite hip reconstructions with two different implants were validated relative to experimental bone and cement strains. The objective was an overall agreement within 10% between experimental and FE strains. Two stem types with different clinical results were analyzed: the Lubinus SPII and the Mueller Curved with loosening rates of 4% and 16% after 10 yr, respectively (Prognosis of total hip replacement. 63rd Annual Meeting of the American Academy of orthopaedic surgeons, Atlanta, USA). For both implant types, six stems were implanted in composite femurs. All specimens were subjected to bending. The Mueller Curved specimens were additionally subjected to torsion. Bone strains were recorded at 10 locations on the cortex and cement strains at three locations within the cement mantle. An FE model was built for both stem types and the experiments were simulated. Bone and cement strains were calculated at the experimental gauge locations. Most FE bone strains corresponded to the mean experimental strains within two standard deviations; most FE cement strains within one standard deviation. Linear regression between the FE and mean experimental strains produced slopes between 0.82 and 1.03, and R(2) values above 0.98. Particularly for the Mueller Curved, agreement improved considerably when FE strains were compared to the strains from the experimental specimen used to build the FE model. The objective of overall agreement within 10% was achieved, indicating that both FE models were successfully validated. This prerequisite for accurately predicting long-term failure has been satisfied.

Bone Cements↗
PubMed2002

Effects of the sterilisation method on the wear of UHMWPE acetabular cups tested in a hip joint simulator.

Ultra-high molecular-weight-polyethylene is the most commonly used bearing material in total joint replacement. Wear of polyethylene is a Serious Clinical problem that limits the longevity of orthopaedic implants. Information on degradative changes in the material properties and on the methods used for the sterilisation of polyethylene may help in the selection process of orthopaedic implants with the best wear resistance. This study was performed to investigate the effects of the sterilisation method (gamma irradiation and ethylene oxide treatment) on the wear and on the changes in physical properties of polyethylene acetabular cups. At this purpose, gamma-sterilised and ethylene oxide (EtO)-sterilised acetabular cups were tested against CoCr femoral heads in a hip joint simulator run for 5 million cycles in bovine calf serum. The crystallinity of the cups was evaluated by micro-Raman spectroscopy as a function of the inner surface position. The partial least square calibration was used to correlate the Raman spectra with the crystallinity of the polymer measured by differential scanning calorimetry. The analysis performed on soak control acetabular cups demonstrated that the gamma-sterilised cups are significantly more crystalline than the EtO-sterilised ones. The mean crystallinity values obtained for the gamma-sterilised and EtO-sterilised soak control cups were 65.0% and 63.4%, respectively. Weight loss measurements revealed that the gamma-sterilised acetabular cups exhibited a lower wear rate than that by EtO-sterilised. Thc Raman results obtained on gamma-sterilised and EtO-sterilised acetabular cups showed that the changes in surface crystallinity were mainly caused by irradiation rather than by the mechanical friction during the in vitro tests.

Analysis of Variance↗
PubMed2002

Nitric oxide synthase in tissues around failed hip prostheses.

Nineteen patients who had undergone hip revision surgery for aseptic loosening of joint prostheses were studied. Tissue samples were harvested at the interface between bone and implant, either at the stem or at the cotyle level. Immunohistochemistry was performed on tissue sections to detect nitric oxide synthase (NOS), the enzyme which enables the synthesis of nitric oxide (NO), a molecule which can activate bone resorption. Quantitative analysis of the positive cells and correlation with the presence of particulate wear debris and radiological data were performed. The authors observed a trend towards a moderate increase in positive cells due to inducible NOS in tissues containing particulate wear debris, especially of a plastic material. This increase, however, did not achieve statistical significance. On the contrary, there was a statistical correlation between iNOS (inducible NOS) and the severity of osteolysis around the prosthetic implant. Pharmacological control of the biosynthesis of NO may be considered in the prevention or treatment of loosening.

Adult↗
PubMed2002

The performance of gamma- and EtO-sterilised UHWMPE acetabular cups tested under severe simulator conditions. Part 1: role of the third-body wear process.

Due to its excellent combination of properties, ultra-high-molecular-weight-polyethylene has been used for the last 30 years in the replacement of damaged articulating cartilage for total joint replacement surgery. However, in some cases, wear, failure and delamination have been observed. Polyethylene performance may be affected by oxidation during consolidation of the resin, sterilisation of the finished specimens and post-irradiation storage. In order to evaluate the influence of the sterilisation method (gamma-irradiation and ethylene oxide(EtO)-treatment) and third-body particles on the ultra-high-molecular-weight-polyethylene wear behaviour, gamma- and EtO-sterilised ultra-high-molecular-weight-polyethylene acetabular cups were tested against CoCrMo femoral heads in a hip joint simulator run for 2.5 million cycles in bovine calf serum in the presence of third-body PMMA particles. Weight loss measurements revealed that the gamma-sterilised acetabular cups exhibited a significantly lower wear rate than those EtO-sterilised. Moreover, significant differences were found for each type of sterilisation between the gravimetric wear trends obtained until 2.5 million cycles in the presence and in the absence of PMMA particles.

Absorption↗
PubMed2002

Comparison of asynchronous and realtime teleconsulting for orthopaedic second opinions.

We studied a teleconsulting service for second opinions in orthopaedics. Three units of the national insurance organization for accidents at work were connected to a large orthopaedic hospital in Bologna. During a 20-month study, 65 consultations were provided: 51 (78%) by asynchronous (store-and-forward) consulting and 14 (22%) by realtime videoconferencing. All the consultations made use of radiology images (radiographs, computerized tomography scans, magnetic resonance imaging scans and ultrasound scans). Video-messages and still images were commonly used to support the asynchronous consultations. More data were transmitted on average for an asynchronous teleconsultation (8 MByte) than in a videoconference (5 MByte). The average time spent by orthopaedic specialists was slightly longer in videoconferences (21 min, SD 8) than in asynchronous teleconsultations (19 min, SD 8). The clinicians confidence in their diagnosis was generally good but was lower in asynchronous consultations. The main problem affecting the telemedicine service was the lack or the low quality of the information received from the referring sites. The clinical complexity of the case and the organizational requirements were declared to be the main factors affecting the choice of consulting procedure. The study showed that the asynchronous method was preferred in the majority of cases and could be easily integrated into clinical practice, although there were some concerns about the diagnostic quality of the information transmitted.

Humans↗
PubMed2002

Growth and remodelling of the autologous bone transplant used in a pediatric femoral reconstruction.

The aim of the present work was to assess how growth and remodelling changed the morphology of the transplanted fibula used to reconstruct the proximal femur of a 5 year old child affected by a Ewing's sarcoma during the first 3 years of follow-up. The morphological evolution of the transplant was quantitatively assessed on diagnostic images. Special software was developed to perform three-dimensional measurements on computed tomography (CT) datasets, while state-of-the-art image processing software was used for conventional radiography. The measurements were then correlated with the loads expected to act on the hip during the various stages of the rehabilitation protocol. A simple cantilever beam model was used for a gross estimate of the risk of fracture of the transplant. The results of the analysis showed that there is no clear correlation between the morphological changes of the autograft and the hip loading conditions experienced. Apart from a drastic increase in the periosteal radius in the frontal plane, occurring in the first 10 months after the operation, the growth of the transplanted fibula seems well within the ranges of the normal fibular growth. The cantilever beam model suggested that, although the autograft is currently subjected to subcritical stresses. morphological evolution could increase the risk of fracture in the next few years if a normal level of loading were allowed.

Bone Remodeling↗
PubMed2002

Surface characterization and debris analysis of ceramic pairings after ten million cycles on a hip joint simulator.

This study was aimed at characterizing the ceramic wear particles produced during tests on a hip joint wear simulator of up to 10 million cycles. Alumina and alumina-zirconia composites were studied as commercial or potential hip joint products respectively. No ceramic particles could be observed, even after a careful isolation procedure. This confirms the low wear rate found for these materials in previous works (of the order of tenths of milligrams per million cycles). Surface characterization was conducted by means of scanning electron microscopy. It confirms the low wear regime of ceramic pairings and allows ceramic wear debris morphology to be defined. The effect of microstructure on surface wear is discussed.

Aluminum Oxide↗
PubMed2001

Pre-clinical validation of a new partially cemented femoral prosthesis by synergetic use of numerical and experimental methods.

The present work reports the pre-clinical validation of an innovative partially cemented femoral prosthesis called cement-locked uncemented (CLU) prosthesis. The inventors of the device under investigation claimed that, when compared to a comparable fully cemented stem, the new stem would present various advantages. Two previous experimental studies confirmed that primary stability and stress shielding were comparable to those of cemented stems. Aim of the present study was to investigate if the remaining claims were confirmed as well. A complete finite element model of the bone-implant complex was created from CT data. The model was validated against in vitro measurements of bone surface strains as well as against primary stability measurements. The peak stresses predicted in the CLU cement mantle were not found significantly lower than those reported in other studies on fully cemented stems. However, once the cement inlet geometry is optimised and the associated stress risers are eliminated, the CLU cement mantle should be subjected to much lower stresses. The stress induced in the stems by both load cases was well below the fatigue limit of the Ti6Al4V alloy. Finite element models predicted for all load cases relative motion between cement and metal lower than 60 microm. This amplitude may be fully accommodated by elastic deformations of the cement micro-ridges. The experimental and numerical results showed the validity of the new fixation concept, although a further optimisation of the geometry of the cement pockets is needed in order to further reduce the stresses in the cement.

Alloys↗
PubMed2001

Mixed oxides prosthetic ceramic ball heads. Part 3: effect of the ZrO2 fraction on the wear of ceramic on ceramic hip joint prostheses. A long-term in vitro wear study.

Using ceramic materials it is possible to obtain a number of beneficial mechanical properties such as considerable hardness, good chemical resistance, high tensile strength, and a good fracture toughness. The use of ceramic-on-ceramic as bearing surfaces for hip joint prostheses has been reported to produce a lower wear rate than other combinations (i.e. metal-on-polyethylene and ceramic-on-polyethylene) in total hip artroplasty. These advantages may increase the life expectancy of hip implants and improve the life of patients. Two new types of mixed-oxide ceramics (alumina and yttria-stabilised zirconia) femoral heads and acetabular cups containing different ratios of alumina and zirconia were compared with pure commercial alumina in terms of wear behaviour in a hip joint simulator. Hip joint wear simulator studies were carried out with a full-peak load of 2030 N and a frequency of 1 Hz in bovine calf serum. After 10 million cycles the measured weight loss of all specimens was very low. However, the experimental results did not show any significant difference between the new experimental mixed-oxide ceramics prototype and the commercial ceramic material couplings.

Aluminum Oxide↗
PubMed2001

Isolation and morphological characterisation of UHMWPE wear debris generated in vitro.

Wear tests are generally carried out on materials used in prosthetic hip implants, in order to obtain a better understanding of the tribological processes involved and improve the quality control of joint prostheses, directed towards reducing the risk of implant failure of innovative prostheses. Ceramic femoral heads of mixed alumina-zirconia oxides as well as zirconia and alumina single oxide heads were tested against UHMWPE acetabular cups in a hip joint simulator. Polyethylene cups and ceramic femoral heads were mounted in a simulator apparatus moving according to a sinusoidal function, under load and in the presence of bovine calf serum as lubricant. Wear particles were isolated from the bovine calf serum collected during the wear tests. An easy to follow method was used to separate the wear particles from the lubricant. Chemical digestive methods were used to separate the wear particles from the lubricant and the isolated particles were studied using scanning electron microscopy. The morphologies of the polyethylene debris showed considerable differences, both in size and shape of the particles, as a function of the coupled head material.

Animals↗
PubMed2001

Even a thin layer of soft tissue may compromise the primary stability of cementless hip stems.

OBJECTIVE: Aim of the present study is to quantify the minimum thickness of mechanically non-bearing regions around a cementless prosthesis necessary to loose the implant enough to activate interface tissue differentiation. DESIGN: A finite element model was used to predict the bone-implant micromotion induced by stair-climbing joint loads for various thickness of non-bearing tissue fully encapsulating the implant. BACKGROUND: The results of a few published studies give indications on the amount of bone-implant relative micromotion that is required to initiate the fibrous differentiation. On the contrary, very little is known on the effect of mechanically non-bearing regions at the interface on the stability of the implant. METHODS: A new modelling strategy was adopted, which allows the simulation of soft tissues layers down to 10 microm of thickness. This technique was used in combination with an accurate and extensively validated finite element model to investigate for an anatomical cementless stem design the effect of the thickness of the soft tissues layer on the induced micro-movements. RESULTS: The stability of the implant was found extremely sensitive to the presence of soft tissue. Soft tissue layers of 300 microm were found sufficient to compromise the osseointegration on most of the stem surface. CONCLUSIONS: This study supports the hypothesis that even thin layers of soft tissue may create micro-movements large enough to activate adverse biological effects. RELEVANCE: Interface layers of soft tissue too thin to be detected by a radiographic control may be sufficient to compromise the mechanical stability of cementless implants.

Biomechanical Phenomena↗
PubMed2001

Initial stability of a cementless acetabular cup design: experimental investigation on the effect of adding fins to the rim of the cup.

Different design solutions have been suggested for improvement of the initial stability of cementless acetabular cups, such as adding threads, spikes, or pegs to the hemispherical geometry, the pore structure of the surface; and screw fixation. This experimental study investigated the effect of fins on the initial stability of the acetabular cup. Three designs were studied, with none, 2, and 12 fins, respectively. The cups were press fit into cavities reamed in 2 different polyurethane foams, used to simulate 2 qualities of cancellous bone. Two millimeter press-fit and exact-fit conditions were investigated. The results show that the type of substrate and the interference value are important in determining the initial stability of the cup. The addition of fins on the cup rim enhances in vitro the initial stability, especially in cases of a poor press fit with a good substrate. This preclinical investigation suggests that the use of a cup design with fins may be beneficial in all cases in which press fit of the cup cannot be assured. However, further clinical studies are required to validate in vivo the efficacy of the fins as additional fixation devices.

Acetabulum↗